Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | |
3M Dyneon™ Fluorel™ FE-5620Q Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. The FE series O-ring grades are the c.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | |
3M Dyneon™ Fluorel™ FE-5621Q Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. The FE series O-ring grades are the c.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | |
3M Dyneon™ Fluorel™ FC-2176 Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. Good general purpose grade with good .. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | |
3M Dyneon™ Fluorel™ FT-2481 Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Non-incorporated cure polymer, 68.6%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, 4% Ca(OH)2, 1.4% Dihydroxy Crosslinker, 0.4% Phosp.. |
|||
Tensile Strength, Ultimate | 15.0 - 60.0 MPa @Temperature 60.0 - 120 °C |
2180 - 8700 psi @Temperature 140 - 248 °F |
Average value: 36.7 MPa Grade Count:1 |
Overview of materials for Polyphenylene Ether, 10% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, 10% Glass Filled". Specific grades with glass content between 5% and 14% are includ.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | ASTM D638 |
Total Finaprene® 411x Styrene-Butadiene TPE Copolymer, 80 Shore A
(discontinued **) Styrene-Butadiene CopolymerDescription: Finaprene® 411x is a thermoplastic elastomer type radial styrene-butadiene block copolymer. Thanks to its high molecular weight, Finaprene® 411x provides e.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | ASTM D638 |
Huntsman PE 1011 Film Extrusion Polyethylene
(discontinued **) Homopolymer, Drug Master File listed product, and FDA compliant.Features: Good impact strength, good machinability, heat seal and foaming characteristicsApplications: Film Extrusion: industrial line.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | ISO 527 |
LATI LATISTAT 43/7-02 Low Density Polyethylene (LDPE) Base Conductive Plastic
(discontinued **) Description: Latistat materials have low specific resistivity. They feature partial electrical conductivity. Selected functional additives give materials with low specific resistivity and reasonable.. |
|||
Tensile Strength, Ultimate | 15.0 - 23.1 MPa | 2180 - 3350 psi | Average value: 17.3 MPa Grade Count:4 |
Overview of materials for High Density Polyethylene (HDPE), Wood Filled This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Wood Filled". Each property range of values reported is minimum and ma.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | ASTM D638 |
ExxonMobil Iotek® 7510 Zinc Ionomer Molding/Extrusion Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A "soft" zinc ionomer with excellent flexibility and impact strength. This ionomer has outstanding adhesion to glass, metals and paper. IOTEK iono.. |
|||
Tensile Strength, Ultimate | 15.0 MPa @Temperature 120 °C |
2180 psi @Temperature 248 °F |
ISO 527 |
LATI LATAMID 12 H FE90 Nylon 12 Base Magnetizable Compound
(Unverified Data**) Description: These are compounds containing a high percentage of magnetizable fillers; compared to traditional techniques for the manufacture of magnets, this allows the molding of complex shapes us.. |
|||
Tensile Strength, Ultimate | 15.0 MPa @Temperature 120 °C |
2180 psi @Temperature 248 °F |
ISO 527 |
LATI LATILUB 82-01M Nylon 12 Base, 1% Molybdenum Disulfide Self Lubricating Plastic
(discontinued **) Description: Latilub self-lubricating plastic materials are more and more often designed to replace metals in applications such as gears, bushings, cams, slides, etc), for which, besides their intri.. |
|||
Tensile Strength, Ultimate | 15.0 - 100 MPa | 2180 - 14500 psi | Average value: 71.3 MPa Grade Count:141 |
Overview of materials for Nylon 66, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 335 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 335 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | Type IV, crosshead speed 2 in/min; ASTM D638 |
DuPont Elvax® 450 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 330 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 335 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 330 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 335 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
Dow Nordel® IP 4640 Molded Golf Grips FormulationNordel® IP 4640 |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | Die C (35 min / 145°C); ASTM D412 |
Dow SE BCP 817 Stereospecific high cis-1,4 Polybutadiene (BR) SE BCP 817 is manufactured by a solution process using cobalt catalyst which produces polymers with a very light color and low ash content. A non-staining stabilizer is added during the production .. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | ASTM D638/D412 |
Covestro Bayflex® MP-10000 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System 0.118 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and of.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | ASTM D412 |
Colorite Polymers CS6041GP Non Lead Wire and Cable Vinyl Compound Description: Colorite specialty wire and cable compounds feature low smoke properties, excellent flame retardance, low temperature flexibility, and resistance to abrasion and chemicals. All are avai.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | |
BASF Lucalen® A 3120 M Ethylene/Acrylate Copolymer Suitable in similar manner as Lucalen A 2920 M or also as a material for coating aluminum, steel, paper and cardboard. Also for processing pipes for transporting petroleum, gas, etc.Data was collec.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | ASTM D638 |
ExxonMobil Escorene® LD-728 High EVA Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A high vinyl acetate copolymer with a low melting temperature and excellent strength properties and toughness.Applications: Injection molding; Foams.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | ASTM D638 |
Huntsman PE8010 Specialty Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Yields film with excellent draw down and machinability.Applications: Film extrusion: gel free film applications.FDA Notes: Conforms to FDA regulation 21 CFR 1.. |