Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 6.40 GPa | 928 ksi | ISO 527 |
Nilit FRIANYL A63 HH-FK 1020 Nylon 6.6 for injection molding, 10% glass fiber and 20% glass ball reinforced Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | |
Radici Radilon® S RV300 (cond.) Nylon 6 Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group. |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | 1 mm/min |
Polimeri Europa KOBLEND PCA PD 935 G4 PC+ABS, 20% Glass Fiber
(discontinued **) Symbol according to ISO 1043/1/2: PC+ABS (GF) Injection moulding grade, reinforced with 20% glass fibres, high stiffness, very good dimensional stability. Main application fields: structural non a.. |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | ASTM D638 |
NOVA Chemicals Dylark® 480P20 High Performance Glass Filled Styrenic Very high modulus, High heat resistance, Excellent flow characteristics, Excellent adhesion to urethaneApplications: Instrument panel substrates, consoles, Cluster housing, interior trimInjection Sp.. |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | ISO 527-1/-2 |
Lanxess Durethan® BG 30 X 000000 Nylon 6, 30% Glass Fiber PA 6, injection molding grade, 30% glass fibers/glass spheres, good surface, low warpage |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | ISO 527-1,-2 |
Lanxess Durethan® BG 30 X H3.0 000000 Nylon 6, 30% Glass Fibers/Glass Spheres PA 6, 30% glass fibers/glass spheres, injection molding, heat-ageing stabilized, low tendency to warp |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min |
Lanxess Durethan® BG 30 X W1 000000 Nylon 6, Glass Fiber Reinforced PA 6, 30% glass fibers/glass spheres, injection molding, low tendency to warp, weather stabilizedInformation provided by LANXESS. |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | |
LATI Latilub 66-20T G/20-V1 PA66, 20% Glass Fiber Reinforced, PTFE Filled, Flame Retardant Self-lubricating product based on Polyamide 66 (PA66). PTFE. Glass fibers. UL94 V-1 classified, with brominated flame retardants, PBB/PBDE free.Availability: Africa & Middle East; Asia Pacific; Euro.. |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL SE1GFN2 PPE+PS (Asia Pacific) PPE+PS blend. 20% Glass reinforced. Non-brominated, non-chlorinated FR system. UL94 V1 listing. Dielectric strength. Dimensional stability. Suitable for E/E applications. |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | ISO 527 Type 1A |
Solvay TECHNYL® C 52G4 MZ25 PA6, 25% mineral filler, DRY Description: TECHNYL® C 52G4 MZ25 is a 25% mineral reinforced melamine cyanurate flame retarded polyamide 6.This product is heat stabilized and is suitable for injection molding. This product is .. |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Lubricomp ZFL34XXC PPE+PS (Europe-Africa-Middle East) LNP* LUBRICOMP* ZFL34XXC is a compound based on PPE+PS Blend resin containing Glass Fiber, PTFE. Added features incluce: Internally Lubricated.This data was supplied by SABIC-IP for the Europe-Afri.. |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON WSF42 PBT (Europe-Africa-Middle East) LNP*STAT-KON* WSF42 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, Stainless Steel Fiber. Added features include: Electrically Conductive. |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP RF003AXH PA 66 LNP* THERMOCOMP* RF003AXH is a compound based on Nylon 66 containing 15% Glass Fiber. Added feature of this material includes: Healthcare. |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Ultem ATX102R PEI+PCE 20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Ultem ATX102R PEI+PCE (Asia Pacific) 20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Noryl GFN1420V PPE+PS (Asia Pacific) Noryl* GFN1420V resin is a high flow blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 20 % glass reinforcement. The resin is suitable for injection molding and is designe.. |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL GFN1520V PPE+HIPS NORYL GFN1520V is a 20% glass fibre reinforced material with improved hydrolytic stability. This grade has been certified for potable water applications up to 85C in Europe and North America, color .. |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL GFN1520V PPE+HIPS (Europe-Africa-Middle East) NORYL GFN1520V is a 20% glass fibre reinforced material with improved hydrolytic stability. Noryl GFN1520V cust spec 1977 has been certified for potable water applications up to 85C in Europe and No.. |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | ISO 527-1/-2 |
Unitika A3130 PA6, 35% Mineral Reinforced, Dry Information provided by Unitika Ltd. |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | ISO 527 |
Azoty Tarnow™ TARNOFORM 300 GF3 POM 15% glass fiber reinforced injection molding grade, suitable for applications where increased strength and stiffness is required.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A... |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | 1mm/min; ISO 527 |
BASF Ultramid® 8260 HS BK-102 40% Mineral Filled PA6 (Dry) Ultramid 8260 HS BK-102 is a heat stabilized, pigmented black, 40% mineral reinforced PA6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined wi.. |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | 1mm/min; ISO 527 |
BASF Ultramid® 8260 HS PA6 (Dry) |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | 1[mm/min]; ISO 527-1/2 |
Akro-Plastic Akromid® A3 GF 15 (2418) PA 6.6 Dry, 15% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat.. |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HFD4412 PC Lexan* HFD4412 is a 20% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release. |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HFD4412 PC (Europe-Africa-Middle East) Lexan* HFD4412 is a 20% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release. |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DFL44 PC (Europe-Africa-Middle East) LNP* Lubricomp* DFL44 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. |
|||
Tensile Modulus | 6.40 GPa | 928 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HFD4412 PC (Asia Pacific) Lexan* HFD4412 is a 20% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release. |