- Polymer Property : Linear Mold Shrinkage = 0.0020 cm/cm
Polymer Property : Linear Mold Shrinkage = 0.0020 cm/cm Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D-955 |
| Plaskolite Optix® CP - 82 UVA General Purpose Acrylic Resin OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli.. |
|||
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Polymer Resources PPX-G10HF Modified-PPO, 10% Glass Reinforced, High Flow Modified-Polyphenylene Oxide, 10% Glass Reinforced, High FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inf.. |
|||
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm @Thickness 3.17 mm |
0.0020 - 0.0040 in/in @Thickness 0.125 in |
ASTM D955 |
| RTP Company RTP 4005 A FR (Hot Water Moldable) Polyphthalamide (PPA), Glass Fiber - Flame Retardant |
|||
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0050 in/in @Thickness 0.126 in |
ASTM D955 |
| Eastman Eastar GN002 Copolyester, Natural
(discontinued **) Eastar GN002 Copolyester is a glycol modified polyethylene terephthalate (PET) with an added mold release. Eastar GN002 copolyester will not crystallize and thus offers wider processing latitude tha.. |
|||
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0060 in/in @Thickness 0.126 in |
ASTM D 955 |
| RTP Company RTP 899 X 125746 A Acetal (POM) Carbon Fiber - Electrically Conductive - High Purity Preliminary Data Sheet |
|||
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 3.17 mm |
0.0020 in/in @Thickness 0.125 in |
ASTM D955 |
| RTP Company RTP 4699 X 93256 Syndiotactic Polystyrene (SPS) Electronic Encapsulation
(disc Electronic EncapsulationComments:Encapsulation GradeUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP .. |
|||
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | |
| Lehmann & Voss LUVOCOM® 1105-7920/RD PEEK, with glass fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Chemical and hydrolysis resistance parts, non flammable.High dimension.. |
|||
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | |
| Lehmann & Voss LUVOCOM® 50/CF/15/TF/15/SI/2/BK-HB Polycarbonate, with carbon fiber, PTFE, lubricant modified Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi.. |
|||
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | |
| Lehmann & Voss LUVOCOM® 65-7712/GY PP-copolymer, with carbon fiber and glass fiber, electrically conducting Applications: Office communication.Strong, stiff parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Information provided by Lehmann & Voss & Co.KG.. |
|||
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | |
| Lehmann & Voss LUVOCOM® 1-0889-2 Polyamide 66, with carbon fiber and glass fiber, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Electrically conductive, suitable for continuous discharging of statically .. |
|||
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | |
| Lehmann & Voss LUVOCOM® 1105/GF/30/BK-1 PEEK, with glass fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Chemical and hydrolysis resistance parts, non flammable.High dimension.. |
|||
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ISO 2577 |
| Polyram RamOfin PPH501G4 Polypropylene, 20% Glass Fiber, Flame Retardant Glass fiber 20% reinforced, halogen free, flame retardant polypropylene for injection molding applications.Information provided by Polyram. |
|||
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm @Thickness 3.17 mm |
0.0020 - 0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| RTP Company RTP 102 FR Polypropylene (PP), Glass Fiber - Flame Retardant |
|||
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 3.17 mm |
0.0020 in/in @Thickness 0.125 in |
ASTM D 955 |
| RTP Company RTP 2207 HF Polyetheretherketone (PEEK), Glass Fiber - High Flow |
|||
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 3.17 mm |
0.0020 in/in @Thickness 0.125 in |
ASTM D955 |
| RTP Company RTP 1203 S-65D Ester-based Thermoplastic Polyurethane Elastomer, Glass Fiber Reinforced |
|||
| Linear Mold Shrinkage | 0.0020 - 0.0035 cm/cm @Thickness 3.17 mm |
0.0020 - 0.0035 in/in @Thickness 0.125 in |
ASTM D955 |
| RTP Company RTP 203 FR UV Nylon 6/6 (PA), Glass Fiber - Flame Retardant - UV Stabilized The RTP series of flame retardant, glass fiber reinforced nylon materials are designed to provide the optimal balance of strength, electrical and ignition resistance properties while exhibiting exce.. |
|||
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm @Thickness 3.17 mm |
0.0020 - 0.0060 in/in @Thickness 0.125 in |
ASTM D955 |
| RTP Company RTP 205 D TFE 13 SI 2 Nylon 6/12 (PA), Glass Fiber - PTFE Lubricated - Silicone Lubricated |
|||
| Linear Mold Shrinkage | 0.0020 - 0.020 cm/cm | 0.0020 - 0.020 in/in | ASTM D955 |
| Cheng Yu Plastic NG1300S Nylon 66, 30% Glass Fiber Reinforced |
|||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Eastman Eastar MN058 Copolyester Eastar copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. Eastar MN058 Copolyester is a medical gra.. |
|||
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ASTM D955 |
| Covestro Bayblend® T 88-4N Polycarbonate/ABS Blend, 20% Glass Fiber Contains 20% glass fiber reinforcement, high stiffness.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – .. |
|||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | |
| E-Polymers TEKASTER® F615G55 55% Glass Fiber Reinforced High Modulus PET Polyester Resin: TEKASTER is thermoplastic polyester resins (PBT, PET) mostly injection molding. PBT has excellent mechanical properties and well balanced engineering plastics with an electrical pe.. |
|||
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 4.00 mm |
0.0020 in/in @Thickness 0.157 in |
|
| CP-Polymer-Technik Wellamid® 6000 GV 25 HWUVCP 25% Glass Fiber Nylon 6, UV Stabilized, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Arkema Group Plexiglas® V825-UVA5A Acrylic Plexiglas® V825-UVA5A is a thermoplastic acrylic resin formulated for injection molding and extrusion applications. It is formulated for specialty lighting packages requiring specific UV transmiss.. |
|||
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D-955 |
| Plaskolite Optix® CP - 75 UVA General Purpose Acrylic Resin OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli.. |
|||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM data MD |
| BASF Capron® 8334G Impact Modified, 40% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron 8334G is a heat stabilized, 40% glass fiber reinforced polyamide 6 molding compound developed for applications requiring a high level of stiffness combined with excellent impact performance. .. |
|||
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm @Thickness 3.17 mm |
0.0020 - 0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| RTP Company RTP 1399 X 115071 B Polyphenylene Sulfide (PPS), Glass Fiber - Carbon Nanotube - ESD Protection |
|||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Sumitomo Bakelite North America FM 4004 Fiberglass and Mineral Reinforced Phenolic Novolac FM 4004 is a fiberglass and mineral reinforced phenolic novolac compound. This compound exhibits excellent dimensional stability and good strength at elevated temperatures, and conforms to the requ.. |
|||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| A. Schulman POLYFLAM™ FCB 1236-8555 General Purpose Homopolymer Polypropylene DescriptionPolyfort® FCB 1236-8555 is a general purpose homopolymer polypropylene filled with 20% glass fiber.Information provided by A. Schulman. |
|||
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm |
0.0020 - 0.0050 in/in @Thickness 0.125 in |
ASTM D955 |
| RTP Company RTP 103 Polypropylene (PP), Glass Fiber |
|||
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm @Thickness 3.17 mm |
0.0020 - 0.0040 in/in @Thickness 0.125 in |
ASTM D955 |
| RTP Company RTP 1199 X 115085 D Polyethylene Terephthalate Glycol Modified (PETG), Carbon Nanotube - ESD Protection |
|||