Polymer Property : Melt Flow = 2.0 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Melt Flow 2.0 g/10 min

@Load 0.325 kg,
Temperature 270 °C
2.0 g/10 min

@Load 0.716 lb,
Temperature 518 °F
Plastcom SLOVAMID 66 HI/1 TS PA66, improved strength
FeaturesModified with thermoplastic reactive caoutchouc, determined for mouldings with high toughness also at minus temperatures. Eligible application for ski-shoes, helmets for sport and other safe..
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
STN EN ISO 1133
Plastcom SLOVAMID® 6 GF 30 AS PA6 reinforced with glass fiber, anti-static agent
PA 6 for injection molding, reinforced with 30% glass fiber, contains antistatic agent for moldings used in the automotive, electrical, building, engineering and hobby industry - holders of electric..
Melt Flow 2.0 g/10 min

@Load 5.00 kg,
Temperature 230 °C
2.0 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ASTM D 1238
SABIC Innovative Plastics Cycolac® GHT3330 ABS (Asia Pacific)
High heat grade of ABS used for interior automotive components.This data was supplied by SABIC-IP for the Asia Pacific region.
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
NOVA Chemicals Dylark® FG7200 High-Heat Styrenic Copolymer
Product Description and Features: Styrene/maleic anhydride copolymer with high-heat resistance and high modulus. Resins designed for use in foam extrusion.Processing: Contact NOVA Chemicals techn..
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Phillips 66 COPYLENE® CR020CL Polypropylene Impact Copolymer
COPYLENE® CR020CL is a random copolymer formulated with advanced clarifier technology and with antistat and is specially designed to excel in extrusion blowmolding processes. EBM bottles will have ..
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Solvay Engineered Polymers INDURE™ E1500 HG TPO  (discontinued **)
Description: INDURE™ E1500 HG is a thermoplastic olefinic elastomer (TPO) designed for high-gloss thermoformed applications where excellent gloss retention after forming is required. This material..
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
M. Holland Company LD225 LDPE  (discontinued **)
Additives: Medium Antiblock, Medium SlipFeatures: Medium Antiblocking, High Clarity, High Gloss, Heat Sealable, Good Processability, Medium SlipUses: FilmProcessing Method: Blown FilmInformation pro..
Melt Flow 2.0 g/10 min
2.0 g/10 min
Exxon Method
ExxonMobil Escorene® LD-307 EVA Film Resin, Clarity, High Impact  (discontinued **)
Data provided by the manufacturer, Exxon Chemical.A 5.0% vinyl acetate copolymer, clarity film resin. Film made from this resin has superior impact strength and heat sealability.Applications: Froze..
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
NOVA Chemicals Novapol® PF-0218-F Butene LLDPE Film Resin
Toughness and strength, Ease of extrusionApplications: Cast films, BlendingAdditives: Process stabilizerFilm properties are typical of blown film extruded at a blowup ratio of 2.5:1, but are depende..
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Phillips 66 COPYLENE® CH020S Polypropylene, Homopolymer, BOPP
COPYLENE™ CH020S is a polypropylene homopolymer resin typically used by customers for BOPP (biaxially oriented polypropylene) Applications: Film ExtrusionInformation provided by Phillips 66.
Melt Flow 2.0 - 4.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 - 4.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
FKuR Kunststoff Bio-Flex® F 1110 Compostable PLA Blend
The BIO-FLEX® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEX® does not contain any sta..
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Inno-Comp INNOPOL® CS 1-6140 N 40% Talc-Filled Polypropylene Homopolymer
INNOPOL® CS 1-6140 N is a 40% talc-filled polypropylene homopolymer compound /PP-H TD40 (ISO 1043)/.INNOPOL® CS 1-6140 N is developed for producing injection molded components for household eq..
Melt Flow <= 2.0 g/10 min

@Load 21.6 kg,
Temperature 230 °C
<= 2.0 g/10 min

@Load 47.6 lb,
Temperature 446 °F
ASTM D1238
Solvay Specialty Polymers Solef® 6020 Polyvinylidene Fluoride (PVDF)
Solef® 6020 PVDF homopolymer has very high viscosity for membranes and lithium batteries. It is available exclusively as powder.Features: Homopolymer; Ultra High ViscosityUses: Batteries; Membran..
Melt Flow 2.0 g/10 min

@Load 3.80 kg,
Temperature 230 °C
2.0 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM Data
Styron Pulse® 840P ABS + Polycarbonate
PULSE® 840P Engineering resin has been designed to provide excellent processability, high heat resistance, and high impact strength at both room and low temperatures. PULSE 840P Engineering resin..
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Borealis Himod™ FT6273 LDPE for Film
Himod FT6273 is a tubular, low-density polyethylene grade for the production of packaging films. Compared to standard LDPE grades, the Himod products provide a combination of higher stiffness and i..
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Borealis Nepol™ GB303HP 30% Long Glass Fiber Reinforced Polypropylene
Nepol GB303HP is a 30% long glass fiber reinforced polypropylene grade, produced using Borealis ` propriety and exclusive, patented Nepol technology intended for injection molding and extrusion. Th..
Melt Flow 2.0 g/10 min
2.0 g/10 min
ASTM D1238
A. Schulman POLYFLAM™ FPP 1007E Talc Filled Homopolymer Polypropylene
DescriptionPolyfort® FPP 1007E is a 40% talc filled homopolymer compound for extrusion applications.Information provided by A. Schulman.
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
A. Schulman POLYBATCH™ ASC-331 Inorganic Antislip Masterbatch Based in Polyethylene
DescriptionPOLYBATCH® ASC-331 is an inorganic antislip masterbatch based in polyethylene. ApplicationThis masterbatch was designed for use in moderate to heavy gauge applications to increase film ..
Melt Flow 2.0 - 4.0 g/10 min
2.0 - 4.0 g/10 min
ASTM D1238
A. Schulman PP 1188-01 Polypropylene Extra High-Impact Polypropylene
DescriptionPolypropylene PP 1188-01 is an extra high-impact polypropylene, copolymer type, with excellent low temperature properties. Information provided by A. Schulman.
Melt Flow 2.0 - 4.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
2.0 - 4.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D 1238
RTP Company RTP 102 FR Polypropylene (PP), Glass Fiber - Flame Retardant
Melt Flow 2.0 g/10 min
2.0 g/10 min
ASTM D1238
A. Schulman POLYFLAM™ FPP 1007E Talc Filled Homopolymer Polypropylene
DescriptionPolyfort® FPP 1007E is a 40% talc filled homopolymer compound for extrusion applications.Information provided by A. Schulman.
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
ELASTO UK Dryflex® 500800S SEBS Based Material, Unfilled Qualities, 80A Hardness, Translucent
The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha..
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
ExxonMobil LL 1002.09 Blown Film Resin
Product Description: LL 1002 resins are butane LLDPE designed for the blown film process. Films made form LL 1002 resins have very good tensile and toughness properties. LL 1002.09 is a granular mat..
Melt Flow 2.0 g/10 min
2.0 g/10 min
ASTM D1238
ExxonMobil Escorene™ FL 00226CC Ethylene Vinyl Acetate Copolymer (European Grade)
Product Description: FL 00226CC is a copolymer of ethylene and vinyl acetate offering low gel. Processing Conditions: Processing temperatures above 230°C (446°F) may cause resin degradation. Machi..
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Braskem TR3020C Random Copolymer Polypropylene
Description: Clarified, high flexural modulus. Applications: Suggested uses include extrusion, blow molding, thermoforming. Process: Blow Molding. This resin meets the requirements for olefin polym..
Melt Flow 2.0 g/10 min
2.0 g/10 min
ASTM D-1238
Bapolene® 222B Polyethylene Film Grade
Bapolene 222B is a butene linear low density polyethylene for blown film applications requiring superior impact strength and toughness. It complies with US FDA 21CFR177.1520.Applications: General p..
Melt Flow 2.0 g/10 min
2.0 g/10 min
Exxon Method
ExxonMobil Escorene® LL-3002 LLDPE/Hexene Premium Cast Stretch Film Resin, 0.8 mil Film  (discontinued **)
Data provided by the manufacturer, Exxon Chemical.A hexene copolymer LLDPE cast film resin. Films made from LL-3002 have outstanding tensile properties as well as stiffness and toughness. These su..
Melt Flow 2.0 g/10 min

@Load 0.325 kg,
Temperature 270 °C
2.0 g/10 min

@Load 0.716 lb,
Temperature 518 °F
Plastcom SLOVALEN PH 69 GF 40 PP, 40% glass fibre, mod. of mech. properties
FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 40% glass fibre, contains the modifier of mechanical properties. Increased strength in comparison with unfilled PP...
Melt Flow 2.0 - 6.0 g/10 min

@Load 12.5 kg,
Temperature 232 °C
2.0 - 6.0 g/10 min

@Load 27.6 lb,
Temperature 450 °F
ASTM D1238
Arkema Group KYNAR® 761 Polyvinylidene Fluoride Powder
Characteristics: White, non-hygroscopic powder. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeability, abrasion resistan..
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
DuPont Bynel® 3933 Anhydride-Modified Ethylene Vinyl Acetate Adhesive Resin  (discontinued **)
Bynel® Series 3900 resins are anhydride-modified ethylene vinyl acetate polymers. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process p..