Victrex® PEEK 150FC30 Easy Flow
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled |
| Manufacturer | Victrex |
| Trade Name | PEEK |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Victrex® PEEK 150FC30 Easy Flow.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: High performance thermoplastic material, 30% reinforced with carbon fibre / graphite / PTFE PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding, easy flow, FDA food contact compliant, colour black.Typical Application Areas: Tribological applications with thin cross sections or long flow lengths for high strength. Excellent wear resistance, very low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.Information provided by Victrex.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ASTM D792 |
| Water Absorption at Saturation | 0.30 % @Temperature 23.0 °C |
0.30 % @Temperature 73.4 °F |
immersion; ISO 62-1 |
| 0.45 % @Temperature 100 °C |
0.45 % @Temperature 212 °F |
immersion; ISO 62-1 | |
| Viscosity | 275000 cP @Temperature 400 °C |
275000 cP @Temperature 752 °F |
Melt; ISO 11443 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | 380°C nozzle, 180°C tool; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | 380°C nozzle, 180°C tool; ISO 294-4 |
| Spiral Flow | 13.0 cm @Thickness 1.00 mm |
5.12 in @Thickness 0.0394 in |
380°C nozzle, 180°C tool |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 83 | 83 | ISO 868 |
| Tensile Strength at Break | 35.0 MPa @Temperature 275 °C |
5080 psi @Temperature 527 °F |
ISO 527 |
| 50.0 MPa @Temperature 225 °C |
7250 psi @Temperature 437 °F |
ISO 527 | |
| 65.0 MPa @Temperature 175 °C |
9430 psi @Temperature 347 °F |
ISO 527 | |
| 100 MPa @Temperature 125 °C |
14500 psi @Temperature 257 °F |
ISO 527 | |
| 160 MPa @Temperature 23.0 °C |
23200 psi @Temperature 73.4 °F |
ISO 527 | |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| Flexural Strength | 45.0 MPa @Temperature 275 °C |
6530 psi @Temperature 527 °F |
ISO 178 |
| 80.0 MPa @Temperature 175 °C |
11600 psi @Temperature 347 °F |
ISO 178 | |
| 160 MPa @Temperature 125 °C |
23200 psi @Temperature 257 °F |
ISO 178 | |
| 230 MPa @Temperature 23.0 °C |
33400 psi @Temperature 73.4 °F |
ISO 178 | |
| Flexural Modulus | 12.0 GPa | 1740 ksi | ISO 178 |
| Compressive Strength | 45.0 MPa @Temperature 200 °C |
6530 psi @Temperature 392 °F |
ISO 604 |
| 110 MPa @Temperature 120 °C |
16000 psi @Temperature 248 °F |
ISO 604 | |
| 170 MPa @Temperature 23.0 °C |
24700 psi @Temperature 73.4 °F |
ISO 604 | |
| Izod Impact, Notched (ISO) | 5.50 kJ/m² | 2.62 ft-lb/in² | ISO 180/A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | ISO 180/U |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179/1U |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 45.0 µm/m-°C | 25.0 µin/in-°F | Average below Tg; ISO 11359 |
| 110 µm/m-°C | 61.1 µin/in-°F | Average above Tg; ISO 11359 | |
| CTE, linear, Parallel to Flow | 12.0 µm/m-°C | 6.67 µin/in-°F | Below Tg; ISO 11359 |
| 15.0 µm/m-°C | 8.33 µin/in-°F | Above Tg; ISO 11359 | |
| Thermal Conductivity | 0.850 W/m-K | 5.90 BTU-in/hr-ft²-°F | Average; ISO 22007-4 |
| 1.70 W/m-K | 11.8 BTU-in/hr-ft²-°F | Along flow; ISO 22007-4 | |
| Melting Point | 343 °C | 649 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 315 °C | 599 °F | ISO 75A-f |
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 |
| 147 °C | 297 °F | Midpoint; ISO 11357 | |
| UL RTI, Mechanical with Impact | 180 °C | 356 °F | UL 746B |
| UL RTI, Mechanical without Impact | 240 °C | 464 °F | UL 746B |
| Oxygen Index | 43 % @Thickness 3.20 mm |
43 % @Thickness 0.126 in |
ISO 4289 |
| Glow Wire Test | 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1e+05 | 1e+05 | 1V; IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 100 °C | <= 212 °F | Hopper Temperature |
| Nozzle Temperature | 380 °C | 716 °F | |
| Mold Temperature | 180 °C | 356 °F | |
| 170 - 200 °C | 338 - 392 °F | ||
| Dry Time | 3.00 hour @Temperature 150 °C |
3.00 hour @Temperature 302 °F |
|
| 5.00 hour @Temperature 120 °C |
5.00 hour @Temperature 248 °F |