Polymer Property : Flexural Strength = 23200 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	160 MPa @Temperature 23.0 °C	23200 psi @Temperature 73.4 °F	ISO 178
DuPont Performance Polymers Rynite® FR515 BK507 PET (Unverified Data**) Rynite® FR515 BK507 is a flame retardant 15% glass reinforced modified polyethtylene terephthalate. Recognized by UL as UL94V-0 at 0.8mm(0.03in). Has a 140C temp index. Excellent balance of electr..
Flexural Strength	160 MPa @Temperature 175 °C	23200 psi @Temperature 347 °F	ISO 178
Victrex® PEEK 450CA40 Polyetheretherketone, 40% Carbon Fibre Reinforced Product Description:High performance thermoplastic material, 40% carbon fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding and extrusion, standard flow, ..
Flexural Strength	160 MPa @Temperature 125 °C	23200 psi @Temperature 257 °F	ISO 178
Victrex® PEEK 450FC30 General Purpose Product Description: High performance thermoplastic material, 30% reinforced with carbon fibre / graphite / PTFE PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding and ext..
Flexural Strength	160 MPa @Thickness 1.57 mm	23200 psi @Thickness 0.0620 in	CW; ASTM D790
Industrial Laminates/Norplex NP192 Synthetic Fabric (discontinued **) Description: 8 oz. aramid and "soft glass" fibers are combined to make a fabric that is stronger than pure aramid and less abrasive than glass fabrics. This material is impregnated with a high tempe..
Flexural Strength	160 MPa @Strain 6.30 %	23200 psi @Strain 6.30 %	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® BKV 130 DUS008 901510 Nylon 6, Glass Fiber Reinforced, Impact Modified PA 6, 30% glass fibers, injection molding, impact modifiedInformation provided by LANXESS.
Flexural Strength	160 MPa @Strain 5.00 %	23200 psi @Strain 5.00 %	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® BKV 30 H2.0 EF 000000 Nylon 6, Glass Fiber Reinforced PA 6, 30% glass fibers, injection molding, improved flowability, heat-aging stabilizedInformation provided by LANXESS.
Flexural Strength	160 MPa @Strain 5.10 %	23200 psi @Strain 5.10 %	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® DP BKV 35 XF 901510 Nylon 6, 35% Glass Fiber PA 6, 35% glass fibers, injection molding, improved flowability, improved surface finishInformation provided by LANXESS.
Flexural Strength	160 MPa @Temperature -40.0 °C	23200 psi @Temperature -40.0 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® NB-5620S Nylon/Olefin GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	160 MPa @Temperature 23.0 °C	23200 psi @Temperature 73.4 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® T-663G15 Nylon-66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	160 MPa @Temperature 80.0 °C	23200 psi @Temperature 176 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® T-669VGB Nylon-66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	160 MPa @Temperature 23.0 °C	23200 psi @Temperature 73.4 °F	Practical Use (Water Absorption 1.6%); ASTM-D790
Toyobo GLAMIDE® TY-181GC Nylon/Elastomer GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	160 MPa @Temperature -40.0 °C	23200 psi @Temperature -40.0 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® TY-502NZ 6T-Nylon GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	160 MPa @Temperature 80.0 °C	23200 psi @Temperature 176 °F	Practical Use (Water Absorption 1.0%); ASTM-D790
Toyobo GLAMIDE® TY-791GT 6T-Nylon GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	160 MPa @Temperature -40.0 °C	23200 psi @Temperature -40.0 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® TY-835TC Nylon-66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	160 MPa @Thickness >=200 mm	23200 psi @Thickness >=7.87 in	ISO 178; IEC/EN 60893-2 5.1
Elektro-Isola G-Etronax B Phenolic, Glass Fabric Reinforcement, Dark Brown, Sheet High performance/price ratio insulation material. Self-extinguishing, halogen-free, very low smoke emission and toxicity. Mechanically much stronger than the Etronit and Etronax types.Information pr..
Flexural Strength	160 MPa @Treatment Temp. 50.0 °C, Time 3600 sec	23200 psi @Treatment Temp. 122 °F, Time 1.00 hour	ISO 178; IEC/EN 60893-2 5.1
Elektro-Isola G-Etronax PM GPO 3 Polyester, Glass Mat, Red, Sheets Description: Good electrical properties such as high breakdown voltage in air and oil and highest arc resistance and tracking resistance. Self-extinguishing. Low smoke emission, halogen-free.Applica..
Flexural Strength	>= 160 MPa @Temperature 150 °C	>= 23200 psi @Temperature 302 °F	Perpendicular to laminations; IEC 1212-2 5.1
Hippe EP GM 203 Glass Mat Reinforced Epoxy Resin - Sheet
Flexural Strength	>= 160 MPa @Temperature 150 °C	>= 23200 psi @Temperature 302 °F	Perpendicular to laminations; IEC 1212-2 5.1
Hippe EP GM 204 Glass Mat Reinforced Epoxy Resin - Sheet
Flexural Strength	160 MPa @Temperature 125 °C	23200 psi @Temperature 257 °F	ISO 178
Victrex® PEEK 150FC30 Easy Flow Product Description: High performance thermoplastic material, 30% reinforced with carbon fibre / graphite / PTFE PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding, easy ..