Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Eurostar Starflam RF0069 PA66, 30% Glass Fiber, Flame Retardant, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Glass Fiber Filled, Flame Retardant
Manufacturer Eurostar Engineering Plastics
Trade Name Starflam
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Starflam RF0069 PA66, 30% Glass Fiber, Flame Retardant, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Starflam RF0069 is a Flame Retardant, 30% Glass Reinforced Polyamide 66 Injection Molding Resin (also known as PA66 30V U2 Z79 or RF1006Z590)Information provided by Eurostar.
Physical Properties Metric English Comments
Density 1.58 g/cc
0.0571 lb/in³
ISO 1183
Water Absorption at Saturation 4.0 %

@Temperature 23.0 °C
4.0 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0020 - 0.0030 cm/cm
0.0020 - 0.0030 in/in
on Tensile Bar; E2P method
Mechanical Properties Metric English Comments
Hardness, Rockwell L 108
108
ISO 2039-2
Tensile Strength at Break 165 MPa
23900 psi
5 mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 9.50 GPa
1380 ksi
1 mm/min; ISO 527
Flexural Strength 190 MPa
27600 psi
2 mm/min; ISO 178
Flexural Modulus 9.30 GPa
1350 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²

@Temperature -20.0 °C
3.33 ft-lb/in²

@Temperature -4.00 °F
80x10x4; ISO 179/1eA
8.00 kJ/m²

@Temperature 23.0 °C
3.81 ft-lb/in²

@Temperature 73.4 °F
80x10x4; ISO 179/1eA
Charpy Impact Unnotched 6.00 J/cm²
28.6 ft-lb/in²
Edgew 80x10x4 sp=62; ISO 179/1eU
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 23.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
12.8 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
40.0 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Hot Ball Pressure Test 123 - 127 °C
253 - 261 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 262 °C
504 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 248 °C
478 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Ae
Vicat Softening Point 258 °C
496 °F
B/120; ISO 306
UL RTI, Electrical 65.0 °C
149 °F
UL RTI, Mechanical with Impact 65.0 °C
149 °F
UL RTI, Mechanical without Impact 65.0 °C
149 °F
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
Oxygen Index 31 %
31 %
ISO 4589
Glow Wire Test 960 °C

@Thickness 2.00 mm
1760 °F

@Thickness 0.0787 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 250 V
250 V
IEC 60112
Processing Properties Metric English Comments
Zone 1 270 - 290 °C
518 - 554 °F
Zone 2 270 - 280 °C
518 - 536 °F
Zone 3 270 - 280 °C
518 - 536 °F
Melt Temperature 270 - 280 °C
518 - 536 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 75.0 - 85.0 °C

@Time 14400 - 21600 sec
167 - 185 °F

@Time 4.00 - 6.00 hour
Moisture Content 0.20 %
0.20 %
Copyright © lookpolymers.com All Rights Reserved