Overview of materials for Polypropylene, Stainless Fiber, EMI

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Stainless Fiber, EMI
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polypropylene, Stainless Fiber, EMI.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Stainless Fiber, EMI". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.960 - 1.30 g/cc
0.0347 - 0.0470 lb/in³
Average value: 1.05 g/cc Grade Count:13
Filler Content 5.00 - 15.0 %
5.00 - 15.0 %
Average value: 10.0 % Grade Count:4
Water Absorption 0.0100 - 0.0200 %
0.0100 - 0.0200 %
Average value: 0.0125 % Grade Count:4
Linear Mold Shrinkage 0.00300 - 0.0250 cm/cm
0.00300 - 0.0250 in/in
Average value: 0.00889 cm/cm Grade Count:11
Linear Mold Shrinkage, Transverse 0.0140 - 0.0250 cm/cm
0.0140 - 0.0250 in/in
Average value: 0.0209 cm/cm Grade Count:5
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 15.0 - 70.0 MPa
2180 - 10200 psi
Average value: 33.4 MPa Grade Count:13
Tensile Strength, Yield 19.0 - 21.4 MPa
2760 - 3100 psi
Average value: 20.5 MPa Grade Count:3
Elongation at Break 2.50 - 76.0 %
2.50 - 76.0 %
Average value: 23.5 % Grade Count:13
Elongation at Yield 5.20 - 8.00 %
5.20 - 8.00 %
Average value: 6.60 % Grade Count:4
Modulus of Elasticity 0.965 - 4.10 GPa
140 - 595 ksi
Average value: 2.04 GPa Grade Count:12
Flexural Yield Strength 27.6 - 109 MPa
4000 - 15800 psi
Average value: 48.5 MPa Grade Count:12
Flexural Modulus 1.10 - 6.20 GPa
160 - 899 ksi
Average value: 2.50 GPa Grade Count:12
Izod Impact, Notched 0.600 - 2.67 J/cm
1.12 - 5.00 ft-lb/in
Average value: 1.60 J/cm Grade Count:10
Izod Impact, Unnotched 3.20 - 5340 J/cm
5.99 - 10000 ft-lb/in
Average value: 8.36 J/cm Grade Count:10
Izod Impact, Notched (ISO) 10.0 - 25.0 kJ/m²
4.76 - 11.9 ft-lb/in²
Average value: 20.0 kJ/m² Grade Count:3
K (wear) Factor 10100 x 10-8 mm³/N-M
5000 x 10-10 in³-min/ft-lb-hr
Average value: 10100 x 10<sup>-8</sup> mm³/N-M Grade Count:3
Thermal Properties Metric English Comments
CTE, linear 54.0 - 140 µm/m-°C
30.0 - 77.8 µin/in-°F
Average value: 103 µm/m-°C Grade Count:4
CTE, linear, Transverse to Flow 120 - 170 µm/m-°C
66.7 - 94.4 µin/in-°F
Average value: 150 µm/m-°C Grade Count:3
Deflection Temperature at 0.46 MPa (66 psi) 95.0 - 138 °C
203 - 280 °F
Average value: 124 °C Grade Count:7
Deflection Temperature at 1.8 MPa (264 psi) 52.8 - 138 °C
127 - 280 °F
Average value: 86.8 °C Grade Count:9
Flammability, UL94 HB
HB
Grade Count:6
Electrical Properties Metric English Comments
Electrical Resistivity 0.0100 - 100 ohm-cm
0.0100 - 100 ohm-cm
Average value: 22.6 ohm-cm Grade Count:9
Surface Resistance 10.0 - 1.00e+6 ohm
10.0 - 1.00e+6 ohm
Average value: 169000 ohm Grade Count:9
Static Decay 2.00 sec
2.00 sec
Average value: 2.00 sec Grade Count:6
Processing Properties Metric English Comments
Processing Temperature 188 - 227 °C
370 - 440 °F
Average value: 204 °C Grade Count:3
Melt Temperature 180 - 246 °C
356 - 475 °F
Average value: 219 °C Grade Count:7
Mold Temperature 20.0 - 65.6 °C
68.0 - 150 °F
Average value: 43.0 °C Grade Count:10
Drying Temperature 79.4 - 90.0 °C
175 - 194 °F
Average value: 81.4 °C Grade Count:7
Moisture Content 0.100 %
0.100 %
Average value: 0.100 % Grade Count:3
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi
Average value: 86.2 MPa Grade Count:6