- Polymer Property : Melt Flow = 2.0 g/10 min
Polymer Property : Melt Flow = 2.0 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | (Condition L) ASTM D-1238 |
| Multibase Multi-Flex® TPE A 7410 NAT Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
| Melt Flow | 2.0 g/10 min @Load 0.325 kg, Temperature 270 °C |
2.0 g/10 min @Load 0.716 lb, Temperature 518 °F |
|
| Plastcom SLOVAMID 6 GF 15 FRG 2 LW PA6, 15% glass fibre, flame retardant FeaturesPA 6 for injection moulding, chemically reinforced with 15% glass fibre, with nonhalogen flame retardant. Main features: flammability in accordance with UL 94 V2 at 1.6 mm, glow wire at 960°.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Premix Thermoplastics PRE-ELEC® ESD 2300 PRE-ELEC ESD 2300 is a static dissipative thermoplastic compound based on PE-HD. The dissipative property is permanent and built into the polymer chain. PRE-ELEC ESD 2300 has been developed for mult.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Phillips 66 COPYLENE® CR020CL Polypropylene Impact Copolymer COPYLENE® CR020CL is a random copolymer formulated with advanced clarifier technology and with antistat and is specially designed to excel in extrusion blowmolding processes. EBM bottles will have .. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Solvay Engineered Polymers INDURE™ E1500 HG TPO
(discontinued **) Description: INDURE™ E1500 HG is a thermoplastic olefinic elastomer (TPO) designed for high-gloss thermoformed applications where excellent gloss retention after forming is required. This material.. |
|||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | Exxon Method |
| ExxonMobil Escorene® LD-104 LDPE Packaging Film Resin, High Clarity
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A homopolymer packaging film resin with excellent clarity and good stiffness. It is excellent either blown film or chill roll casting equipment. I.. |
|||
| Melt Flow | 2.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Ineos ABS Lustran® 743 General Purpose, High-Impact
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionLANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholding under a JV with La.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| NOVA Chemicals Novapol® LA-0218-AB LDPE Foam Resin
(discontinued **) Good heat sealing latitude, Moderate toughness, Easy processabilityApplications: Specifically designed for foam process, Blends with LLDPEAdditives: Good heat sealing latitude, Moderate toughness, E.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D 1238 |
| NOVA Chemicals Novapol® PF-0218-B Butene Copolymer LLDPE Film Resin PF-0218-B complies with the U.S. FDA specifications for olefin polymers and may be used in the U.S. as an article or component of an article intended for use in contact with food, without temperatur.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| LyondellBasell Lupolen® 5261 Z Q 456 High Density Polyethylene, Pipe and Sheet Extrusion Grade Lupolen 5261 Z Q 456 is a high density polyethylene (HDPE) with high melt viscosity for ram extrusion of peroxide crosslinked pipes (PE-Xa). The product is supplied as a nominal 20 mesh (840 µm) .. |
|||
| Melt Flow | 2.0 - 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 - 4.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| FKuR Kunststoff Bio-Flex® F 1130 Compostable PLA Blend The BIO-FLEX® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEX® does not contain any sta.. |
|||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Flint Hills 23T2A Random Copolymer Polypropylene Features: Clarified, autoclave and good impact strength. Product does not contain animal derived components.Applications: Designed for Blow molding and ThermoformingInformation provided by Flint H.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| LG Chemical LUTENE-H XL1800 HDPE Description: LUTENE-H XL 1800 is a optimum materials for under-floor heating and drinking water pipe by RAM type extrusion. It is excellent product with long-term internal pressure creep property an.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| IRPC Polimaxx Polene 2500H Polypropylene Block Copolymer CHARACTERISTICS: EXCELLENT HIGH IMPACT, HIGH TOUGHNESS GOOD EXTRUDABILITYAPPLICATIONS: SHEET / BLOW MOLD EXTRUSION AND INJECTION MOLDING FOR CORRUGATE SHEETS, SHEETS FOR FILE, HOUSEWARES, CONTAINERS.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
| Silon Tabond 3012 Adhesive Resin TABOND 3012 is an LLDPE based adhesive resin.Characteristics: • Highest adhesion to aluminium, copper, brass and steel • Adhesion durability at elevated temperatures and pressure cycling p.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
| Silon Tabond 3042 Impact Modifier for PA Tabond 3042 is a chemically modified Ethylene Copolymer/LLDPE.Information provided by Silon |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Borealis Nepol™ GB303HP 30% Long Glass Fiber Reinforced Polypropylene Nepol GB303HP is a 30% long glass fiber reinforced polypropylene grade, produced using Borealis ` propriety and exclusive, patented Nepol technology intended for injection molding and extrusion. Th.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
Base Resin; ISO 1133 |
| Borealis Superclean™ LR4201S Crosslinkable Polyethylene Insulation for Medium and High Voltage Power Cables Superclean LR4201S is a Superclean crosslinkable low density polyethylene (XLPE) for medium and high voltage power cable insulation. The formulation of LR4201S provides an optimum combination of go.. |
|||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| UBE V215 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Westlake DA591 9.0% Ethylene Vinyl Acetate Copolymer Westlake DA591 resin is a 9.0% EVA copolymer designed as a tie layer in multi-layered food packaging film. It has excellent clarity, excellent toughness, good resistance to load deformation, and goo.. |
|||
| Melt Flow | 2.0 - 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 - 4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D 1238 |
| RTP Company RTP 105 CC FR Polypropylene (PP), Glass Fiber - Chemically Coupled - Flame Retardant - UL94 V-0 |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Borealis Supercure™ LS4201R Polyethylene Insulation Compound, Crosslinkable Supercure™ LS4201R is a crosslinkable natural polyethylene compound, specially designed for insulation applications. Applications: Supercure™ LS4201R is intended for insulation of XLPE power cabl.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| ELASTO UK Dryflex® 500600S SEBS Based Material, Unfilled Qualities, 60A Hardness, Translucent The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| ELASTO UK Dryflex® 500800S SEBS Based Material, Unfilled Qualities, 80A Hardness, Translucent The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha.. |
|||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ExxonMobil Method |
| ExxonMobil LD331.08 EVA LD 331.08 Very Clear, High Impact Film Resin LD 331 Series films have superior impact strength and heat sealabilityInformation provided by ExxonMobil Chemical |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| DuPont Performance Polymers Delrin® 100T BK602 Acetal (POM)
(Unverified Data**) Toughened High Viscosity Acetal Homopolymer Delrin 100T BK602 is a toughened high viscosity acetal homopolymer grade with superior impact resistance. It is designed for highly stressed parts where o.. |
|||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | melt flow rate; ExxonMobil Method |
| ExxonMobil Vistamaxx™ 3020FL Propylene-based Elastomer - High Purity, Low Gel Product Description: Vistamaxx 3020FL propylene-based elastomer is an olefinic elastomer primarily composed of isostatic propylene repeat units with random ethylene distribution. It is produced us.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Braskem F020HC High Crystallinity Polypropylene Homopolymer Description: Very High Flexural Modulus, High ClarityApplications: Suggested Uses Include Compounding, Packaging, Thermoformed ContainersThis resin meets the requirements for olefin polymers as defi.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 400 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 752 °F |
ASTM D1238 |
| Solvay Specialty Polymers AvaSpire® AV-621 GF30 Polyaryletherketone (PAEK)
(Unverified Data**) AvaSpire AV-621 GF30 is a 30% glass fiber reinforced version of AvaSpire AV-621. This formulation offers better dimensional stability and lower warpage than 30% glass reinforced PEEK. This resin ret.. |
|||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | Condition I; ASTM D1238 |
| Asahi Kasei Delpet® 80N Acrylic Molding Compound, High Heat Grade 80N has high heat resistance and strength. Recommended for taillight lenses, reflectors, and other auto parts, and general lighting fixtures. General Delpet® qualities include attractive transpar.. |
|||