Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 265 MPa | 38400 psi | |
Plastcom SLOVAMID 66 GF 33 PA66, 33% glass fibre FeaturesChemically reinforced with 33% glass fibre, suitable for mouldings with high strength and toughness also at minus temperatures. Used in the automotive, engineering and electrical industry. A.. |
|||
Flexural Strength | 265 MPa | 38400 psi | ASTM D790 |
Niche Polymer PA66GF33BK Nylon 66, 33% Glass Fiber Filled Information provided by Niche Polymer |
|||
Flexural Strength | 265 MPa | 38400 psi | ASTM D790 |
Niche Polymer PA66GF33N Nylon 66, 33% Glass Fiber Filled Information provided by Niche Polymer |
|||
Flexural Strength | 265 MPa | 38400 psi | |
Lehmann & Voss LUVOCOM® 1-7004 Polyamide 66, with glass fiber and carbon fiber, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Electrically conductive, suitable for continuous discharging of statically .. |
|||
Flexural Strength | 265 MPa | 38400 psi | |
Lehmann & Voss LUVOCOM® 1105-8402 PEEK, with glass fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Chemical and hydrolysis resistance parts, non flammable.High dimension.. |
|||
Flexural Strength | 265 MPa | 38400 psi | 5 mm/min; ISO 178 |
Gromax BFG30-AS00N1 Nylon 6 30% Glass Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
Flexural Strength | 265 MPa | 38400 psi | 5 mm/min; ISO 178 |
Gromax BFG30-BN00N1 Nylon 6 30% Glass Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
Flexural Strength | 265 MPa | 38400 psi | ISO 178 |
SABIC Innovative Plastics LNP Stat-kon EE006EM PEI LNP* Stat-kon* EE006EM is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding.This data was supplied by .. |
|||
Flexural Strength | 265 MPa | 38400 psi | GB/T 9341-2008 |
Sichuan Deyang Haton® hGR40DL Polyphenylene Sulfide, Glass Fiber Reinforced Injection molding, low chlorineInformation provided by Sichuan Deyang Chemical Co., LTD |
|||
Flexural Strength | 265 MPa | 38400 psi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® XP-2140C PPS Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 265 MPa | 38400 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP RF00AH PA 66 LNP* THERMOCOMP* RF00AH is a compound based on Nylon 66 resin containing 50% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
Flexural Strength | 265 MPa | 38400 psi | ISO 178 |
Unitika A1022GFL60 PA6, 60% Glass Fiber Reinforced, Conditioned Information provided by Unitika Ltd. |
|||
Flexural Strength | 265 MPa | 38400 psi | 2 mm/min; ISO 178 |
Eurostar Staramide AG6 PA66, 30% Glass Filled, Injection Molded AG6 is a 30% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier. |
|||
Flexural Strength | 265 MPa | 38400 psi | ASTM D790 |
Adell AR-37 Nylon 66, 35% Glass Reinforced Data provided by Adell Plastics, Inc. |
|||
Flexural Strength | 265 MPa @Temperature -40.0 °C |
38400 psi @Temperature -40.0 °F |
ASTM Test |
BASF Ultramid® 8272G HS BK-102 12% Glass Filled PA6 (Conditioned) Ultramid 8272G HS BK-102 is a 12% glass fiber reinforced, black pigmented, thermally modified, nylon 6 blow molding compound offering an excellent balance of engineering properties combined with the.. |
|||
Flexural Strength | 265 MPa @Temperature 23.0 °C |
38400 psi @Temperature 73.4 °F |
|
Ceradyne Ceralloy® 225 Titanium Diboride Features:electrical conductancewear resistancehardnessApplications:wear componentsballistic armorsputtering targetsInformation provided by Ceradyne Company |
|||
Flexural Strength | 265 MPa | 38400 psi | dry; ISO 178 |
DSM Novamid® 3021GH30 BK629 PA66-GF30 30% Glass Reinforced, Heat Stabilized |
|||
Flexural Strength | 265 MPa | 38400 psi | ISO 178 |
SABIC Innovative Plastics LNP Verton UV007S PPA LNP VERTON* UV007S is a compound based on Polyphthalamide resin containing Long Glass, Long Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP .. |