Polymer Property : Flexural Strength = 155 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 155 MPa
22500 psi
Quadrant EPP Duratron® PAI T4501 PAI + graphite + PTFE, compression moulded (ISO Data)
Compression moulded Duratron T4501 PAI is similar in composition to Duratron T4301 PAI, and is selected when larger shapes are required Very high maximum allowable service temperature in air (250°C..
Flexural Strength <= 155 MPa
<= 22500 psi
ISO 178
Polykemi AB SCANAMID 66 A43^E F14 Nylon 66, Glass Fiber Reinforced, Modified
Information provided by Polykemi AB
Flexural Strength 155 MPa
22500 psi
ASTM D790
Ravago Manufacturing Americas Enviramid™ N2315HL Post Consumer Recycle Nylon 6, 15% Glass Filled
Heat Stabilized, Lubricated, Black and made from EnViramid™ Post Consumer Recycled NylonInformation provided by Ravago.
Flexural Strength 155 MPa
22500 psi
ASTM D 790
RTP Company RTP 381 TFE 13 SI 2 Polycarbonate (PC), Carbon Fiber - PTFE Lubricated - Silicone Lubricated
Flexural Strength 155 MPa
22500 psi
ASTM D 790
RTP Company RTP 385 HEC Polycarbonate (PC); Nickel-Coated Carbon Fiber - EMI/RFI/ESD Protection
Flexural Strength 155 MPa

@Temperature 100 °C
22500 psi

@Temperature 212 °F
ISO 178
Solvay Specialty Polymers Amodel® A-1340 HS Polyphthalamide (PPA) Resin, 40% Mineral/Glass Reinforced, Dry as Molded &a
AMODEL® A-1340 HS is a 40% mineral/glass reinforced, heat stabilized polyphthalamide (PPA) which exhibits a high deflection temperature, high flexural modulus, high tensile strength and low warpage..
Flexural Strength 155 MPa

@Thickness 3.17 mm
22500 psi

@Thickness 0.125 in
ASTM D790
PTS Tristar® PC-30GFR 30% Glass Reinforced Polycarbonate
Information provided by Polymer Technology and Services, LLC (PTS).
Flexural Strength 155 MPa
22500 psi
ASTM D790
PolyOne Edgetek® PF-20CF/000 Polysulfone  (discontinued **)
The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for ..
Flexural Strength 155 MPa
22500 psi
Lehmann & Voss LUVOCOM® 1850-8023 PBT, with carbon fiber
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Electrically conductive, suitable for continuous discharging of statically generated electricit..
Flexural Strength 155 MPa
22500 psi
Lehmann & Voss LUVOCOM® 19-8373 Polyamide 46, with carbon fiber, lubricant modified
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Reduced moment of inertia compared with metal parts.Antistatic.Improved fri..
Flexural Strength 155 MPa
22500 psi
Lehmann & Voss LUVOCOM® 20-8368 Polyphthalamide, with carbon fiber and PTFE
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Low influence from moisture and temperature to measures and electrical prop..
Flexural Strength 155 MPa
22500 psi
ASTM D790
LG Chemical LUPOS HR-2407 Heat Resistant SAN, 40% Glass Fiber Reinforced
LUPOS resins are glass fiber reinforced styrene copolymers. LUPOS have improved strength, rigidity and dimensional stability. They offer excellent heat resistance, minimal mold shrinkage and have ..
Flexural Strength 155 MPa
22500 psi
1.3 mm/min; ASTM D790
Lavergne VYPET VNT 325 PET 25% Glass - Mineral Reinforced
Vypet 325 is a 25% glass/mineral reinforced PET injection molding compound designed for electrical and structural applications.Features: High temperature performance; Good balance resilience-stiffne..
Flexural Strength 155 MPa
22500 psi
CW; ASTM D790
Haysite H1000 Polyester Laminate
Haysite Grade 1000 laminate sheet is an outstanding material that is used in applications requiring exceptional weather and corrosion resistance. Grade H1000's unique polyester resin system provide..
Flexural Strength 155 MPa
22500 psi
Haysite HCR-125 Corrosion Resistant Vinyl Ester/Glass Sheet
A fiber glass reinforced thermoset sheet using DEREKANE® 470 vinylester in the resin matrix with flame retardant and ultraviolet inhibitors. Standard color is beige. Derakane® 470 is a registe..
Flexural Strength 155 MPa
22500 psi
ASTM D790
LG Chemical Lupox® GP-2151F General Purpose PBT, 15% Glass Fiber Reinforced, Flame Retardant
LUPOX semi-crystalline thermoplastic PBT resins exhibit properties including high strength, rigidity and good resistance to fatigue and creep at elevated temperatures. Furthermore, LUPOX resins sho..
Flexural Strength 155 MPa
22500 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP Stat-kon DCL33 PC (Europe-Africa-Middle East)
LNP* Stat-kon* DCL4033 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP ..
Flexural Strength 155 MPa
22500 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Valox® DR51 PBT (Europe-Africa-Middle East)
VALOX DR51 is a 15% glass fiber reinforced PBT injection moulding resin with excellent mechanical, thermal and electrical performance. Applications: spotlights, appliance housings, handles.
Flexural Strength 155 MPa
22500 psi
ASTM D 790
SABIC Innovative Plastics Valox® PDR4908 PBT (Asia Pacific)
This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Strength >= 155 MPa
>= 22500 psi
ISO 178
Polyram PlusTek RA303G3 Nylon 66 for Injection Molding, 15% Glass Fiber Reinforced, Heat Stabilized, Hydrolysis Resistant
15% Glass fiber reinforced, heat stabilized and hydrolysis resistant Nylon 66 for injection molding applications.Information provided by Polyram.
Flexural Strength 155 MPa
22500 psi
ASTM-D790
Polyram Polytron P40B03 Copolymer Polypropylene, Chemically Coupled 40% Long Glass Fiber
A CHEMICALLY COUPLED 40% LONG GLASS FIBERS REINFORCED BLACK POLYPROPYLENE, HEAT STABILIZED FOR INJECTION MOLDING APPLICATION.These products have significantly improved impact performance characteris..
Flexural Strength 155 MPa
22500 psi
ASTM D 790
RTP Company RTP 2200 AR 15 Polyetheretherketone (PEEK), Aramid Fiber
Preliminary Data Sheet
Flexural Strength 155 MPa
22500 psi
ASTM D790
Polyram PlusTek RA307G4 Nylon 6.6, 20% Glass Fiber
20% glass fiber reinforced heat stabilized polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Strength 155 MPa
22500 psi
ASTM D790
A. Schulman SCHULAMID® 66 GF13 13% Glass Fiber Reinforced Nylon 66
Information provided by A. Schulman.
Flexural Strength 155 MPa
22500 psi
ISO 178
Celanese CELANEX 3216 PBT, 15% Glass Reinforced
Celanex 3216 is a non-exuding (UL and CSA approved V-0 at 1/32 inch and 5V at 1/8 inch ),15% fiberglass reinforced polybutylene terephthalate which has an excellent balance of mechanical properties ..
Flexural Strength 155 MPa
22500 psi
ASTM D790
Adell BW-17 Nylon 6, 35% Glass Reinforced; Superior Finish
Data provided by Adell Plastics, Inc.
Flexural Strength 155 MPa
22500 psi
dry; ISO 178
DSM Novamid® 1013PL1 NAT PA6-MX
Injection Molding
Flexural Strength 155 MPa
22500 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Valox® VX4920 PBT (Europe-Africa-Middle East)
VALOX VX4920 is a 20% glass reinforced nucleated PBT/ASA blend with excellent mechanical properties, high dimensional stability and low density. Applications: connectors and automotive industry.
Flexural Strength 155 MPa
22500 psi
ISO 178
Celanese THERMX CG023 PCT, 20% Glass Reinforced
Thermx« CG023 is a 20% glass fiber reinforced polycyclohexylenedimethylene terephthalate for injection molding.Information provided by Celanese
Flexural Strength 155 MPa
22500 psi
ASTM D 790
RTP Company RTP 4605 HI FR Syndiotactic Polystyrene (SPS), Glass Fiber - Impact Modified - Flame Retardant