- Polymer Property : Tensile Strength at Break = 25.0 MPa
Polymer Property : Tensile Strength at Break = 25.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ISO 527 |
| Murtfeldt Original Material ”S”® plus + ESD Polyethylene, Conductive Material ”S”® plus+ ESD has extremely low electrical resistance and is an optimum conductor. Full voltage dissipation for earthed components at maximum speed enables safe, spark-free work. This m.. |
|||
| Tensile Strength at Break | <= 25.0 MPa | <= 3630 psi | ISO/R527 |
| Polykemi AB POLYfill PPC T25020 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | STN EN ISO 527-2 |
| Plastcom PLASTALEN® PH 52 T 20 Polypropylene reinforced with mineral filler PP homopolymer for injection molding with the content of 20 % mineral filler, heat stabilized. Application in automotive industry. Delivered in black grade.Information Provided by Plastcom spol. s r.. |
|||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D412 |
| Polimeri Europa Europrene® SOL TH 2315 Styrene - Ethylene / Butylene Block Copolymer Europrene® SOL TH 2315 is a linear block copolymer obtained by selective hydrogenation of styrene-butadiene-styrene block copolymers. The polymer is based on styrene and ethylene/butylene, where b.. |
|||
| Tensile Strength at Break | <= 25.0 MPa | <= 3630 psi | ISO/R527 |
| Polykemi AB POLYfill PPC T25020 UV Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ISO 527-2 |
| Total Lacqrene® 1235 High Impact Polystyrene
(discontinued **) LACQRENE® 1235 is a high gloss, high impact polystyrene used in injection molding and co-extrusion. This grade produces articles with a surface gloss level equivalent to that of certain grades of .. |
|||
| Tensile Strength at Break | >= 25.0 MPa | >= 3630 psi | DIN 53504 |
| Huntsman AVALON® 75 ABX Thermoplastic Polyurethane Introduction: AVALON 70 ABX is a high performance polyester based thermoplastic polyurethane for injection molding. AVALON 70 ABX is part of the AVALON Perform Range and offers a specially designed,.. |
|||
| Tensile Strength at Break | >= 25.0 MPa | >= 3630 psi | DIN 53504 |
| Huntsman AVALON® 80 ABX Thermoplastic Polyurethane Introduction: AVALON 80 ABX is a high performance polyester based thermoplastic polyurethane for injection molding. AVALON 80 ABX is part of the AVALON Perform Range and offers a specially designed,.. |
|||
| Tensile Strength at Break | 25.0 - 27.0 MPa | 3630 - 3920 psi | ASTM D683 |
| Loxim 830 02T V0 Polypropylene Compound, 30% Talc Filled, Flame Retardant Information provided by Loxim Industries |
|||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | |
| LATI Laticonther 52/11 GR/70 PP Homopolymer High thermal conductivity product based on Polypropylene homopolymer (PPh). Graphite.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lat.. |
|||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | |
| LATI Latistat 47/7-03 PP Copolymer Dissipative product based on Polypropylene copolymer (PPc). Unfilled. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Ter.. |
|||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ISO 527-1, -2 |
| LyondellBasell Hostacomâ„¢ SP98F/94 Thermoplastic Polyolefin Elastomer Description: Hostacomâ„¢ SP98F/94 Black medium melt flow, 2,300 MPa flexural modulus, mineral-filled thermoplastic elastomeric olefin (TEO) resin has a very good combination of stiffness, impact .. |
|||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics ULTEM SILTEM-STM1500 PEI (Europe-Africa-Middle East) SILTEM STM1500 is a flexible siloxane-polyetherimide copolymer for cable and wire coatings. RoHS compliant. |
|||
| Tensile Strength at Break | >= 25.0 MPa | >= 3630 psi | 50 mm/min; ASTM D638 |
| Solvay Specialty Polymers Hyflon® MFA® F1540 Perfluoropolymer Hyflon® MFA is a unique family of perfluoro polymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, high flexural endurance, inherent flame re.. |
|||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP STAT-LOY AX06484 ABS LNP* STAT-LOY* AX06484 is a compound based on ABS resin containing Talc. Added feature of this grade is: Antistatic, Extrudeable. |
|||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics LNP Stat-loy AX06484X ABS LNP* Stat-Loy* AX06484 is a compound based on ABS resin containing mineral filler. Characteristics of this grade is it is extrudeable and static dissipative.This data was supplied by SABIC-IP for t.. |
|||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Thermocomp M10009A PP (Europe-Africa-Middle East) LNP* STARFLAM* M10009A is a compound based on Polypropylene resin, containing Flame Retardant. Added features include : Flame Retardant.This data was supplied by SABIC-IP for the Europe-Africa-Middl.. |
|||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D412 |
| Sumitomo Chemical ESPOLEX® 817 Thermoplastic Elastomer ESPOLEX® TPE Series is a group of thermoplastic elastomers produced by Sumitomo Chemical Company. Among its material advantages, ESPOLEX® TPE Series is distinguished by offering many low-densi.. |
|||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | Type IV specimen, compression molded, crosshead speed 2 in/min; ASTM D638 |
| DuPont Nucrel® 925 Ethylene-Methacrylic Acid Copolymer Resin Nucrel® 925 is a tough, lightweight, easily processed ethylene copolymer resin. This resin is inherently flexible without the need for plasticizers. The resin can be pigmented, UV-stabilized for .. |
|||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | 500mm/min; ASTM D638 Type IV Specimen |
| Westlake MC2001 High Density Polyethylene Coating Westlake MC2001 is a high density polyethylene designed for extrusion coating and lamination applications. MC2001 provides improved barrier properties, temperature resistance, stress crack resistanc.. |
|||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D638 |
| Total PS CPDS 818 Easy Flow, Non-Deca Polystyrene Total Petrochemicals Polystyrene 818 is a high heat resistant, high impact Polystyrene for injection molding and extrusion/thermoforming. It is recommended for the manufacturing of articles which r.. |
|||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D638 |
| Eastman Eastar MN200 Copolyester Eastar Copolyester MN200 is an amorphous copolyester with excellent flow characteristics as well as radiation resistance and chemical resistance.Applications/UsesMedical |
|||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D 638 |
| Cossa Polimeri ESTAPROP 1040 V2 K Flame Retardant Polypropylene PP copolymerFlame retardant class V2, halogen free, good mechanical characteristicsInformation provided by Cossa Polimeri S.r.l. |
|||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D 638 |
| Cossa Polimeri ESTAPROP K 1280 T8 Polypropylene, 40% Mineral Filled PP copolymer 40% mineral fillerExcellent physical and mechanical characteristics, good surface appearanceInformation provided by Cossa Polimeri S.r.l. |
|||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D638 |
| Aclo Accutech Polypropylene Homopolymer HP0334M10CL Mica Reinforced Coupled |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 120 °C |
3630 psi @Temperature 248 °F |
ASTM Test |
| BASF Ultramid® 8272G HS BK-102 12% Glass Filled PA6 (Conditioned) Ultramid 8272G HS BK-102 is a 12% glass fiber reinforced, black pigmented, thermally modified, nylon 6 blow molding compound offering an excellent balance of engineering properties combined with the.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 80.0 °C |
3630 psi @Temperature 176 °F |
ASTM Test |
| BASF Ultramid® HPN 9362 40% Mineral Filled PA6 (Conditioned) Ultramid HPN 9362 is a 40% mineral reinforced, impact modified nylon 6 injection molding compound. It is one of the High Productivity Nylon series having improved surface appearance while reducing c.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 80.0 °C |
3630 psi @Temperature 176 °F |
ISO Data |
| BASF Ultramid® HPN 9362 40% Mineral Filled PA6 (Conditioned) Ultramid HPN 9362 is a 40% mineral reinforced, impact modified nylon 6 injection molding compound. It is one of the High Productivity Nylon series having improved surface appearance while reducing c.. |
|||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D638 |
| 3M Dyneon™ FEP 6307Z Fluorinated Ethylene Propylene Fluorothermoplastic Granules Dyneon FEP 6307Z is offered for extrusion, injection molding and transfer molding for the wire and cable and chemical process industries. Their distinguishing features include: Excellent electrical .. |
|||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | 50 mm/min; ISO 527 |
| Fainplast Compounds Propylplus 703 Polypropylene Cable Compound Polypropylene, halogen-free cable compound with superior thermo-mechanical properties, outstanding heat resistance, and high electrical propertiesSolid Polypropylene (flexible)Information provided b.. |
|||