Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 20.0 MPa | 2900 psi | STN EN ISO 527-2 |
Plastcom PLASTALEN® PC 69 T 10 003 Polypropylene reinforced with mineral filler Modified PP copolymer for injection molding with the content of 10% mineral filler. Application in all automotive industry. Delivered in black.Information Provided by Plastcom spol. s r.o. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | STN EN ISO 527-2 |
Plastcom SLOVALEN PH 78 FRT 5 Polypropylene Homopolymer, Halogen Free and Phosphor Free Flame Retardant FeaturesModified homopolymer PP for injection moulding, contains the modifier of mechanical properties and non halogen and free phosphor flame retardant. Increased strength in comparison with unfil.. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | 2 in/min; ASTM D638 |
RheTech Products FT2600-00UV Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: Interior trimSplash shieldScuff padsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ISO 527 |
Polimeri Europa Eraclene® ML 70 U High Density Polyethylene - Injection Molding Eraclene ML 70 U is a gas phase high density polyethylene resin (HDPE) with antioxidants, suitable for injection molding application.This grade has a narrow molecular weight distribution. It combin.. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | 2 in/min; ASTM D638 |
Polimeros Mexicanos Rotolene® Industrial Black Linear Medium Density Polyethylene Hexene Copolymer Linear Medium Density Polyethylene grade which is fully UV8 stabilized. High quality Polyethylene compounded in black, formulated for rotational molding applications requiring excel.. |
|||
Tensile Strength at Break | >= 20.0 MPa | >= 2900 psi | ASTM D882 |
M. Holland Company MAGMA® LL1091-K LLDPE
(discontinued **) Features: Good Heat Seal, Good Processability, Good Tear Strength, Good ToughnessProcessing Method: ExtrusionInformation provided by M. Holland. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
3M Dyneon™ THV 220A Fluorothermoplastic
(discontinued **) THV 220A is a flexible, transparent fluoroplastic composed of tetrafluoroethylene, hexafluoropropylene, and vinylidene fluoride in the form of agglomerate. It is soluble in ketones, esters, or ether.. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
Ineos Styrenics 495F High-Impact Polystyrene Resin (Global) Description: High-impact, high-flow grade for a wide variety of applications, including appliance components, consumer electronics housings, magnetic and optical media, building and construction, pa.. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
Iran Petrochemical (PCC) HIPS 7240 High Impact Polystyrene HIPS7240 is a very high impact polystyrene used in the extrusion industry. The good melt strength of this grade makes it particularly suitable for deep-draw thermoforming. HIPS 7240 is available in .. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL WCA871 PPE-TPE (Asia Pacific) Halogen-free flame retardant Flexible Noryl extrusion grade intended for evaluation in applications such as insulation and cable jacket. Flame retardant performance and mechanical properties capable.. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | UL 1581 |
SABIC Innovative Plastics NORYL WCD801AU PPE-TPE (Asia Pacific) Flexible, UV stabilized, halogen free extrusion grade for applications such as wire insulation and cable jacket. Good color stability after UV weathering per ASTM D4459. Light color capable. Flame r.. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON CD000I PS (Asia Pacific) LNP* Stat-kon* CD000I is a compound based on Polystyrene resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D412 |
Sumitomo Chemical ESPOLEX® 3255 Thermoplastic Elastomer ESPOLEX® TPE Series is a group of thermoplastic elastomers produced by Sumitomo Chemical Company. Among its material advantages, ESPOLEX® TPE Series is distinguished by offering many low-densi.. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ISO 527-2 |
Total PSI 4440(EU) High Impact Polystyrene 4440 is a high impact polystyrene for the injection molding of parts demanding good dimensional stability at high temperatures, particularly front and back covers for television sets. In addition, .. |
|||
Tensile Strength at Break | 20.0 - 45.0 MPa | 2900 - 6530 psi | ASTM D638 |
Daikin POLYFLON M-111 PTFE Molding Powder, Fine Cut Fine cut powder.Processing Methods: Compression molding.Features: Produces moldings with extremely smooth and fine surface. Suited to making packing and gaskets since moldings have an especially go.. |
|||
Tensile Strength at Break | 20.0 - 45.0 MPa | 2900 - 6530 psi | ASTM D638 |
Daikin POLYFLON MG-1040F PTFE 20% Glass Fiber Filled Molding Powder, High Apparent Density, Free Flow 20% glass fiber filled. High apparent density and free-flowing properties. High wear resistance, low friction, good electrical properties.Applications: Mechanical and electrical service. Availabl.. |
|||
Tensile Strength at Break | 20.0 - 45.0 MPa | 2900 - 6530 psi | ASTM D638 |
Daikin POLYFLON MG-1050 PTFE 25% Glass Fiber Filled Molding Powder 25% glass fiber filled. High wear resistance, low friction, good electrical properties.Applications: Mechanical and electrical service. Available in all forms (e.g. bearings, gaskets, valve seats,.. |
|||
Tensile Strength at Break | >= 20.0 MPa | >= 2900 psi | ISO R 527 |
Fainplast Compounds FRT 91 Flexible PVC, Insulation Telephone cables |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ISO R 527-2 |
Arkema Group OREVAC® 18732 Grafted Maleic Anhydride Polypropylene OREVAC 18732 and 18732P are maleic anhydride grafted polypropylene used in the manufacturing of multiplayer structures. These products are available in pellets or in powder. OREVAC 18732 and 18732P .. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
Arkema Group OREVAC® 9318 EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre.. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
Azdel SuperLite® SL550600-100 PP Resin Matrix / 55% Glass Fiber (2 mm Molded Thickness) AZDEL SuperLite® SL550600-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ISO R 527 |
Addiplast Addilene J 520 M20 Polypropylene Copolymer Mineral reinforced, improved rigidityInformation provided by Addiplast. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ISO R 527 |
Addiplast Addilene PMD 50213 Polypropylene Copolymer Mineral reinforced, improved scratch resistanceInformation provided by Addiplast. |
|||
Tensile Strength at Break | 20.0 MPa @Temperature 80.0 °C |
2900 psi @Temperature 176 °F |
ISO Data |
BASF Ultramid® 8231G HS 14% Glass Filled PA6 (Conditioned) Ultramid 8231G HS is a heat stabilized, 14% glass fiber reinforced nylon 6 injection molding compound. It is also available in non-heat stabilized (Ultramid 8231) and/or pigmented versions. The gla.. |
|||
Tensile Strength at Break | 20.0 - 35.0 MPa | 2900 - 5080 psi | TM-019G |
AorTech Biomaterials Elast-Eon™ E2A Biomedical Polyurethane Pellets Elast-Eon™ 2A is a polyurethane with a 40% hard segment content and a mixed polyether/siloxane soft segment. It comes in pellet form. The pellets are colorless to yellowish and are soluble in DMAc... |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | cured; ISO 6922 |
3M Scotch-Weld™ EC2500 General Purpose Instant Adhesive 3M™ Scotch-Weld™ General Purpose Instant Adhesives are single component, high strength ethyl cyanoacrylate adhesive designed to bond to a variety of substances including most plastics, rubbers, me.. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | film; ASTM D638 |
3M Dyneon™ THV 221GZ Fluoroplastic Granules 3M™ Dyneon™ Fluoroplastic Granules THV 221GZ is a flexible, transparent fluoroplastic composed of tetrafluoroethylene, hexafluoropropylene, and vinylidene fluoride in the form of pellets. It provi.. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
Azdel SuperLite® SL551200-100 PP Resin Matrix / 55% Glass Fiber (4 mm Molded Thickness) AZDEL SuperLite® SL551200-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible R351AE Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
Arkema Group LOTRYL® 16 MA 003 Copolymer Ethylene - Methyl Acrylate LOTRYL® 16 MA 003 is a random copolymer of ethylene and methyl acrylate made by high-pressure radicalar polymerisation process. Due to the methyl acrylate content, LOTRYL® 16 MA 003 is a polymer o.. |