Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 80.0 MPa | 11600 psi | STN EN ISO 178 |
Plastcom PLASTAMID® 66 BT B 27 A PA66 PA66 for compounding, modified for general use, with excellent manufacturing properties. Use: automotive, engineering, electrical and consumer-goods industry - electrical tools, fasteners, clamps, h.. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | STN EN ISO 178 |
Plastcom PLASTAMID® 66 BT N 32 C PA66 PA66 basic type for injection molding, compounding, extrusion. Use: automotive, engineering, electrical and consumer-goods industry - electrical tools, fasteners, clamps, hobby tools, toys. Delivere.. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
Polimeri Europa Edistir N 1782 Polystyrene General purpose polystyrene with good flow and high heat resistance. Suggested for direct gassing extrusion of heavy gage insulating boards (XPS) and in blend with high concentration of clear SBS f.. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
Nilit FRIANYL B63 TF20 Nylon 6 for injection molding, 20% PTFE lubricated Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | 80.0 - 100 MPa | 11600 - 14500 psi | Compression; ISO 178 |
Raschig Group MELOPLAS® 3025 MF Cellulose-reinforced and inorganically filled MF molding compound in white and colored shades. High surface hardness, good UV and heat stability, very good resistance to chemicals - also to foodstu.. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | |
Lehmann & Voss LUVOCOM® 50-0957 Polycarbonate, with PTFE, easy flowing Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Improved friction and wear behaviour. Emergency running proper.. |
|||
Flexural Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | ASTM D790 |
Gromax PBT 1100-211L Product Description: PBT unreinforced middle viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Exce.. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
Mitsubishi Xantar® MX 1000 Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
Mitsubishi Xantar® MX 1021 FD Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
SABIC Innovative Plastics LNP Lubricomp JL003 PES LNP* Lubricomp* JL003 is a compound based on Polyethersulfone resin containing PTFE.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
Solvay TECHNYL® B 230 PA66/6, DRY Description: Unreinforced and modified copolyamide 66/6, with high flexibility and improved impact resistance, for injection molding.Available in: Asia Pacific and EuropeProduct Applications: TECHN.. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
Solvay TECHNYL® A 217 PA66, Conditioned Description: TECHNYL ® A 217 is an unreinforced polyamide 66, heat stabilized, standard viscosity, for injection molding. It is available in black color.Benefits: This product offers all the prim.. |
|||
Flexural Strength | 80.0 MPa @Temperature 175 °C |
11600 psi @Temperature 347 °F |
4; ISO 178 |
Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry) Amodel® A-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, high flexural modulus and high tensile strength. Excellent creep resist.. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | ASTM D790 |
Polyram RamLloy PBB106 PC/ABS Alloy, UV Stabilized UV stabilized PC/ABS alloy for injection molding applications.Information provided by Polyram. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | ISO 178-93 |
Wellman Wellamid® MRT1487 BK 32% Mineral Reinforced, Toughened Grade Nylon 66 Description: Mineral Reinforced, Toughened Grade Nylon 66Information provided by Wellman. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | ASTM-D790 |
Polyram RamTal PM7009 Acetal, UV Stabilized UV stabilized polyacetal copolymer for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
Zeon Chemicals Zeonor® 1020R Cyclo Olefin Polymer Zeonor® is a line of thermoplastic polyolefin resin with an excellent combination of optical and electronic properties. These unique Cyclo Olefin Polymer (COP) was developed by Zeon Corporation usi.. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | D790 |
Zhejiang Juner 302-G0 Flammable Resistant and Low Separate Out Mode Applications: Electrons and Electricity: TV Components, Plugs of Computers, Exhaust Fans of Computers, Plugs, Sockets, Shells of Electronics, Framework of Level Output Transformers, Pipe Pedestals, .. |
|||
Flexural Strength | 80.0 MPa @Strain 3.50 % |
11600 psi @Strain 3.50 % |
ISO 178 |
DuPont Performance Polymers Delrin® FG500P NC010 Acetal (POM)
(Unverified Data**) Medium Viscosity Acetal Homopolymer Developed for Food Contact Applications Delrin FG500P is a medium viscosity acetal homopolymer with improved thermal stability. It has been developed for consider.. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
Chi Mei Wonderloy® PC-365 PC/ABS Alloy High Heat, High Impact |
|||
Flexural Strength | >= 80.0 MPa @Diameter >=100 mm |
>= 11600 psi @Diameter >=3.94 in |
Perpendicular to laminations; IEC 1212-2 4.1 |
Hippe PF CC 22 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Rolled Tube Used in mechanical and electrical applications. Coarse weave (18-30 threads per cm).Information provided by Hippe. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | ASTM D790, ISO 178 |
EPICHEM Epicarb PC Polycarbonate Characteristics: high fluidity, good impact |
|||
Flexural Strength | >= 80.0 MPa @Diameter >=100 mm |
>= 11600 psi @Diameter >=3.94 in |
Perpendicular to laminations; IEC 1212-2 4.1 |
Hippe PF CC 31 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in mechanical, electrical and electronic applications. Fine weave (>30 threads per cm).Information provided by Hippe. |
|||
Flexural Strength | 80.0 MPa | 11600 psi | 23°C, 50% RH; ASTM D790 |
Asahi Kasei Xyron® A1400 PPE/PA Oil ResistantInformation provided by Asahi Kasei |
|||
Flexural Strength | 80.0 - 100 MPa | 11600 - 14500 psi | Compression; ISO 178 |
Raschig Group 5567 DAP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl phthalate molding compound free from halogens. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exc.. |
|||
Flexural Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | ASTM D790 |
Gromax PBT 1200-211D Product Description: PBT unreinforced middle viscosity injection molding grade.Characteristics:Excellent electrical propertyExcellent temperature resistance, high heat distortion temperature.Excelle.. |