Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | >= 20.0 MPa | >= 2900 psi | ISO 527 |
Murtfeldt Original Material ”S”® plus + Bright ESD Polyethylene, Conductive Material ”S”® plus+ Bright ESD is a light plastic with high conductivity and a voltage-dissipating effect on earthed components. This material is ideal for use in applications where a high value.. |
|||
Tensile Strength, Yield | 20.0 - 25.0 MPa | 2900 - 3630 psi | ISO.527 DN.53455 |
Polimersan Plastics POLIPOLEN® (Polyethylene) HD-PE 500 PE 500: Polyethylenes with molecular weight higher than 500,000 gr/mol. POLIPOLEN® PE (POLYETHYLENE) is maintained from coke oven gas or from natural gas or from Ethene or Ethane which is produce.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | |
Radici Radilon® S USX200 (cond.) Nylon 6 Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | |
LyondellBasell Lupolen® UHM 201 MDPE, Ultra-High Molecular Weight For the production of very high abrasion and impact resistant parts with lower slip/stick friction, as well as higher stress crack and chemical resistance. Apart from anticorrosion products, this m.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | 150°C for 1,000 hrs; ASTM D1458 |
Fujipoly Industries Sarcon® 85GSR Thin-Film GSR Sarcon GSR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GSR is a composite of.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
Ineos Nova 5404 High Impact Polystyrene High impact, Good environmental stress crack resistance, USP Class VIApplications: Thermoformed containers and lids, Hot and cold beverage cups, Custom sheet, Single service packagingProperties were.. |
|||
Tensile Strength, Yield | 20.0 MPa @Temperature 23.0 °C |
2900 psi @Temperature 73.4 °F |
ASTM D638 |
Ineos 3560 Polypropylene Impact Copolymer This is a special high melt flow, nucleated, high impact copolymer polypropylene for injection molding applications. It offers excellent impact resistance and a high flexural modulus.ApplicationsAu.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
Ineos Styrenics Avantra® 594E High Impact Styrenic Polymer (NAFTA) Description: Avantra® 594E is a super high-impact polystyrene grade that delivers excellent processing efficiency along with toughness and high gloss in a wide variety of injection molding applic.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638-02 |
Ipiranga Petrochem PCD 0810 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO 527-1, -2 |
LyondellBasell Hostacomâ„¢ CB189FC/1 Thermoplastic Polyolefin Elastomer Description: Hostacomâ„¢ CB189FC/1 medium melt flow, 1,300 MPa flexural modulus, precolored, mineral-filled thermoplastic elastomeric olefin (TEO) resin has a very good balance of impact, stiffne.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP YP003 Polyester Elastomer (Europe-Africa-Middle East) LNP* LUBRICOMP* YP003 is a compound based on Polyester Elastomer containing PTFE, Silicone. Added features include; Internally Lubricated. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | 50mm/min; ISO 527 |
Styrolution Styrolux 3G55 SBC Styrolux 3G55 is a thermoplastic styrene-butadiene block copolymer which is suitable for film and sheet extrusion, and thermoforming. It offers and outstanding combination of crystal clarity and ex.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
SCG Chemicals EL-Leneâ„¢ M3804 Butene (C4) Rotational Molding Resin Natural base resin available in pellet / powder formKey Characteristics:High stiffnessGood processingFair impact resistanceTypical Applications: General-purpose products, such as small-to-medium wa.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | 50 mm/min; ISO 527 |
A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene DescriptionPolyfort® FPP 1876 is a 22% mineral filled copolymer UV Inhibited Polypropylene. It is high flow. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO 527 |
Polyram RamShine PS580 High Impact Polystyrene, Flame Retardant Flame retardant V-0, high impact polystyrene for injection molding applications.Information provided by Polyram. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | |
Trelleborg R399 Commercial Natural Rubber Polyisoprene All information provided by Trelleborg |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | 50 mm/min; ISO 527 |
A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene DescriptionPolyfort® FPP 1876 is a 22% mineral filled copolymer UV Inhibited Polypropylene. It is high flow. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
UBE 7115U Nylon 6/12 Copolymer Description: UBESTA Nylon 12 CopolymerInformation provided by UBE. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D 638 |
Cossa Polimeri ESTAPROP KUR 1010 TG05 Polypropylene, 5% Mineral Filled PP copolymer 5% mineral fillerElastomer modified, very high impact strength at low temperatureInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength, Yield | 20.0 MPa @Strain 100 % |
2900 psi @Strain 100 % |
ISO 527-1/-2 |
Covestro Desmopan® DP 3364D Polyurethane As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
Tensile Strength, Yield | 20.0 MPa @Strain 100 % |
2900 psi @Strain 100 % |
ISO 527-1/-2 |
Covestro Desmopan® DP 8715 Polyurethane + ABS injection molding grademodified with ABSgood low-temperature flexibilitygood wear resistanceApplicationSki boot shellsAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and of.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO 527-2 |
ExxonMobil Exxtral™ BMV 208 Performance Polyolefin Product Description: Polyolefin injection molding compound with very high flow, high stiffness, good low temperature impact resistance, and excellent processability for automotive exterior trim appl.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | (2.0 in/min); ASTM D638 |
ExxonMobil HDPE HD 8660.29 High Density Polyethylene Resin Product Description: HD 8660 series are high density hexane copolymers designed to offer superior toughness and stiffness. They are ideally suited for applications that require the optimum balance o.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | (2.0 in/min); ASTM D638 |
ExxonMobil HDPE HD P8660.29 High Density Polyethylene Resin Product Description: HD 8660 series are high density hexane copolymers designed to offer superior toughness and stiffness. They are ideally suited for applications that require the optimum balance o.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO 527 |
Azoty Tarnow™ TARFLEN ST PTFE Free-Flowing suspension powder for ram extrusion of rods, pipes and other profiles.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
Tensile Strength, Yield | 20.0 MPa @Temperature 120 °C |
2900 psi @Temperature 248 °F |
ISO Data |
BASF Ultramid® 8202 PA6 (Conditioned) Ultramid 8202 is a low viscosity, general purpose polyamide 6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is also available in heat stabilized (Ult.. |
|||
Tensile Strength, Yield | 20.0 MPa @Temperature 120 °C |
2900 psi @Temperature 248 °F |
ISO Data |
BASF Ultramid® 8253 PA6 (Dry) Ultramid 8253 is an unfilled, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications. It is also available in heat stabilized (Ultramid 8253 HS) and/o.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0436T40L Talc Reinforced |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D-638 |
Axiall 19940-03 Wire & Cable Flexible PVC THHN-THWN circuit sizes. Best suited for 1/64 wall, 18 AWG and smaller. UL recognized for THHN, THW, THWN, TW. Oil resistant II and VW-1 rated.Information provided by Georgia GulfGeorgia Gulf bec.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
Tipco Tipcolene® IA 933 IN - 20% Talc/Mineral Reinforced Polypropylene Copolymer, High Flow, Stiffness & Impact Strength 20% Mineral Reinforced, High Stiffness, High Impact PP CopolymerApplications: Automotive InteriorsProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India... |