Polymer Resources PPX/NY GP2 Modified PPO, Medium Heat PPX/Nylon 6,6 Alloy (Unverified Data**)

Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Molded
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polymer Resources PPX/NY GP2 Modified PPO, Medium Heat PPX/Nylon 6,6 Alloy (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.

Physical Properties	Metric	English	Comments
Density	1.10 g/cc	0.0397 lb/in³	ASTM D792
Linear Mold Shrinkage	0.010 - 0.013 cm/cm	0.010 - 0.013 in/in	ASTM D955
Melt Flow	10 - 30 g/10 min	10 - 30 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	55.2 MPa	8000 psi	ASTM D638
Tensile Strength, Yield	57.9 MPa	8400 psi	ASTM D638
Flexural Strength	8.96 MPa	1300 psi	ASTM D790
Flexural Modulus	2.07 GPa	300 ksi	ASTM D790
Izod Impact, Notched	1.87 J/cm	3.50 ft-lb/in	ASTM D256
Gardner Impact	>= 28.2 J	>= 20.8 ft-lb	ASTM D3029

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	154 °C	310 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	129 °C	265 °F	ASTM D648

Processing Properties	Metric	English
Rear Barrel Temperature	266 - 302 °C	510 - 575 °F
Middle Barrel Temperature	271 - 302 °C	520 - 575 °F
Front Barrel Temperature	277 - 302 °C	530 - 575 °F
Melt Temperature	279 - 302 °C	535 - 575 °F
Mold Temperature	76.7 - 121 °C	170 - 250 °F
Drying Temperature	93.3 - 107 °C	200 - 225 °F
Dry Time	3 - 5 hour	3 - 5 hour