BASF Ultramid® HPN 9362 40% Mineral Filled PA6 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® HPN 9362 40% Mineral Filled PA6 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid HPN 9362 is a 40% mineral reinforced, impact modified nylon 6 injection molding compound. It is one of the High Productivity Nylon series having improved surface appearance while reducing cycle time. It possesses excellent balance of strength, stiffness and toughness combined with a high level of drop weight impact, excellent processability and chemical resistance to greases, oils and hydrocarbons.
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
dry; ISO 1183
Water Absorption 4.9 %
4.9 %
beginning dry; ISO 62
Moisture Absorption at Equilibrium 1.4 %
1.4 %
beginning dry (23°C/50% R.H.); ISO 62
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa
6530 psi
0.2 in/min; ASTM Test
20.0 MPa

@Temperature 120 °C
2900 psi

@Temperature 248 °F
ISO Data
20.0 MPa

@Temperature 120 °C
2900 psi

@Temperature 248 °F
ASTM Test
25.0 MPa

@Temperature 80.0 °C
3630 psi

@Temperature 176 °F
ASTM Test
25.0 MPa

@Temperature 80.0 °C
3630 psi

@Temperature 176 °F
ISO Data
95.0 MPa

@Temperature -40.0 °C
13800 psi

@Temperature -40.0 °F
ASTM Test
95.0 MPa

@Temperature -40.0 °C
13800 psi

@Temperature -40.0 °F
ISO Data
Tensile Strength, Yield 45.0 MPa
6530 psi
2 in/min; ASTM Test
45.0 MPa
6530 psi
50mm/min; ISO 527
20.0 MPa

@Temperature 120 °C
2900 psi

@Temperature 248 °F
ISO Data
20.0 MPa

@Temperature 120 °C
2900 psi

@Temperature 248 °F
ASTM Test
25.0 MPa

@Temperature 80.0 °C
3630 psi

@Temperature 176 °F
ASTM Test
25.0 MPa

@Temperature 80.0 °C
3630 psi

@Temperature 176 °F
ISO Data
90.0 MPa

@Temperature -40.0 °C
13100 psi

@Temperature -40.0 °F
ASTM Test
90.0 MPa

@Temperature -40.0 °C
13100 psi

@Temperature -40.0 °F
ISO Data
Elongation at Break 30 %
30 %
50mm/min, Nominal strain; ISO 527
30 %
30 %
2 in/min; ASTM Test
30 %
30 %
0.2 in/min; ASTM Test
9.0 %

@Temperature -40.0 °C
9.0 %

@Temperature -40.0 °F
ASTM Test
9.0 %

@Temperature -40.0 °C
9.0 %

@Temperature -40.0 °F
ISO Data
25 %

@Temperature 120 °C
25 %

@Temperature 248 °F
ISO Data
25 %

@Temperature 120 °C
25 %

@Temperature 248 °F
ASTM Test
40 %

@Temperature 80.0 °C
40 %

@Temperature 176 °F
ASTM Test
40 %

@Temperature 80.0 °C
40 %

@Temperature 176 °F
ISO Data
Elongation at Yield 27 %
27 %
2 in/min; ASTM Test
27 %
27 %
50mm/min; ISO 527
5.1 %

@Temperature -40.0 °C
5.1 %

@Temperature -40.0 °F
ISO Data
5.1 %

@Temperature -40.0 °C
5.1 %

@Temperature -40.0 °F
ASTM Test
25 %

@Temperature 80.0 °C
25 %

@Temperature 176 °F
ASTM Test
25 %

@Temperature 120 °C
25 %

@Temperature 248 °F
ISO Data
30 %

@Temperature 80.0 °C
30 %

@Temperature 176 °F
ISO Data
30 %

@Temperature 120 °C
30 %

@Temperature 248 °F
ASTM Test
Tensile Modulus 2.90 GPa
421 ksi
1mm/min; ISO 527
0.600 GPa

@Temperature 120 °C
87.0 ksi

@Temperature 248 °F
ISO Data
0.860 GPa

@Temperature 80.0 °C
125 ksi

@Temperature 176 °F
ISO Data
6.60 GPa

@Temperature -40.0 °C
957 ksi

@Temperature -40.0 °F
ISO Data
Flexural Strength 50.0 MPa
7250 psi
ASTM Test
25.0 MPa

@Temperature 120 °C
3630 psi

@Temperature 248 °F
ASTM Test
30.0 MPa

@Temperature 93.0 °C
4350 psi

@Temperature 199 °F
ASTM Test
35.0 MPa

@Temperature 65.0 °C
5080 psi

@Temperature 149 °F
ASTM Test
155 MPa

@Temperature -40.0 °C
22500 psi

@Temperature -40.0 °F
ASTM Test
Flexural Modulus 1.56 GPa
226 ksi
ASTM Test
0.740 GPa

@Temperature 120 °C
107 ksi

@Temperature 248 °F
ASTM Test
0.850 GPa

@Temperature 93.0 °C
123 ksi

@Temperature 199 °F
ASTM Test
0.970 GPa

@Temperature 65.0 °C
141 ksi

@Temperature 149 °F
ASTM Test
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Processing Properties Metric English Comments
Melt Temperature 275 °C
527 °F
Injection molding
Mold Temperature 95.0 °C
203 °F
Injection molding
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Form Pellets
Impact Modified Yes
Primary Processing Technique Injection Molding
Processing Injection Molding