Haynes Multimet® alloy, 1.6 mm thick sheet, 1177°C heat treatment, rapid air cooled

Category Metal , Superalloy , Iron Base
Manufacturer Haynes International, Inc.
Trade Name Multimet®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes Multimet® alloy, 1.6 mm thick sheet, 1177°C heat treatment, rapid air cooled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and is readily fabricated. Current applications include aircraft, including tailpipes and tailcones, afterburner parts, exhaust manifolds, combustion chambers, turbine blades, buckets and nozzles. Excellent service for high temperature bolts.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.20 g/cc
0.296 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 159
159
Converted from Rockwell B hardness.
Hardness, Knoop 176
176
Converted from Rockwell B hardness.
Hardness, Rockwell B 92
92
Hardness, Vickers 201
201
Converted from Rockwell B hardness.
Tensile Strength, Ultimate 814 MPa
118000 psi
18.0 MPa

@Temperature 1288 °C
 2610 psi

@Temperature 2350 °F
23.0 MPa

@Temperature 1260 °C
 3340 psi

@Temperature 2300 °F
33.0 MPa

@Temperature 1204 °C
 4790 psi

@Temperature 2199 °F
48.0 MPa

@Temperature 1149 °C
 6960 psi

@Temperature 2100 °F
90.0 MPa

@Temperature 1093 °C
 13100 psi

@Temperature 1999 °F
170 MPa

@Temperature 982 °C
 24700 psi

@Temperature 1800 °F
268 MPa

@Temperature 871 °C
 38900 psi

@Temperature 1600 °F
403 MPa

@Temperature 760 °C
 58500 psi

@Temperature 1400 °F
507 MPa

@Temperature 649 °C
 73500 psi

@Temperature 1200 °F
647 MPa

@Temperature 538 °C
 93800 psi

@Temperature 1000 °F
676 MPa

@Temperature 427 °C
 98000 psi

@Temperature 801 °F
Tensile Strength, Yield 400 MPa

@Strain 0.200 %
 58000 psi

@Strain 0.200 %
21.0 MPa

@Strain 0.200 %,
Temperature 1204 °C
 3050 psi

@Strain 0.200 %,
Temperature 2199 °F
30.0 MPa

@Strain 0.200 %,
Temperature 1149 °C
 4350 psi

@Strain 0.200 %,
Temperature 2100 °F
58.0 MPa

@Strain 0.200 %,
Temperature 1093 °C
 8410 psi

@Strain 0.200 %,
Temperature 1999 °F
117 MPa

@Strain 0.200 %,
Temperature 982 °C
 17000 psi

@Strain 0.200 %,
Temperature 1800 °F
207 MPa

@Strain 0.200 %,
Temperature 871 °C
 30000 psi

@Strain 0.200 %,
Temperature 1600 °F
247 MPa

@Strain 0.200 %,
Temperature 760 °C
 35800 psi

@Strain 0.200 %,
Temperature 1400 °F
259 MPa

@Strain 0.200 %,
Temperature 649 °C
 37600 psi

@Strain 0.200 %,
Temperature 1200 °F
274 MPa

@Strain 0.200 %,
Temperature 538 °C
 39700 psi

@Strain 0.200 %,
Temperature 1000 °F
292 MPa

@Strain 0.200 %,
Temperature 427 °C
 42400 psi

@Strain 0.200 %,
Temperature 801 °F
Elongation at Break 49 %
49 %
in 50.8 mm
7.0 %

@Temperature 1288 °C
 7.0 %

@Temperature 2350 °F
 in 50.8 mm
12 %

@Temperature 760 °C
 12 %

@Temperature 1400 °F
 in 50.8 mm
15 %

@Temperature 871 °C
 15 %

@Temperature 1600 °F
 in 50.8 mm
19 %

@Temperature 1260 °C
 19 %

@Temperature 2300 °F
 in 50.8 mm
28 %

@Temperature 649 °C
 28 %

@Temperature 1200 °F
 in 50.8 mm
29 %

@Temperature 1204 °C
 29 %

@Temperature 2199 °F
 in 50.8 mm
36 %

@Temperature 1149 °C
 36 %

@Temperature 2100 °F
 in 50.8 mm
38 %

@Temperature 1093 °C
 38 %

@Temperature 1999 °F
 in 50.8 mm
51 %

@Temperature 982 °C
 51 %

@Temperature 1800 °F
 in 50.8 mm
54 %

@Temperature 427 °C
 54 %

@Temperature 801 °F
 in 50.8 mm
54 %

@Temperature 538 °C
 54 %

@Temperature 1000 °F
 in 50.8 mm
Modulus of Elasticity 200 GPa
29000 ksi
124 GPa

@Temperature 871 °C
 18000 ksi

@Temperature 1600 °F
152 GPa

@Temperature 649 °C
 22000 ksi

@Temperature 1200 °F
152 GPa

@Temperature 760 °C
 22000 ksi

@Temperature 1400 °F
165 GPa

@Temperature 427 °C
 23900 ksi

@Temperature 801 °F
172 GPa

@Temperature 538 °C
 24900 ksi

@Temperature 1000 °F
Poissons Ratio 0.298
0.298
RT
0.315

@Temperature 426 °C
 0.315

@Temperature 799 °F
0.319

@Temperature -78.0 °C
 0.319

@Temperature -108 °F
0.325

@Temperature 650 °C
 0.325

@Temperature 1200 °F
0.339

@Temperature 816 °C
 0.339

@Temperature 1500 °F
Shear Modulus 77.0 GPa
11200 ksi
Calculated
Thermal Properties Metric English Comments
CTE, linear 15.3 µm/m-°C

@Temperature 23.0 - 300 °C
 8.50 µin/in-°F

@Temperature 73.4 - 572 °F
15.6 µm/m-°C

@Temperature 23.0 - 400 °C
 8.67 µin/in-°F

@Temperature 73.4 - 752 °F
16.0 µm/m-°C

@Temperature 23.0 - 500 °C
 8.89 µin/in-°F

@Temperature 73.4 - 932 °F
16.7 µm/m-°C

@Temperature 23.0 - 600 °C
 9.28 µin/in-°F

@Temperature 73.4 - 1110 °F
17.2 µm/m-°C

@Temperature 23.0 - 700 °C
 9.56 µin/in-°F

@Temperature 73.4 - 1290 °F
17.5 µm/m-°C

@Temperature 23.0 - 800 °C
 9.72 µin/in-°F

@Temperature 73.4 - 1470 °F
17.8 µm/m-°C

@Temperature 23.0 - 1000 °C
 9.89 µin/in-°F

@Temperature 73.4 - 1830 °F
17.8 µm/m-°C

@Temperature 23.0 - 900 °C
 9.89 µin/in-°F

@Temperature 73.4 - 1650 °F
18.4 µm/m-°C

@Temperature 23.0 - 1100 °C
 10.2 µin/in-°F

@Temperature 73.4 - 2010 °F
Specific Heat Capacity 0.435 J/g-°C

@Temperature >=100 °C
 0.104 BTU/lb-°F

@Temperature >=212 °F
Thermal Conductivity 15.9 W/m-K

@Temperature 300 °C
 110 BTU-in/hr-ft²-°F

@Temperature 572 °F
17.3 W/m-K

@Temperature 400 °C
 120 BTU-in/hr-ft²-°F

@Temperature 752 °F
18.6 W/m-K

@Temperature 500 °C
 129 BTU-in/hr-ft²-°F

@Temperature 932 °F
20.0 W/m-K

@Temperature 600 °C
 139 BTU-in/hr-ft²-°F

@Temperature 1110 °F
20.0 W/m-K

@Temperature 200 °C
 139 BTU-in/hr-ft²-°F

@Temperature 392 °F
Melting Point 1288 - 1354 °C
2350 - 2469 °F
Solidus 1288 °C
2350 °F
Liquidus 1354 °C
2469 °F
Optical Properties Metric English Comments
Emissivity (0-1) 0.88

@Temperature 1090 °C
 0.88

@Temperature 1990 °F
 Oxidized
Component Elements Properties Metric English Comments
Carbon, C 0.080 - 0.16 %
0.080 - 0.16 %
Cb + Ta 0.75 - 1.25 %
0.75 - 1.25 %
Chromium, Cr 20 - 22.5 %
20 - 22.5 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000930 ohm-cm

@Temperature 22.0 °C
 0.0000930 ohm-cm

@Temperature 71.6 °F