Greene Tweed Arlon® 1555 PEEK, Carbon, Graphite Filled
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled |
| Manufacturer | Greene Tweed |
| Trade Name | Arlon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Greene Tweed Arlon® 1555 PEEK, Carbon, Graphite Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Arlon® is a tough, high-temperature, semi-crystalline, thermoplastic presenting a unique combination of mechanical, thermal, chemical and electrical properties. Greene, Tweed uses several proprietary manufacturing and machining processes to ensure that Arlons properties consistently outperform the competition.Greene, Tweed offers several different Arlon materials, and all provide high tensile strength and elongation properties, excellent shear strength and creep resistance, outstanding fatigue resistance, broad chemical and radiation resistance, and no susceptibility to hydrolysis (steam/hot water). Our engineers work one on one with customers to find the right solution for each specific application.Information provided by Greene Tweed.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 |
| Deformation | 0.10 % | 0.10 % | ASTM D621 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 98 | 98 | ASTM D785 |
| Hardness, Shore D | 87 | 87 | ASTM D2240 |
| Tensile Strength at Break | 146 MPa | 21200 psi | ASTM D368 |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| Flexural Strength | 188.0 MPa | 27260 psi | |
| 228 MPa | 33000 psi | ASTM D790 | |
| 126.8 MPa @Temperature 149 °C |
18390 psi @Temperature 300 °F |
||
| Flexural Modulus | 9.65 GPa | 1400 ksi | Flexural 0.5% Secant Modulus; ASTM D790 |
| 6.55 GPa @Temperature 149 °C |
950 ksi @Temperature 300 °F |
||
| Compressive Yield Strength | >= 4.14 MPa | >= 600 psi | |
| Compressive Strength | 170 MPa | 24600 psi | ASTM D695 |
| Shear Strength | 68.9 MPa | 10000 psi | Transverse; ASTM D732 |
| 89.6 MPa | 13000 psi | Axial; ASTM D732 | |
| 23.4 MPa @Temperature 260 °C |
3400 psi @Temperature 500 °F |
||
| 50.3 MPa @Temperature 149 °C |
7300 psi @Temperature 300 °F |
||
| 68.3 MPa @Temperature 65.6 °C |
9900 psi @Temperature 150 °F |
||
| Secant Modulus | 11.38 GPa | 1651 ksi | Tensile 0.5% Secant Modulus; ASTM D638 |
| Coefficient of Friction, Dynamic | 0.17 | 0.17 | PV=12600 psi-ft./min.; ASTM G77 |
| K (wear) Factor | 131 x 10-8 mm³/N-M | 65.0 x 10-10 in³-min/ft-lb-hr | ASTM G77 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.4 µm/m-°C @Temperature <=149 °C |
8.00 µin/in-°F @Temperature <=300 °F |
ASTM E228 |
| 30.6 µm/m-°C @Temperature >=149 °C |
17.0 µin/in-°F @Temperature >=300 °F |
ASTM E228 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black |
Users viewing this material also viewed the following:
- Park Electrochemical Nelco® N4000-29 BC® Buried Capacitance™ Multifunctional Epoxy
- Kennametal Stellite Stellite® SF20 Cobalt Alloy
- SABIC Innovative Plastics LNP LUBRICOMP KFL32R Acetal Copolymer
- Hexcel® HexWeb® HRH-36 - 1/8 - 6.0 Para-Aramid/Phenolic Core
- Hexcel® Redux® 206-NA Foaming adhesive film
- Polyplastics Duranex® 3400 Polybutylene Terephthalate (PBT), Standard, 40% GF filled
- Chosun Refractories MSC-1 Blast Furnace Tap-Hole Refractory
- Engineered Plastics EPPC 2014B Polycarbonate
- A. Schulman ComAlloy Hiloy® 622 Nylon 6/6, Glass Reinforced, UL
- DuPont Elvax® 3190LG Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion (discontinued **)
Copyright © lookpolymers.com All Rights Reserved