Solvay Specialty Polymers KetaSpire® KT-820 SL45 Polyetheretherketone (PEEK)

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK)
Manufacturer Solvay Specialty Polymers
Trade Name KetaSpire®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers KetaSpire® KT-820 SL45 Polyetheretherketone (PEEK).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
KetaSpire® KT-820 SL45 is a PEEK based compound specifically designed to provide exceptionally low wear rates and good mechanical properties in applications where an external lubricant is provided.Features: Fatigue Resistant; Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; Good Wear Resistance; High Heat ResistanceUses: Automotive Applications; Bushings; Gears; Oil/Gas Applications; Thrust WasherInjection Molding Notes: Back Pressure: minimumInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.50 g/cc
0.0542 lb/in³
ASTM D792
Water Absorption 0.030 %

@Time 86400 sec
 0.030 %

@Time 24.0 hour
 ISO 62
Viscosity 380000 cP

@Shear Rate 1000 1/s,
Temperature 400 °C
 380000 cP

@Shear Rate 1000 1/s,
Temperature 752 °F
 Melt Viscosity; ASTM D3835
Linear Mold Shrinkage, Flow 0.00 - 0.0020 cm/cm

@Thickness 3.18 mm
 0.00 - 0.0020 in/in

@Thickness 0.125 in
Linear Mold Shrinkage, Transverse 0.013 - 0.015 cm/cm

@Thickness 3.18 mm
 0.013 - 0.015 in/in

@Thickness 0.125 in
 ASTM D955
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 400 °C
 2.0 g/10 min

@Load 4.76 lb,
Temperature 752 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 90
90
ASTM D785
Tensile Strength 161 MPa
23400 psi
ASTM D638
Tensile Strength, Yield 197 MPa
28600 psi
5 mm/min, Type 1A; ISO 527-2
Elongation at Break 1.5 %
1.5 %
Type 1A, 5 mm/min; ISO 527-2
1.5 %
1.5 %
5 mm/min; ASTM D638
Tensile Modulus 18.3 GPa
2650 ksi
ASTM D638
25.3 GPa
3670 ksi
1 mm/min, Type 1A; ISO 527-2
Flexural Strength 265 MPa
38400 psi
ASTM D790
273 MPa
39600 psi
ISO 178
Flexural Modulus 16.6 GPa
2410 ksi
ASTM D790
24.1 GPa
3500 ksi
ISO 178
Compressive Strength 127 MPa
18400 psi
ASTM D695
Shear Strength 84.1 MPa
12200 psi
ASTM D732
Izod Impact, Notched 0.690 J/cm
1.29 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.30 J/cm
9.93 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 8.50 kJ/m²
4.04 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 43.0 kJ/m²
20.5 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 17.0 µm/m-°C

@Temperature -50.0 - 50.0 °C
 9.44 µin/in-°F

@Temperature -58.0 - 122 °F
 1
Specific Heat Capacity 1.25 J/g-°C

@Temperature 50.0 °C
 0.299 BTU/lb-°F

@Temperature 122 °F
 ASTM C351
1.67 J/g-°C

@Temperature 200 °C
 0.399 BTU/lb-°F

@Temperature 392 °F
 ASTM C351
Thermal Conductivity 0.360 W/m-K
2.50 BTU-in/hr-ft²-°F
ASTM C177
Melting Point 342 °C
648 °F
ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 299 °C
570 °F
Annealed; ASTM D648
Glass Transition Temp, Tg 152 °C
306 °F
DSC
Processing Properties Metric English Comments
Rear Barrel Temperature 366 °C
691 °F
Middle Barrel Temperature 371 °C
700 °F
Front Barrel Temperature 377 °C
711 °F
Nozzle Temperature 382 °C
720 °F
Mold Temperature 177 - 204 °C
351 - 399 °F
Drying Temperature 149 °C

@Time 14400 sec
 300 °F

@Time 4.00 hour
Descriptive Properties Value Comments
Additive Carbon Fiber + PTFE Lubricant
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Black
Form Pellets
Injection Rate Fast
Processing Technique Injection Molding; Machining; Profile Extrusion
RoHS Compliance RoHS Compliant
Screw Compression Ratio 2.5:1.0 to 3.5:1.0