Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 25.0 MPa | 3630 psi | ISO 527 |
Murtfeldt Original Material ”S”® plus + ESD Polyethylene, Conductive Material ”S”® plus+ ESD has extremely low electrical resistance and is an optimum conductor. Full voltage dissipation for earthed components at maximum speed enables safe, spark-free work. This m.. |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | ISO 527 |
Murtfeldt Original Material ”S”® plus + LF Polyethylene, Low Friction This material has half the sliding friction coefficient of the Original Material ”S”®. This enables an increased machine running speed at the same time as less abrasion and thus a lower maintenan.. |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | STN EN ISO 527-2 |
Plastcom PLASTALEN® PQ 81 N 003 Polypropylene with improved impact strength PP copolymer regranulate for injection molding, impact modified. General use in all industry branches. Delivered in natural mode and in the full RAL color scale.Information Provided by Plastcom spol.. |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | STN EN ISO 527-2 |
Plastcom PLASTALEN® PQ 82 N 003/1M Polypropylene with improved impact strength PP copolymer regranulate for injection molding, impact modified. General use in all industry branches. Delivered in natural mode and in the full RAL color scale.Information Provided by Plastcom spol.. |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | ISO 37 |
PolyOne OnFlex™ U 5370A-S0015 Thermoplastic Elastomer (TPE) OnFlex™-U thermoplastic elastomer compounds are based on thermoplastic polyurethane elastomers (TPE-U). The OnFlex™-U 5300 series are based upon alloys of SEBS and TPU, combining the advantages of.. |
|||
Tensile Strength at Break | <= 25.0 MPa | <= 3630 psi | ISO/R527 |
Polykemi AB POLYfill PPC TS15020E Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | STN EN ISO 527-2 |
Plastcom PLASTALEN® PH 52 T 20 Polypropylene reinforced with mineral filler PP homopolymer for injection molding with the content of 20 % mineral filler, heat stabilized. Application in automotive industry. Delivered in black grade.Information Provided by Plastcom spol. s r.. |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | ISO 527-1/-2 |
DSM Arnitel® EM402-L Polyether Ester Elastomer (European Grade)
(discontinued **) Product description: Arnitel® combines the advantages of engineering thermoplastics, being easy to process with excellent mechanical properties, at the same time with the flexibility of rubbers.Arn.. |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D638 |
Lushan M-1 Adhesive Resin for Barrier Container and Tube Adhesive resin Lushan series for barrier container and tube is used for bonding a wide variety of materials, It’s most often used to adhering PE and EVOH, PP and EVOH, etc. Adhesive resins Lush.. |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | |
LATI Latistat 47/7-03 PP Copolymer Dissipative product based on Polypropylene copolymer (PPc). Unfilled. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Ter.. |
|||
Tensile Strength at Break | >= 25.0 MPa | >= 3630 psi | 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Hyflon® MFA® F1540 Perfluoropolymer Hyflon® MFA is a unique family of perfluoro polymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, high flexural endurance, inherent flame re.. |
|||
Tensile Strength at Break | 25.0 - 50.0 MPa @Thickness 2.00 mm |
3630 - 7250 psi @Thickness 0.0787 in |
50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 6020 Polyvinylidene Fluoride (PVDF) Solef® 6020 PVDF homopolymer has very high viscosity for membranes and lithium batteries. It is available exclusively as powder.Features: Homopolymer; Ultra High ViscosityUses: Batteries; Membran.. |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Stat-loy AX06484X ABS LNP* Stat-Loy* AX06484 is a compound based on ABS resin containing mineral filler. Characteristics of this grade is it is extrudeable and static dissipative.This data was supplied by SABIC-IP for t.. |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D638 |
SCG Chemicals EL-Proâ„¢ P401S Polypropylene Flat Yarn/Sheet Key Characteristics: Excellent mechanical propertiesRecommended Applications:Stretch tape for jumbo woven sheetMonofilament for rope and sheetInformation provided by SCG Chemicals |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D 638 |
Cossa Polimeri ESTAPROP 1040 V2 K Flame Retardant Polypropylene PP copolymerFlame retardant class V2, halogen free, good mechanical characteristicsInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D 638 |
Cossa Polimeri ESTAPROP H 1080 TG Polypropylene, 40% Mineral Filled PP homopolymer 40% mineral fillerExcellent stiffness, good dimensional stabilityInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | ISO 527-1/-2 |
Covestro Desmopan® DP 1970AW Polyurethane As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | ISO 527-1/-2 |
Covestro Desmopan® DP 3070AU Polyurethane injection molding gradefree from plasticizersApplicationInjection molded engineering partshard - soft systemsAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially .. |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | ISO 527-1/-2 |
Covestro Desmopan® DP 9370AU Polyurethane Extrusion- and injection molding gradewith special UV stabilizersvery good hydrolysis and microbial resistancegood low-temperature flexibilityfree from plasticizershigh moisture vapor transmission r.. |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | ISO 527-1/-2 |
Covestro Desmopan® KU 2-8671 Polyurethane As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | ISO 527-2/50 |
ExxonMobil Exxtral™ HMU 234 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin, black colored, with high stiffness, high heat stabilization, low emissions and low odor for automotive HVAC and under-the-hood applic.. |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | ISO 527 |
Eurotec® Tecolen® CP20 MF20 NL XC30 PPCP, 20% mineral filled, flame retardant - halogen (RoHS compliant), heat stabilized, natural Information provided by Eurotec® |
|||
Tensile Strength at Break | 25.0 MPa @Temperature 120 °C |
3630 psi @Temperature 248 °F |
ASTM Test |
BASF Ultramid® 8202C HS PA6 (Dry) Ultramid 8202C HS is a heat stabilized, low viscosity, PA6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also.. |
|||
Tensile Strength at Break | 25.0 MPa @Temperature 120 °C |
3630 psi @Temperature 248 °F |
ASTM Test |
BASF Ultramid® 8202C PA6 (Dry) Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique .. |
|||
Tensile Strength at Break | 25.0 MPa @Temperature 80.0 °C |
3630 psi @Temperature 176 °F |
ASTM Test |
BASF Ultramid® HPN 9362 40% Mineral Filled PA6 (Conditioned) Ultramid HPN 9362 is a 40% mineral reinforced, impact modified nylon 6 injection molding compound. It is one of the High Productivity Nylon series having improved surface appearance while reducing c.. |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | 300mm/min; DIN 53455/ISO 527 |
3M 7847 Laser Markable Label Material 3M™ Laser Markable Label Material 7847 and 7848 are specialty film label materials where a laser can ablate the top layer of a dual-layer facestock to create an image. The same laser can also kiss .. |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | STN EN ISO 527-2 |
Plastcom SLOVALEN PH 81 C 40 Polypropylene Homopolymer and Copolymer, 40% Micronized Talc FeaturesModified homopolymer and copolymer PP for injection moulding with the content of 40% micronized, chemically modified talc. Increased strength, rigidity and thermal application up to 130°C... |
|||
Tensile Strength at Break | <= 25.0 MPa | <= 3630 psi | ISO/R527 |
Polykemi AB POLYfill PPC T5020 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | ISO 527 |
Eastman 9921W PET Injection Molded
(discontinued **) Voridian PET 9921W is a copolymer PET. Typical applications include containers for automotive parts, household products, and pharmaceutical and food packaging. Voridian PET thermoplastic polyesters .. |
|||
Tensile Strength at Break | 25.0 MPa | 3630 psi | |
Plastcom SLOVALEN PH 91 C 20 PP, 20% mineral filling FeaturesModified homopolymer and copolymer PP for injection moulding with the contenct of 20% microground, chemically modified talc. Increased strength, rigidity and thermal application up to 100°C.. |