- Polymer Property : Melt Flow = 30 g/10 min
Polymer Property : Melt Flow = 30 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 20 - 30 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 - 30 g/10 min @Load 4.76 lb, Temperature 446 °F |
STN EN ISO 1133 |
| Plastcom PLASTALEN® PQ 81 N 003 Polypropylene with improved impact strength PP copolymer regranulate for injection molding, impact modified. General use in all industry branches. Delivered in natural mode and in the full RAL color scale.Information Provided by Plastcom spol.. |
|||
| Melt Flow | 25 - 30 g/10 min @Load 5.00 kg, Temperature 190 °C |
25 - 30 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| Polyplastic Armoflen® PO MF 65-4 Polypropylene, 65% Calcium Carbonate Information provided by PolyPlastic Group. |
|||
| Melt Flow | 15 - 30 g/10 min @Load 2.16 kg, Temperature 210 °C |
15 - 30 g/10 min @Load 4.76 lb, Temperature 410 °F |
ASTM D1238 |
| NatureWorks® Ingeo™ 6202D Fiber Grade PLA NatureWorks® PLA polymer 6202D is a thermoplastic fiber-grade resin derived primarily from annually renewable resources. Available in pellet form, 6202D is designed for extrusion into mechanically .. |
|||
| Melt Flow | 20 - 30 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 - 30 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238/L |
| NIZHNEKAMSKNEFTEKHIM PP 1362R (Z21S) Propylene Homopolymer Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance when P.. |
|||
| Melt Flow | 20 - 30 g/10 min @Load 1.20 kg, Temperature 300 °C |
20 - 30 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PC-FD4-[color]-1 Polycarbonate, FDA-compliant Feedstocks, Easy Flow with Mold Release, Gamma Resistant Polycarbonate, FDA-compliant Feedstocks, Easy Flow with Mold Release, Gamma ResistantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pig.. |
|||
| Melt Flow | 18 - 30 g/10 min @Load 1.20 kg, Temperature 300 °C |
18 - 30 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PC-GP4-[color]-1 Polycarbonate, General Purpose, Easy Flow with Mold Release Polycarbonate, General Purpose, Easy Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Infor.. |
|||
| Melt Flow | 18 - 30 g/10 min @Load 1.20 kg, Temperature 300 °C |
18 - 30 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PC-GP4-[color]-3 Polycarbonate, UV-stabilized, Easy Flow Polycarbonate, UV-stabilized, Easy FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by P.. |
|||
| Melt Flow | 18 - 30 g/10 min @Load 1.20 kg, Temperature 300 °C |
18 - 30 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PC-GP4-[color]-5 Polycarbonate, FDA-compliant Feedstocks, Easy Flow Polycarbonate, FDA-compliant Feedstocks, Easy FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr.. |
|||
| Melt Flow | 20 - 30 g/10 min @Load 1.20 kg, Temperature 300 °C |
20 - 30 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PC-IM4 Polycarbonate, Impact Modified, Easy Flow Polycarbonate, Impact Modified, Easy FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by.. |
|||
| Melt Flow | 10 - 30 g/10 min @Load 3.80 kg, Temperature 300 °C |
10 - 30 g/10 min @Load 8.38 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PPX/NY GP2 PPO/Nylon 66 Alloy, Medium Heat Polyphenylene Oxide/Nylon 66 Alloy , General Purpose, Medium HeatProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.. |
|||
| Melt Flow | 20 - 30 g/10 min @Load 11.6 kg, Temperature 250 °C |
20 - 30 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources PPX-GP4 Modified-PPO, General Purpose Modified-Polyphenylene Oxide, General Purpose, 210F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati.. |
|||
| Melt Flow | 20 - 30 g/10 min @Load 11.6 kg, Temperature 250 °C |
20 - 30 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources PPX-GP4-IM Modified-PPO, Impact Modified Modified-Polyphenylene Oxide, Impact Modified, 210F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati.. |
|||
| Melt Flow | 20 - 30 g/10 min | 20 - 30 g/10 min | ASTM D1238 |
| Polymer Resources PPX-GP4 Modified PPO, General Purpose with HDT of 210 F
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Melt Flow | 10 - 30 g/10 min @Load 2.16 kg, Temperature 170 °C |
10 - 30 g/10 min @Load 4.76 lb, Temperature 338 °F |
ISO 1133 |
| Lubrizol Advanced Materials PEARLBOND® 106 Linear Thermoplastic Polyurethane Pearlbond™ 106.is a linear, aromatic polyurethane, supplied in form of small white or slightly yellowish granules, which combines a high crystallisation rate with a very high thermoplasticity l.. |
|||
| Melt Flow | 15 - 30 g/10 min @Load 2.16 kg, Temperature 170 °C |
15 - 30 g/10 min @Load 4.76 lb, Temperature 338 °F |
ISO 1133 |
| Lubrizol Advanced Materials PEARLBOND® 520 Linear Thermoplastic Polyurethane Pearlbond™ 520 is a linear, polycaprolactone-copolyester polyurethane, supplied in form of white spherical granules with a very high crystallization rate and a very high thermoplasticity level... |
|||
| Melt Flow | 10 - 30 g/10 min @Load 2.16 kg, Temperature 177 °C |
10 - 30 g/10 min @Load 4.76 lb, Temperature 351 °F |
|
| Taiwan Sheen Soon Sheenthane® AH-592 TPU for Hotmelt Adhesive Thermoplastic polyurethane elastomer for soft hotmelt adhesiveExcellent bonding strength for polyester, TPU, nylon, PVC, leather, fabrics, etc. Melt flow may be customized. Used for hot melt adhes.. |
|||
| Melt Flow | 20 - 30 g/10 min @Temperature 230 °C |
20 - 30 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
| A. Schulman POLYFORT™ FPP 1007X Extra High Flow, Talc Fortified Homopolymer Polypropylene DescriptionPolyfort® FPP 1007X is an extra high flow, 40% talc fortified homopolymer polypropylene. Information provided by A. Schulman. |
|||
| Melt Flow | 20 - 30 g/10 min @Temperature 230 °C |
20 - 30 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
| A. Schulman POLYFORT™ PP 2175HU Toyota High Flow Copolymer Polypropylene DescriptionPolyfort® PP 2175HU Toyota is a high flow copolymer polypropylene.Information provided by A. Schulman. |
|||
| Melt Flow | 20 - 30 g/10 min @Temperature 230 °C |
20 - 30 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
| A. Schulman POLYFORT™ FPP 1007X Extra High Flow, Talc Fortified Homopolymer Polypropylene DescriptionPolyfort® FPP 1007X is an extra high flow, 40% talc fortified homopolymer polypropylene. Information provided by A. Schulman. |
|||
| Melt Flow | 20 - 30 g/10 min @Temperature 230 °C |
20 - 30 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
| A. Schulman POLYFORT™ PP 2175HU Toyota High Flow Copolymer Polypropylene DescriptionPolyfort® PP 2175HU Toyota is a high flow copolymer polypropylene.Information provided by A. Schulman. |
|||
| Melt Flow | 20 - 30 g/10 min @Temperature 230 °C |
20 - 30 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
| A. Schulman POLYFORT™ PP 2175HU-31 High Flow Copolymer Polypropylene DescriptionPolyfort® PP 2175HU-31 is a high flow copolymer polypropylene.Information provided by A. Schulman. |
|||
| Melt Flow | 20 - 30 g/10 min @Temperature 230 °C |
20 - 30 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
| A. Schulman POLYFORT™ FPP 1007X Extra High Flow, Talc Fortified Homopolymer Polypropylene DescriptionPolyfort® FPP 1007X is an extra high flow, 40% talc fortified homopolymer polypropylene. Information provided by A. Schulman. |
|||
| Melt Flow | 20 - 30 g/10 min @Temperature 230 °C |
20 - 30 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
| A. Schulman POLYFORT™ PP 2175HU Toyota High Flow Copolymer Polypropylene DescriptionPolyfort® PP 2175HU Toyota is a high flow copolymer polypropylene.Information provided by A. Schulman. |
|||
| Melt Flow | 20 - 30 g/10 min @Temperature 230 °C |
20 - 30 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
| A. Schulman POLYFORT™ PP 2175HU Toyota High Flow Copolymer Polypropylene DescriptionPolyfort® PP 2175HU Toyota is a high flow copolymer polypropylene.Information provided by A. Schulman. |
|||
| Melt Flow | 20 - 30 g/10 min @Temperature 230 °C |
20 - 30 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
| A. Schulman POLYFORT™ PP 2175HU-31 High Flow Copolymer Polypropylene DescriptionPolyfort® PP 2175HU-31 is a high flow copolymer polypropylene.Information provided by A. Schulman. |
|||
| Melt Flow | 20 - 30 g/10 min @Load 5.00 kg, Temperature 372 °C |
20 - 30 g/10 min @Load 11.0 lb, Temperature 702 °F |
|
| Daikin NEOFLON AP-201SH PFA Semiconductor Grade NEOFLON PFA semiconductor grade.Applications: Good fluidity, suited to making moldings of complex shapes, requiring high fluidity.Information provided by Daikin Industries. |
|||
| Melt Flow | 20 - 30 g/10 min @Load 5.00 kg, Temperature 265 °C |
20 - 30 g/10 min @Load 11.0 lb, Temperature 509 °F |
ASTM D1238 |
| Covestro Makroblend® EL 703 Polycarbonate + Polyester-based Blend, Impact Modified, Flame-Retardant, UV Stabilized Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
| Melt Flow | 4.0 - 30 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 - 30 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Aaron Industries AAROLENE® ARPP H 200-1 Polypropylene Compounded Resin AAROLENE® ARPP 200 Series Polypropylene Compounded ResinColor may be specified. Melt Flow Index may be specified. |
|||
| Melt Flow | 25 - 30 g/10 min | 25 - 30 g/10 min | ASTM D1238 |
| Polymer Resources AC-GP3 Acetal Copolymer, High Flow, Thin Walled Molding
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Melt Flow | 20 - 30 g/10 min @Temperature 230 °C |
20 - 30 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
| A. Schulman POLYFORT™ FPP 1007X Extra High Flow, Talc Fortified Homopolymer Polypropylene DescriptionPolyfort® FPP 1007X is an extra high flow, 40% talc fortified homopolymer polypropylene. Information provided by A. Schulman. |
|||