 POLYMER SEARCH

Styrolution Terlux® 2812 TR MABS

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded
Manufacturer Styrolution
Trade Name Terlux®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styrolution Terlux® 2812 TR MABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Terlux 2812 TR is a transparent grade of MABS for injection molding with high flowability.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
Physical Properties Metric English Comments
Water Absorption 0.70 %
0.70 %
ISO 62
Moisture Absorption at Equilibrium 0.35 %
0.35 %
23°C/50% R.H.; ISO 62
Linear Mold Shrinkage 0.0055 cm/cm
0.0055 in/in
ASTM Data; MD
Melt Flow 8.0 g/10 min

@Temperature 220 °C
 8.0 g/10 min

@Temperature 428 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 42.0 MPa
6090 psi
50mm/min; ISO 527
42.0 MPa
6090 psi
2 in/min; ASTM Test
Elongation at Break 20 %
20 %
50mm/min, Nominal strain; ISO 527
Elongation at Yield 4.0 %
4.0 %
50mm/min; ISO 527
Tensile Modulus 1.90 GPa
276 ksi
1mm/min; ISO 527
1.92 GPa
278 ksi
ASTM Test
Izod Impact, Notched 0.590 J/cm

@Thickness 3.17 mm
 1.11 ft-lb/in

@Thickness 0.125 in
 ASTM Test
Charpy Impact Unnotched 11.0 J/cm²
52.4 ft-lb/in²
ISO 179
7.00 J/cm²

@Temperature -30.0 °C
 33.3 ft-lb/in²

@Temperature -22.0 °F
 ISO 179
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
ISO 179
0.200 J/cm²

@Temperature -30.0 °C
 0.952 ft-lb/in²

@Temperature -22.0 °F
 ISO 179
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 µm/m-°C
44.4 µin/in-°F
ISO 11359
Deflection Temperature at 0.46 MPa (66 psi) 89.0 °C
192 °F
annealed; ASTM Test
93.0 °C
199 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 78.0 °C
172 °F
annealed; ASTM Test
87.0 °C
189 °F
ISO 75
Vicat Softening Point 87.0 °C
189 °F
Rate "A" Loading 1 (50 degC/h 10N); ASTM Test
87.0 °C
189 °F
(50 °C/h / 50N) - B/50; ISO 306
Glass Transition Temp, Tg 107 °C
225 °F
10 K/min; ISO 11357-1/-3
Optical Properties Metric English Comments
Transmission, Visible 80 %
80 %
unknown thickness
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 2.8

@Frequency 1.00e+6 Hz
 2.8

@Frequency 1.00e+6 Hz
 IEC 60250
3.0

@Frequency 100 Hz
 3.0

@Frequency 100 Hz
 IEC 60250
Dissipation Factor 0.013

@Frequency 1.00e+6 Hz
 0.013

@Frequency 1.00e+6 Hz
 IEC 60250
0.016

@Frequency 100 Hz
 0.016

@Frequency 100 Hz
 IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 230 - 260 °C
446 - 500 °F
Injection Molding
250 °C
482 °F
Injection molding
Mold Temperature 50.0 - 80.0 °C
122 - 176 °F
Injection Molding
90.0 °C
194 °F
Ejection temperature
Injection Velocity 60.0 mm/sec
2.36 in/sec
Injection molding
Drying Temperature 70.0 °C
158 °F
Injection Molding
Dry Time 2 - 4 hour
2 - 4 hour
Injection Molding
Moisture Content 0.70 %
0.70 %
ASTM Data
Descriptive Properties Value Comments
Color Clear
Commercial Status North America and Europe
Impact Modified Yes
Injection Molding Regrind <10%
NSF Std. 51 No
NSF Std. 61 No
Primary Processing Technique Injection Molding
Processing Blow Molding
Film Extrusion
Injection Molding
Profile Extrusion
Sheet Extrusion
Thermoforming
Special characteristic Platable
UL.UL-C Yes