Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 35.0 MPa | 5080 psi | STN EN ISO 178 |
Plastcom PLASTALEN® PH 52 T 20 003/1M Polypropylene reinforced with 20% mineral filler PP homopolymer for injection molding with the content of 20 % mineral filler, heat stabilized. Application in automotive industry. Delivered in black grade.Information Provided by Plastcom spol. s r.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | |
Plastcom SLOVALEN PC 13 T 30 PP, 30% mineral filling FeaturesModified copolymer PP for injection moulding or extrusion parts with the content of 30 % mineral filler. Increased rigidity, strength and impact strenght.Delivered in natural mode and in the.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | |
Plastcom SLOVALEN PC 16 FRD 1 PP, flame retardant Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.0.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | STN EN ISO 178 |
Plastcom SLOVALEN PC 78 FRD 3 Polypropylene Copolymer, Halogen Flame Retardant FeaturesDetermined for environment where contact with water is possible because the electric properties do not change by conditioning. Application - terminals, coil forms, guides in washing machine.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | 2 mm/min; ISO 178 |
Polimeri Europa Edistir ICE R 830D Polystyrene Environmental stress cracking resistant (ESCR) HIPS. ICE PD R 830D combines high impact strength with an improved chemical resistance to oils, fats and chemical agents, such as detergents for both i.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ASTM D790 |
SABIC PS 325 High Impact Polystyrene for Injection Molding Product Description: High Impact Polystyrene PS 325 is manufactured by continuous mass polymerization of styrene monomer. An elastomer is incorporated during polymerization to achieve impact resis.. |
|||
Flexural Strength | <= 35.0 MPa | <= 5080 psi | ISO 178 |
Polykemi AB POLYfill PPC K5025 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ISO 178 |
Nilit FRIANYL A63 CU90 Nylon 6.6 for injection molding, 90% copper filled Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | <= 35.0 MPa | <= 5080 psi | ISO 178 |
Polykemi AB SCANFILL Injection CPC35051 PP/PE, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 35.0 - 60.0 MPa | 5080 - 8700 psi | Transverse |
Quadrant Plastic Composites MultiQ® Concrete Thermoplastic Panel Composite MultiQ is a product line of thermoplastic composites in panel form whose specific properties make them particularly suitable as an environmental alternative to plywood in outdoor applications. Howev.. |
|||
Flexural Strength | >= 35.0 MPa | >= 5080 psi | |
MarkeTech Repton 902 Cordierite Mg-Al-Si Oxide REPTON setter tiles, kiln furniture, and special fixtures are lightweight, ridge, and high strength ceramics that resist distortion and spalling, even when thermal cycled many times. They are availa.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ISO 178 |
Solvay TECHNYL® C 230 PA6, Conditioned Description: Unreinforced polyamide PA6, with improved impact resistance, for injection molding.Available in: EuropeProduct Applications: This grade has improved impact strength and higher flexibili.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-KON MX10301C PP LNP* STAT-KON* MX10301C is a compound based on Polypropylene containing Proprietary Filler(s). Added features of this grade include: Electrically Conductive, Clean Compounding System. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp MX01767C PP LNP* Stat-Kon* MX01767C is a compound based on Polypropylene containing Proprietary Fillers. Charactiers of this grade are Statically Conductive, Clean Compound System.This data was supplied by SAB.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | 2 mm/min; ISO 178 |
Sax Polymers SAXALEN PPH319FX21 Polypropylene Homopolymer SAXALEN PPH319FX21 is a unfilled Polypropylene - Homopolymer intended for injection molding. It has flame retardant properties and suitable to produce thin-walled parts.Information provided by SAX P.. |
|||
Flexural Strength | 35.0 MPa @Temperature 23.0 °C |
5080 psi @Temperature 73.4 °F |
2mm/min; 80x10x4mm; ISO 178 |
SYNTHOS Krasten® 662E High Impact Polystyrene High impact grade with properties suitable for thermoforming. Processed mainly by extrusion and thermoforming. Production of demanding visual appearance plates, technical parts, sheets and molded pa.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ASTM D790 |
Polyram RamOfin PPC501 Polypropylene, Flame Retardant Flame retardant polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | 2 mm/min; ISO 178 |
Chi Mei Polyrex® PH-88 Polystyrene - High Impact High impact |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ASTM D790 |
Aclo Accutech Polypropylene Homopolymer HP0336C10L Calcium Reinforced |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ASTM D790 |
Aclo Accutech Polypropylene Homopolymer HP0336C30L Calcium Reinforced |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ASTM D790 |
Aclo Accutech Polypropylene Homopolymer HP0339C10L Calcium Reinforced |
|||
Flexural Strength | 35.0 MPa | 5080 psi | cond.; ISO 178 |
Azoty Tarnow™ Tarnamid® T-27 MCS V0 Polyamide 6 - Flame Retarded, Unreinforced Flame retarded (class V0), bromine and red phosphorus free, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has th.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ASTM Test |
BASF Ultramid® 8202 HS BK-102 PA6 (Conditioned) Ultramid 8202 HS BK-102 is an unfilled, heat stabilized, pigmented black, low viscosity, general purpose injection molding PA6 exhibiting excellent fluidity for filling thin sections. It possesses .. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ASTM Test |
BASF Ultramid® 8202 HS PA6 (Conditioned) Ultramid 8202 HS is a heat stabilized, low viscosity, general purpose nylon 6 injection molding homopolymer. It possesses the combination of strength and toughness and has excellent chemical and ab.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | ASTM Test |
BASF Ultramid® 8202 PA6 (Conditioned) Ultramid 8202 is a low viscosity, general purpose polyamide 6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is also available in heat stabilized (Ult.. |
|||
Flexural Strength | 35.0 MPa @Temperature 93.0 °C |
5080 psi @Temperature 199 °F |
ASTM Test |
BASF Ultramid® 8260 40% Mineral Filled PA6 (Dry) Ultramid 8260 is a 40% mineral reinforced PA6 injection molding compound. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability including low.. |
|||
Flexural Strength | 35.0 MPa @Temperature 65.0 °C |
5080 psi @Temperature 149 °F |
ASTM Test |
BASF Ultramid® HPN 9362 40% Mineral Filled PA6 (Conditioned) Ultramid HPN 9362 is a 40% mineral reinforced, impact modified nylon 6 injection molding compound. It is one of the High Productivity Nylon series having improved surface appearance while reducing c.. |
|||
Flexural Strength | 35.0 MPa | 5080 psi | cond.; ISO 178 |
Azoty Tarnow™ Tarnamid® T-27 MCS 850 Polyamide 6 - Flame Retarded, Unreinforced Glow wire resistance 850°C, bromine and red phosphorus free, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has .. |
|||
Flexural Strength | <= 35.0 MPa | <= 5080 psi | ISO 178 |
Polykemi AB POLYfill PPC T1020 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |