Polymer Property : Tensile Strength at Break = 55.2 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.2 MPa
8000 psi
2 in/min; ASTM D638
RheTech Products F43-01 35% Glass Fiber/Mineral Co-Reinforced Polypropylene Copolymer, Chemically Coupled, Black
Applications: Fan shroudsDip trayFunctional supportsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 55.2 MPa
8000 psi
2 in/min; ASTM D638
RheTech Products G13P100-347UV 13% Glass Fiber Reinforced Polypropylene, UV Stabilized, 109D Medium Pewter
Applications: Dome lamp housingsFuel filler pocketInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 55.2 MPa
8000 psi
2 in/min; ASTM D638
RheTech Products G13P100-553UV 13% Glass Fiber Reinforced Polypropylene, UV Stabilized, (GM 501F) Dark Smoke Gray
Applications: Interior trimAir ducts - distributionFuel filler pocketInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break 55.2 MPa
8000 psi
ASTM D638
Polymer Resources PC-GP3-TFE10 Polycarbonate, 10% PTFE, High Flow, Wear Resistant
Polycarbonate, General Purpose, High Flow, Wear ResistantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informa..
Tensile Strength at Break 55.2 MPa
8000 psi
ASTM D638
Polymer Resources PC-IM1 Polycarbonate, Impact Modified, Low Flow
Polycarbonate, Impact Modified, Low FlowProcess: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided ..
Tensile Strength at Break 55.2 MPa
8000 psi
ASTM D638
Polymer Resources PC-IM1-UV Polycarbonate, Impact Modified, Low Flow, UV-stabilized
Polycarbonate, Impact Modified, Low Flow, UV-stabilizedProcess: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inform..
Tensile Strength at Break 55.2 MPa
8000 psi
ASTM D638
Polymer Resources PPX/NY GP2 PPO/Nylon 66 Alloy, Medium Heat
Polyphenylene Oxide/Nylon 66 Alloy , General Purpose, Medium HeatProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples..
Tensile Strength at Break 55.2 MPa
8000 psi
ASTM D638
Polymer Resources PPX-GP1-[color]EN Modified PPO, Extrusion Grade with HDT of 265 F
Process: Extrusion Notes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Tensile Strength at Break 55.2 MPa
8010 psi
ASTM D 638
NOVA Chemicals Dylark® FG7300 High-Heat Styrenic Copolymer
Product Description and Features: Styrene/maleic anhydride copolymer with high-heat resistance and high modulus. Resins designed for use in foam extrusion.Processing: Contact NOVA Chemicals techn..
Tensile Strength at Break 55.2 MPa
8000 psi
ASTM D638
Polymer Resources PPX-GP1 Modified PPO, General Purpose with HDT of 265 F  (Unverified Data**)
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Tensile Strength at Break 55.2 MPa

@Thickness 50.8 mm
8000 psi

@Thickness 2.00 in
ASTM D638
Teknor Apex Synres® PP G10 17 Polypropylene, Glass Reinforced
Notes: The Specialty Compounding Division offers a proprietary line of glass reinforced polypropylene. Typical applications include automotive, building and construction, industrial as well as many ..
Tensile Strength at Break 55.2 MPa
8000 psi
Abatron AboCast 8103-21 High-Performance Dielectric Epoxy
AboCast 8103-21 is a dielectric in/outdoor epoxy system with superior arc-track resistance, high voltage and heat resistance, low ash and ion content, and it is chlorine-free. This system combines r..
Tensile Strength at Break 55.2 MPa
8000 psi
2.0 in/min; ASTM D638
LTL Color Compounds ColorFast® FRPC100 Polycarbonate, Flame-Retarded
Flame-retarded V0, high impact injection molding polycarbonateAll information provided by LTL Color Compounders, Inc.
Tensile Strength at Break 55.2 MPa
8000 psi
2.0 in/min; ASTM D638
LTL Color Compounds ColorFast® FRPC400 Polycarbonate, Flame-Retarded
Flame-retarded V0, high impact injection molding polycarbonateAll information provided by LTL Color Compounders, Inc.