- Polymer Property : Modulus of Elasticity = 24900 ksi
Polymer Property : Modulus of Elasticity = 24900 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 172 GPa @Temperature 400 °C |
24900 ksi @Temperature 752 °F |
|
| Outokumpu 2205 Duplex Stainless Steel Duplex stainless combining high mechanical strength with good corrosion resistance.Applications: Pulp and paper industryDesalination plantsFlue-gas cleaningCargo tanks and pipe systems in chemical t.. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 400 °C |
24900 ksi @Temperature 752 °F |
|
| Outokumpu 4401 Cr-Ni-Mo Austenitic Stainless Steel General purpose steel with excellent corrosion resistance, particularly in the presence of halides.Applications: FiltersBraiding for hydraulic hosesShaftsFastenersMarine componentsAvailable in hot r.. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 400 °C |
24900 ksi @Temperature 752 °F |
|
| Outokumpu 4404 Cr-Ni-Mo Austenitic Stainless Steel General purpose steel with excellent corrosion resistance, particularly in the presence of halides.Applications: FiltersBraiding for hydraulic hosesShaftsFastenersMarine componentsAvailable in hot r.. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 400 °C |
24900 ksi @Temperature 752 °F |
|
| Outokumpu 4429 Cr-Ni-Mo Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), cold rolled strip/sheet and rod forms. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 400 °C |
24900 ksi @Temperature 752 °F |
|
| Outokumpu 4432 Cr-Ni-Mo Austenitic Stainless Steel General purpose steel with excellent corrosion resistance, particularly in the presence of halides.Applications: FiltersBraiding for hydraulic hosesShaftsFastenersMarine componentsAvailable in hot r.. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 400 °C |
24900 ksi @Temperature 752 °F |
|
| Outokumpu 4501 Duplex Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto) form. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 400 °C |
24900 ksi @Temperature 752 °F |
|
| Outokumpu SAF 2507® Duplex Stainless Steel Applications: Pulp and paper industryDesalination plantsFlue-gas cleaningCargo tanks and pipe systems in chemical tankersSeawater systemsFirewalls and blast walls on offshore platformsBridgesCompone.. |
|||
| Modulus of Elasticity | 172 GPa | 24900 ksi | |
| Honeywell Spectra® 1000 Fiber Spectra® fiber 1000, the second in a series of Spectra® fibers, was developed to meet customers’ needs for increased performance. It is available in a multitude of deniers for use in a wi.. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 538 °C |
24900 ksi @Temperature 1000 °F |
|
| Haynes Multimet® alloy, 1.6 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 800 °C |
24900 ksi @Temperature 1470 °F |
|
| Haynes 242® alloy, after 1000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 800 °C |
24900 ksi @Temperature 1470 °F |
|
| Haynes 242® alloy, after 4000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 800 °C |
24900 ksi @Temperature 1470 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 800 °C |
24900 ksi @Temperature 1470 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed, 40% cold work, aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 500 °C |
24900 ksi @Temperature 932 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 500 °C |
24900 ksi @Temperature 932 °F |
|
| Haynes 556® alloy, 10% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 500 °C |
24900 ksi @Temperature 932 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 500 °C |
24900 ksi @Temperature 932 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 500 °C |
24900 ksi @Temperature 932 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 500 °C |
24900 ksi @Temperature 932 °F |
|
| Haynes 556® alloy, all-weld metal GTAW Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 500 °C |
24900 ksi @Temperature 932 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 500 °C |
24900 ksi @Temperature 932 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 500 °C |
24900 ksi @Temperature 932 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 550.0 °C |
24900 ksi @Temperature 1022 °F |
|
| Latrobe CBS-600™ VIM-VAR Carburizing Bearing and Gear Steel CBS-600 VIM-VAR is a carburizing bearing and gear steel designed for service temperatures up to 600°F. Double vacuum melting is employed to provide optimum tensile properties as well as describe.. |
|||
| Modulus of Elasticity | 172 GPa @Temperature 500 °C |
24900 ksi @Temperature 932 °F |
|
| Haynes 556® alloy, 20% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||