Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 35.0 MPa | 5080 psi | |
Plastcom SLOVALEN PC 12 T 30 TS PP reinforced with 30% mineral filler Features: Modified copolymer PP for injection moulding or extrusion parts with the content of 30 % mineral filler. Increased rigidity, strength and impact strenght.Delivered in natural mode and in t.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | |
Plastcom SLOVALEN PC 13 T 30 PP, 30% mineral filling FeaturesModified copolymer PP for injection moulding or extrusion parts with the content of 30 % mineral filler. Increased rigidity, strength and impact strenght.Delivered in natural mode and in the.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | |
Plastcom SLOVALEN PC 16 FRD 1 PP, flame retardant Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.0.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | |
Plastcom SLOVALEN PQ 81 T 25 PP, 25% mineral filling FeaturesModified PP for injection moulding with the content of 25% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased shri nkage. Gen.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | 2 mm/min; ISO 178 |
Polimeri Europa Edistir ICE R 830D Polystyrene Environmental stress cracking resistant (ESCR) HIPS. ICE PD R 830D combines high impact strength with an improved chemical resistance to oils, fats and chemical agents, such as detergents for both i.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ASTM D790 |
SABIC PS 325 High Impact Polystyrene for Injection Molding Product Description: High Impact Polystyrene PS 325 is manufactured by continuous mass polymerization of styrene monomer. An elastomer is incorporated during polymerization to achieve impact resis.. |
|||
Flexural Strength | <= 35.0 MPa | <= 5080 psi | ISO 178 |
Polykemi AB POLYfill PP CIQ10015ER UV Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 35.0 - 45.0 MPa | 5080 - 6530 psi | ASTM D790-03 |
Proto3000 Objet Digital Materials™ DM_8430 Polypropylene-like Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide.. |
|||
Flexural Strength | 35.0 - 45.0 MPa | 5080 - 6530 psi | ASTM D790-03 |
Proto3000 Objet Digital Materials™ DM_8530_Gray60 Polypropylene-like Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoBlackPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to pr.. |
|||
Flexural Strength | <= 35.0 MPa | <= 5080 psi | ISO 178 |
Polykemi AB POLYfill PPC K5025 PP, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ISO 178 |
Nilit FRIANYL A63 CU90 Nylon 6.6 for injection molding, 90% copper filled Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | >= 35.0 MPa | >= 5080 psi | ASTM D790 |
NIZHNEKAMSKNEFTEKHIM 825ES High Impact Polystyrene Grade 825ES is a high impact polystyrene designed for extrusion and hot molding application. It is suited for hot molded deep drawn industrial packages and multilayer shaped sheet production via ex.. |
|||
Flexural Strength | <= 35.0 MPa | <= 5080 psi | ISO 178 |
Polykemi AB POLYfill PPH B8065 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ISO 178 |
Fiberfil® M-2450 BK9083 Polypropylene Copolymer, 20% Talc Information provided by FIBERFIL Engineered Plastics |
|||
Flexural Strength | 35.0 MPa @Temperature 23.0 °C |
5080 psi @Temperature 73.4 °F |
2mm/min; 80x10x4mm; ISO 178 |
SYNTHOS Krasten® 662E High Impact Polystyrene High impact grade with properties suitable for thermoforming. Processed mainly by extrusion and thermoforming. Production of demanding visual appearance plates, technical parts, sheets and molded pa.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-LOY KX95702 Acetal LNP STAT-LOY* KX95702 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Antistat. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP M7001XXH PP LNP* THERMOCOMP* M7001XXH is a compound based on Polypropylene resin containing proprietary antimicrobial additves. Designed for touch surfaces in patient critical healthcare applications. Added f.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP M7002XXH PP LNP* THERMOCOMP* M7002XXH is a compound based on Polypropylene resin containing proprietary antimicrobial additives. Designed for touch surfaces in healthcare applications. Added features include:.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | 2 mm/min; ISO 178 |
Chi Mei Polyrex® PH-88 Polystyrene - High Impact High impact |
|||
Flexural Strength | 35.0 MPa | 5080 psi | cond.; ISO 178 |
Azoty Tarnow™ Tarnamid® T-27 MCS V2 Polyamide 6 - Flame Retarded, Unreinforced Flame retarded (class V2), bromine and red phosphorus free, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has th.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ISO 178 |
Ascend Performance Materials Vydyne® 20NSP Nylon 66, Conditioned Vydyne® 20NSP is a general-purpose, highly nucleated, lubricated PA66 resin available in natural color. It is designed to crystallize rapidly in order to reduce cycle times and increase productivit.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ASTM Test |
BASF Ultramid® 8202 PA6 (Conditioned) Ultramid 8202 is a low viscosity, general purpose polyamide 6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is also available in heat stabilized (Ult.. |
|||
Flexural Strength | 35.0 MPa @Temperature 65.0 °C |
5080 psi @Temperature 149 °F |
ASTM Test |
BASF Ultramid® HPN 9362 40% Mineral Filled PA6 (Conditioned) Ultramid HPN 9362 is a 40% mineral reinforced, impact modified nylon 6 injection molding compound. It is one of the High Productivity Nylon series having improved surface appearance while reducing c.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | |
Biomer P226 PHB Biodegradable Polymer PHB is a isotactic, absolutely linear, thermoplastic homopolyester built of 3-hydroxy butyric acid. The formula of the subunit is -[O-CH(CH3)-CH2-CO]-. PHB is free from even traces of catalysts. P.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ASTM D790 |
Aclo Accutech Polypropylene CP0409HUUVV Copolymer UV Stabilized Approved to Suzuki PP-S3 Med Grey T01 |
|||
Flexural Strength | 35.0 MPa | 5080 psi | cond.; ISO 178 |
Azoty Tarnow™ Tarnamid® T-27 MCS 850 Polyamide 6 - Flame Retarded, Unreinforced Glow wire resistance 850°C, bromine and red phosphorus free, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has .. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ASTM D790 |
Teknor Apex Sinelec CCB6814 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Features: Electrically Conductive Uses: Corrugated Sheet Forms: Pellets Processing Method: Injection Method; Sheet Extr.. |
|||
Flexural Strength | <= 35.0 MPa | <= 5080 psi | ISO 178 |
Polykemi AB POLYfill PPC T1020 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ISO 178 |
Ascend Performance Materials Vydyne® 20NSP BLK Nylon 66, Conditioned Vydyne® 20NSP BLK is a general-purpose, high nucleated, lubricated PA66 resin. Available in black, it is designed to crystallize rapidly in order to reduce cycle times and increase productivity thr.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ISO 178 |
Ascend Performance Materials Vydyne® 20NSP1 Nylon 66, Conditioned Availability:Asia PacificEuropeNorth AmericaAdditive:LubricantNucleating Agent Features: Fast Molding CycleGeneral PurposeGood Mold ReleaseGood StiffnessHigh RigidityLubricatedNucleatedUses:Bearings.. |