Polymer Resources PPX-FR1-[color]-EN Modified-PPO, V-0 Flame Retardant, Extrusion Grade

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Heat Resistant
Manufacturer Polymer Resources, LTD
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PPX-FR1-[color]-EN Modified-PPO, V-0 Flame Retardant, Extrusion Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Modified-Polyphenylene Oxide, V-0 Flame Retardant, 190F HDT, Extrusion GradeFeatures: • Bromine Free • Chlorine FreeProcess: ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.08 g/cc
1.08 g/cc
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 15 - 40 g/10 min

@Load 11.6 kg,
Temperature 250 °C
 15 - 40 g/10 min

@Load 25.6 lb,
Temperature 482 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 113
113
ASTM D785
Tensile Strength at Break 46.9 MPa
6800 psi
ASTM D638
Tensile Strength, Yield 56.5 MPa
8200 psi
ASTM D638
Elongation at Break 50 %
50 %
ASTM D638
Flexural Strength 89.6 MPa
13000 psi
ASTM D790
Flexural Modulus 2.28 GPa
330 ksi
ASTM D790
Izod Impact, Notched 1.60 J/cm

@Temperature -40.0 °C
 3.00 ft-lb/in

@Temperature -40.0 °F
 ASTM D256
3.74 J/cm

@Temperature 22.8 °C
 7.00 ft-lb/in

@Temperature 73.0 °F
 ASTM D256
Gardner Impact 16.9 J
12.5 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 87.8 °C
190 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 82.2 °C
180 °F
ASTM D648
UL RTI, Electrical 110 °C

@Thickness 1.50 mm
 230 °F

@Thickness 0.0591 in
 UL 746
110 °C

@Thickness 1.70 mm
 230 °F

@Thickness 0.0669 in
 UL 746
110 °C

@Thickness 3.00 mm
 230 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical with Impact 110 °C

@Thickness 1.50 mm
 230 °F

@Thickness 0.0591 in
 UL 746
110 °C

@Thickness 1.70 mm
 230 °F

@Thickness 0.0669 in
 UL 746
110 °C

@Thickness 3.00 mm
 230 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical without Impact 95.0 °C

@Thickness 1.50 mm
 203 °F

@Thickness 0.0591 in
 UL 746
95.0 °C

@Thickness 1.70 mm
 203 °F

@Thickness 0.0669 in
 UL 746
95.0 °C

@Thickness 3.00 mm
 203 °F

@Thickness 0.118 in
 UL 746
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
ASTM D257
Dielectric Strength 22.0 kV/mm
560 kV/in
ASTM D149
Comparative Tracking Index 250 - 400 V
250 - 400 V
UL 746
Hot Wire Ignition, HWI >= 120 sec

@Thickness 1.50 mm
 >= 120 sec

@Thickness 0.0591 in
 UL 746
>= 120 sec

@Thickness 1.70 mm
 >= 120 sec

@Thickness 0.0669 in
 UL 746
>= 120 sec

@Thickness 3.00 mm
 >= 120 sec

@Thickness 0.118 in
 UL 746
High Amp Arc Ignition, HAI 60 - 120 arcs

@Thickness 1.50 mm
 60 - 120 arcs

@Thickness 0.0591 in
 UL 746
60 - 120 arcs

@Thickness 1.70 mm
 60 - 120 arcs

@Thickness 0.0669 in
 UL 746
60 - 120 arcs

@Thickness 3.00 mm
 60 - 120 arcs

@Thickness 0.118 in
 UL 746
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature >= 171 °C
>= 340 °F
Middle Barrel Temperature >= 188 °C
>= 370 °F
Front Barrel Temperature >= 188 °C
>= 370 °F
Melt Temperature 193 - 216 °C
380 - 420 °F
Drying Temperature 71.1 - 82.2 °C
160 - 180 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.001