BASF Ultramid® 8272G HS BK-102 12% Glass Filled PA6 (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled
Manufacturer	BASF
Trade Name	Ultramid®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® 8272G HS BK-102 12% Glass Filled PA6 (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid 8272G HS BK-102 is a 12% glass fiber reinforced, black pigmented, thermally modified, nylon 6 blow molding compound offering an excellent balance of engineering properties combined with the melt strength ideally suited for blow molding and other applications requiring ultra high melt viscosity. It exhibits improved strength, stiffness and creep resistance compare to standard blow molding grades. Outstanding permeability and chemical resistance to oils, hydrocarbons and most solvents are other advantages along with excellent stiffness ad the ability to fabricate complex shapes for cost effective metal replacements.

Physical Properties	Metric	English	Comments
Density	1.22 g/cc	0.0441 lb/in³	dry; ISO 1183
Water Absorption	1.4 %	1.4 %	24 hour; ISO Test
	8.3 %	8.3 %	beginning dry; ISO 62
Moisture Absorption at Equilibrium	2.3 %	2.3 %	beginning dry (23°C/50% R.H.); ISO 62
Linear Mold Shrinkage	0.0030 cm/cm	0.0030 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	60.0 MPa	8700 psi	0.2 in/min; ASTM Test
	25.0 MPa @Temperature 120 °C	3630 psi @Temperature 248 °F	ISO Data
	25.0 MPa @Temperature 120 °C	3630 psi @Temperature 248 °F	ASTM Test
	40.0 MPa @Temperature 80.0 °C	5800 psi @Temperature 176 °F	ASTM Test
	40.0 MPa @Temperature 80.0 °C	5800 psi @Temperature 176 °F	ISO Data
	110 MPa @Temperature -40.0 °C	16000 psi @Temperature -40.0 °F	ASTM Test
	110 MPa @Temperature -40.0 °C	16000 psi @Temperature -40.0 °F	ISO Data
Tensile Strength, Ultimate	60.0 MPa	8700 psi	5mm/min; ISO 527
Tensile Strength, Yield	65.0 MPa	9430 psi	50mm/min; ISO 527
	65.0 MPa	9430 psi	2 in/min; ASTM Test
Elongation at Break	20 %	20 %	50mm/min, Nominal strain; ISO 527
	30 %	30 %	2 in/min; ASTM Test
	2.0 % @Temperature -40.0 °C	2.0 % @Temperature -40.0 °F	ASTM Test
	2.0 % @Temperature -40.0 °C	2.0 % @Temperature -40.0 °F	ISO Data
	20 % @Temperature 120 °C	20 % @Temperature 248 °F	ISO Data
	20 % @Temperature 120 °C	20 % @Temperature 248 °F	ASTM Test
	30 % @Temperature 80.0 °C	30 % @Temperature 176 °F	ASTM Test
	30 % @Temperature 80.0 °C	30 % @Temperature 176 °F	ISO Data
Elongation at Yield	15 %	15 %	50mm/min; ISO 527
	15 %	15 %	2 in/min; ASTM Test
Tensile Modulus	3.10 GPa	450 ksi	1mm/min; ISO 527
	1.50 GPa @Temperature 120 °C	218 ksi @Temperature 248 °F	ISO Data
	1.90 GPa @Temperature 80.0 °C	276 ksi @Temperature 176 °F	ISO Data
	6.40 GPa @Temperature -40.0 °C	928 ksi @Temperature -40.0 °F	ISO Data
Flexural Strength	80.0 MPa	11600 psi	ASTM Test
	265 MPa @Temperature -40.0 °C	38400 psi @Temperature -40.0 °F	ASTM Test
Flexural Modulus	1.97 GPa	286 ksi	ASTM Test
Izod Impact, Notched	0.400 J/cm @Temperature -40.0 °C	0.749 ft-lb/in @Temperature -40.0 °F	ASTM Test
	1.55 J/cm @Thickness 3.17 mm	2.90 ft-lb/in @Thickness 0.125 in	ASTM Test

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093

Processing Properties	Metric	English	Comments
Melt Temperature	275 °C	527 °F	Injection molding
Mold Temperature	95.0 °C	203 °F	Injection molding

Descriptive Properties	Value	Comments
Color	BK-102
Commercial Status	Active America
Form	Pellets
Impact Modified	No
Primary Processing Technique	Blow Molding
Processing	Blow molding
	Injection Molding
Special characteristic	Heat stabilized or stable to heat