Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 30.0 MPa | 4350 psi | ISO 527 |
Polimeri Europa Eraclene® MP 94 U High Density Polyethylene - Injection Molding Eraclene MP 94 U is a gas phase high density polyethylene homopolymer resin (HDPE) with antioxidants, suitable for injection molding application.This grade has a narrow molecular weight distribution.. |
|||
Tensile Strength, Yield | 30.0 - 50.0 MPa | 4350 - 7250 psi | Compression; ISO 527 |
Raschig Group AMPLA® 2500 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Excellent elasticity and shock resistance, low post-shrinkage, very good electrical values, high heat.. |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM Data |
Americas Styrenics Styron® XL-8023VC High Impact Polystyrene
(discontinued **) STYRON® XL-8023 VC high impact polystyrene is designed to provide molders of VCR cassettes with the impact and gloss they require, at economics and processability highly advantaged over ABS resins... |
|||
Tensile Strength, Yield | 30.0 MPa @Temperature 23.0 °C |
4350 psi @Temperature 73.4 °F |
50 mm/min; ASTM D638 |
Solvay Specialty Polymers Halar® 350LC Polyethylene, Chlorotrifluoroethylene (ECTFE)
(Unverified Data**)& Information provided by Solvay Specialty Polymers. |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | |
LyondellBasell Lupolen® 6021 D HDPE, Blow Molding Grade Easy flow, blow molding grade for small, rigid, thin-walled containers (up to 5 l), pots (up to 1 l), bottles and canisters (up to 5 l) for packaging mineral oil, antifreeze, brake fluid; drink bott.. |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | 50 mm/min; ISO 527-1,-2 |
Inno-Comp INNOPOL® CS 2-3000 Polypropylene Block-Copolymer INNOPOL® CS 2-3000 is a polypropylene block-copolymer compound. This grade is available in nature and custom colored form.INNOPOL® CS 2-3000 is developed for producing injection molded automot.. |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | |
Ineos ABS TRIAX® 1120 ABS/Nylon Blend, Injection Grade, As Conditioned Injection molding grade with good flow and stress corrosion cracking resistance, good chemical resistance (fuel, cleaning agents), high impact and notched impact strength, good acoustical damping be.. |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | |
Ineos ABS Triax® KU 2-3050 ABS + Polyamide Blend (Conditioned) Key Features:UnfilledHigh impact or high impact modifiedLight stabilized or stable to lightHeat stabilized or stable to heatSuitable processing methods:Injection molding |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D638 |
Iran Petrochemical (PCC) 60507 High Density Polyethylene 60507 is a HDPE injection molding grade which combines good flowability with balanced physical properties. This resin is well suited for general purpose applications requiring high stiffness. Applic.. |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | ISO 527 type 1 A |
Solvay TECHNYL® C 442 Black V PA6, Conditioned Description: Unreinforced polyamide PA6, high viscosity, with high flexibility and very high impact resistance even at low temperature, for extrusion.Available in: Europe Product Applications: It ha.. |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON AX01706 ABS LNP* STAT-KON* AX01706 is a compound based on ABS containing proprietary fillers. Added feature of this grade is: Electrically Conductive. |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Halar® 930LCW Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) Medium ViscosityAdditional Properties: Crystallization Heat - ASTM D3418 40.0 J/g; Heat of Fusion - ASTM D3418 42.0 J/g; Thermal Stability - TGA 405 °CInformation provided by Solvay Specialty Pol.. |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Stat-loy A3000Z ABS LNP* Stat-loy* A3000Z is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for t.. |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Stat-loy A3000Z ABS (Asia Pacific) LNP* Stat-loy* A3000Z is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for t.. |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D638 |
Total PPR 6827MZ Polypropylene, Random Copolymer - High Flow Clarified - for Injection Molding Clarity. TOTAL Polypropylene 6827MZ exhibits superior clarity and produces molded parts with improved impact compared with parts molded from homopolymer polypropylene.Antistat. 6827MZ contains an a.. |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | ISO 527-2 |
Total PS CPDS FT875 Flame Retardant Polystyrene POLYSTYRENE (PS) COMPOUND (CPDS) FT875 is a high impact, halogen free flame retardant polystyrene. PS CPDS FT875 offers high heat stability and is recommended for the manufacturing of articles whic.. |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D 638 |
Cossa Polimeri ESTAPROP H 1080 TG Polypropylene, 40% Mineral Filled PP homopolymer 40% mineral fillerExcellent stiffness, good dimensional stabilityInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | 2 in/min, Type IV bar; ASTM D-638 |
Chevron Phillips Marlex® 9514H Polyethylene; HDPE High density polyethylene. This gas phase, high molecular weight hexene copolymer is tailored for lightweight blow molded applications that: Require excellent stiffness to ESCR ratioRequire good m.. |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | cond; ISO 527-1/-2 |
DSM Novamid® ST220 NAT PA6-I Impact Modified, Injection Molding, Medium Viscosity |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® XE 4158 nat PA612 Product description: Grilamid XE 4158 natural is a medium viscosity Polyamide 12 with super high impact strength. The main features of Grilamid XE 4158 natural are: Very good hydrolysis resistanceGo.. |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® LC6200 BK385 Nylon 612
(Unverified Data**) Toughened Polyamide 612 Developed for ExtrusionInformation provided by DuPont Performance Polymers |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0334W40L1 Wollastonite Reinforced |
|||
Tensile Strength, Yield | 30.0 MPa @Temperature 80.0 °C |
4350 psi @Temperature 176 °F |
ASTM Test |
BASF Ultramid® 8202C PA6 (Conditioned) Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique .. |
|||
Tensile Strength, Yield | 30.0 MPa @Temperature 80.0 °C |
4350 psi @Temperature 176 °F |
ISO Data |
BASF Ultramid® 8202C PA6 (Conditioned) Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique .. |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0339M40L Mica Reinforced |
|||
Tensile Strength, Yield | 30.0 - 35.0 MPa | 4350 - 5080 psi | 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 11008 PVDF Copolymer
(discontinued **) Key features of this grade: Low Viscosity, Wire & Cable, Plenum, Formulated. Recommended processing is extrusion. Available as powder & granules.General information about SOLEF® PVDF: SOLEF® PVD.. |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 1068-32 Black40% Mineral Filled Polypropylene DescriptionPolyfort® FPP 1068-32 Black is a 40% mineral filled polypropylene designed for use when improved heat resistance, dimensional stability and high stiffness is needed. ApplicationApplicati.. |
|||
Tensile Strength, Yield | 30.0 MPa | 4350 psi | 2.0 in/min; ASTM D638 |
Ineos Nova 8049 High Performance Styrenic Enhanced Polystyrene
(discontinued **) High gloss at 60°=95; at 20°C=90, Improved scuff resistance, Custom colorsApplications: Injection molding, Cost effective replacement for some ABS applications, Excellent for applications where hi.. |
|||
Tensile Strength, Yield | 30.0 MPa @Temperature 23.0 °C |
4350 psi @Temperature 73.4 °F |
50mm/min; ISO 527-2/1A/50 |
SYNTHOS Krasten® 552M High Impact Polystyrene High impact grade with a wide range of Applications. Processed mainly by injection moulding. Production of consumer goods and technical parts subjected to increased mechanical stress. Good results i.. |