Plaskolite Optix® CA - 900 High Impact Grade Acrylic Resin
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Impact Modified, Molded , Acrylic, Optical Grade, Molded |
| Manufacturer | Plaskolite |
| Trade Name | Optix® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plaskolite Optix® CA - 900 High Impact Grade Acrylic Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
OPTIX® impact-modified grades offer 7 to 10 times the impact resistance of general purpose polymers while maintaining optical clarity.Information provided by Plaskolite, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D-792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D-955 |
| Melt Flow | 3.7 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.7 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 55.2 MPa | 8000 psi | ASTM D-638 |
| Elongation at Break | 25 % | 25 % | ASTM D-638 |
| Modulus of Elasticity | 2.00 GPa | 290 ksi | ASTM D-638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D-790 |
| Izod Impact, Notched | 0.427 J/cm @Thickness 6.35 mm |
0.800 ft-lb/in @Thickness 0.250 in |
ASTM D-256 |
| Gardner Impact | 2.82 J @Thickness 3.17 mm |
2.08 ft-lb @Thickness 0.125 in |
Falling Weight; ASTM D-3029 GB |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C | 38.9 µin/in-°F | ASTM D-696 |
| Maximum Service Temperature, Air | 50.0 °C | 122 °F | UL-746 ABC |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F | ASTM D-648 |
| Vicat Softening Point | 104 °C | 220 °F | ASTM D-1525 |
| Flammability, UL94 | HB | HB |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 2.0 % | <= 2.0 % | ASTM D-1003 |
| Transmission, Visible | 92 % | 92 % | ASTM D-1003 |
Users viewing this material also viewed the following:
- MV Labs CA1000 CaSO4 Calcium sulfate
- P & P Technology EC-J Silver Aluminum Loaded Silicone
- Pau Tai Avanstab OTS-3850 Organotin Stabilizer Octyl Thiotins/Methyl Thiotin
- Mo-Sci Corporation GL-0193 Hollow Glass Spheres
- Solvay Specialty Polymers Amodel® A-6135 HN Polyphthalamide (PPA), 35% Glass Fiber (Conditioned)
- Solvay Specialty Polymers Halar® 6514 Ethylene Chlorotrifluoroethylene Copolymer (ECTFE)
- Arlon 44430B020 0.020" (0.508 mm) Uncured Silicone Rubber with Fiberglass Substrate
- C.O.I.M. LARIPUR® LPR6520 Standard Adipate Ester Polyurethane
Copyright © lookpolymers.com All Rights Reserved