- Polymer Property : Tensile Strength, Ultimate = 2610 psi
Polymer Property : Tensile Strength, Ultimate = 2610 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 18.0 MPa | 2610 psi | ASTM D638 |
| NCMT NanoPAC™ S205 High Performance Polypropylene Nanocomposite Characteristics: High stiffness Supplementary of ABS Good impact resistant Less shrinkage Good thermal conductivity Applications: Toys Industry AutomobileInformation provided by Nano Composite Mater.. |
|||
| Tensile Strength, Ultimate | 18.0 MPa | 2610 psi | ISO 527 |
| Premix Thermoplastics PRE-ELEC® PP 1370 PRE-ELEC PP 1370 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELE.. |
|||
| Tensile Strength, Ultimate | 18.0 MPa | 2610 psi | |
| Reliance Industries BIOMER P240 compared to LDPE, HDPE, PHBInformation provided by Reliance Industries |
|||
| Tensile Strength, Ultimate | 18.0 MPa | 2610 psi | |
| 3M Dyneon™ Fluorel™ FC-2144 Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. Higher viscosity version of FC-2123. .. |
|||
| Tensile Strength, Ultimate | 18.0 MPa | 2610 psi | |
| 3M Dyneon™ Fluorel™ FC-2181 Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. Combines high elongation with excelle.. |
|||
| Tensile Strength, Ultimate | 18.0 - 18.0 MPa @Temperature 60.0 - 60.0 °C |
2610 - 2610 psi @Temperature 140 - 140 °F |
Average value: 18.0 MPa Grade Count:1 |
| Overview of materials for Polystyrene, Heat Resistant Grade This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Heat Resistant Grade". Each property range of values reported is minimum and maximum values.. |
|||
| Tensile Strength, Ultimate | 18.0 MPa | 2610 psi | ASTM Data |
| Americas Styrenics Styron® 489M High Impact Polystyrene
(discontinued **) STYRON® 489M high impact polystyrene resin is a high flow resin with excellent impact. When used unmodified for the manufacture of food contact articles STYRON 489M complies with the US Food, Drug .. |
|||
| Tensile Strength, Ultimate | 18.0 MPa @Temperature 60.0 °C |
2610 psi @Temperature 140 °F |
ISO 527 |
| LATI LASTIROL TR-V0 Polystyrene (PS) (UL94 V-0)
(discontinued **) Description: Lastirol thermoplastics are polystyrene (PS) products. The Lastirols feature excellent dimensional stability, good flowability, and can be molded without any particular problem. Glass f.. |
|||
| Tensile Strength, Ultimate | 18.0 MPa @Temperature 120 °C |
2610 psi @Temperature 248 °F |
ISO 527 |
| LATI LATAN 13 Medium Viscosity Polyoxymethylene Copolymer (POM)
(Unverified Data**) Description: Latan series thermoplastics are polyoxymethylene copolymer (POM) products. The main applications for Latan feature good wear resistance, chemical inertness and low water absorption (gea.. |
|||
| Tensile Strength, Ultimate | 18.0 - 34.0 MPa @Temperature 100 - 100 °C |
2610 - 4930 psi @Temperature 212 - 212 °F |
Average value: 26.5 MPa Grade Count:2 |
| Overview of materials for Polytetrafluoroethylene (PTFE), Glass Filled, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Glass Filled, Molded". Each property range of values reported is minimum.. |
|||
| Tensile Strength, Ultimate | 18.0 - 34.0 MPa | 2610 - 4930 psi | Average value: 21.5 MPa Grade Count:11 |
| Overview of materials for Fluorinated Ethylene Propylene (FEP), Molded/Extruded This property data is a summary of similar materials in the MatWeb database for the category "Fluorinated Ethylene Propylene (FEP), Molded/Extruded". Each property range of values reported is minimu.. |
|||
| Tensile Strength, Ultimate | 18.0 MPa @Temperature 90.0 °C |
2610 psi @Temperature 194 °F |
ISO 527 |
| LATI LATAMID 12 H FE90 Nylon 12 Base Magnetizable Compound
(Unverified Data**) Description: These are compounds containing a high percentage of magnetizable fillers; compared to traditional techniques for the manufacture of magnets, this allows the molding of complex shapes us.. |
|||
| Tensile Strength, Ultimate | 18.0 MPa | 2610 psi | |
| Freudenberg Simrit Simriz® 486 Universal FFKT Perfluoroelastomer Compound Perfluoro elastomers – or FFKM for short – have an ideal combination of characteristics, with their excellent chemical resistance, high level of temperature resistance, and high levels of .. |
|||
| Tensile Strength, Ultimate | 18.0 MPa | 2610 psi | ASTM D638 |
| LyondellBasell Astryn 75F4-4 Polypropylene Copolymer, 40% Talc Key Features: conventional melt flow, high modulus, mineral-filled polypropylene copolymer, high strength, high stiffness, good aestheticsApplications: small appliances, electrical components, house.. |
|||
| Tensile Strength, Ultimate | 18.0 MPa @Temperature 1288 °C |
2610 psi @Temperature 2350 °F |
|
| Haynes Multimet® alloy, 1.6 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Tensile Strength, Ultimate | 18.0 MPa | 2610 psi | Type IV, crosshead speed 2 in/min; ASTM D638 |
| DuPont Elvax® 660 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
| Tensile Strength, Ultimate | 18.0 - 34.0 MPa | 2610 - 4930 psi | ASTM D638 |
| Zeus FEP Tubing FEP, fluorinated ethylene propylene, is a melt processable fluoropolymer that allows for long, continuous lengths and has several distinct advantages over PTFE. Applications where FEP tubing is usua.. |
|||
| Tensile Strength, Ultimate | 18.0 MPa | 2610 psi | Type IV, crosshead speed 2 in/min; ASTM D638 |
| DuPont Elvax® 360 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
| Tensile Strength, Ultimate | 18.0 MPa | 2610 psi | ISO 527-1 |
| Chengdu Polyster FH2040 Thermoplastic Polyether-ester Elastomer (TPEE) Blend of H2040 and self-made flame retardant material. Excellent flex resistance at low temperatures. Excellent flex-fatigue resistance. Applications requiring flexibility at low temperatures and fl.. |
|||
| Tensile Strength, Ultimate | 18.0 MPa | 2610 psi | ISO 527-1 |
| Chengdu Polyster H3303 Thermoplastic Polyether-ester Elastomer (TPEE) Low modulus molding and injection grade. Contains improved color- stable antioxidants. Excellent flex resistance at low temperatures. Moldable even in thin sections. Can be used in light-colored pro.. |
|||
| Tensile Strength, Ultimate | 18.0 MPa | 2610 psi | ISO 527-1 |
| Chengdu Polyster H3303B Thermoplastic Polyether-ester Elastomer (TPEE) Low modulus molding and extrusion grade. Contains color-stable antioxidants. Excellent low-temperature properties. Excellent flex-fatigue resistance. Excellent creep resistance. CVJ boots, hose jack.. |
|||
| Tensile Strength, Ultimate | 18.0 MPa | 2610 psi | |
| Dow DOWLEX™ IP-10 High Density Polyethylene Next Generation DOWLEX® IP-10 resin is a high density polyethylene resin specifically designed for reusable case applications including, poultry, fast food, automotive, retail, fresh produce, bever.. |
|||
| Tensile Strength, Ultimate | 18.0 - 20.0 MPa | 2610 - 2900 psi | |
| Biomer P240 PHB Biodegradable Polymer PHB is a isotactic, absolutely linear, thermoplastic homopolyester built of 3-hydroxy butyric acid. The formula of the subunit is -[O-CH(CH3)-CH2-CO]-. PHB is free from even traces of catalysts. P.. |
|||
| Tensile Strength, Ultimate | 18.0 - 38.0 MPa | 2610 - 5510 psi | Average value: 32.9 MPa Grade Count:59 |
| Overview of materials for High Density Polyethylene (HDPE), Pipe Grade This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Pipe Grade". Each property range of values reported is minimum and max.. |
|||
| Tensile Strength, Ultimate | 18.0 - 40.0 MPa @Temperature 60.0 - 120 °C |
2610 - 5800 psi @Temperature 140 - 248 °F |
Average value: 29.3 MPa Grade Count:1 |
| Overview of materials for Polypropylene with Glass Fiber + Bead Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with Glass Fiber + Bead Filler". Each property range of values reported is minimum and max.. |
|||
| Tensile Strength, Ultimate | 18.0 MPa | 2610 psi | ASTM D412 |
| KKPC KOSYN KTR 302 Thermoplastic Elastomer (TPE) Thermoplastic Elastomer (TPE)Characteristics: KOSYN KTR101 is linear block copolymer made by solution polymerization which polymerizes butadiene and styrene in organic solvent. It is thermoplastics .. |
|||
| Tensile Strength, Ultimate | 18.0 MPa | 2610 psi | |
| 3M Dyneon™ Fluorel™ FLS-2650 Fluoroelastomer VF2 + HFP + TFE Terpolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Non-incorporated cure polymer, 70.3%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, 1.8% Luperco™ 101XL Peroxide, and 2.5 % Triallyl .. |
|||
| Tensile Strength, Ultimate | 18.0 MPa | 2610 psi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| DuPont Performance Polymers VTR 8605 (GF-S) Peroxide Cured Fluoroelastomer (FKM) Formulation
(discontinued ** FormulationVTR 8605 |
|||