Solvay Specialty Polymers AvaSpire® AV-755 SL45 Polyaryletherketone (PAEK)

Category Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Carbon Fiber Filled
Manufacturer Solvay Specialty Polymers
Trade Name AvaSpire®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers AvaSpire® AV-755 SL45 Polyaryletherketone (PAEK).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AV-755 SL45 is a wear resistant grade of AvaSpire® polyaryletherketone (PAEK) designed to provide low wear rates and high pressure-velocity (PV) tolerance in lubricated wear environments. Like the other members of the AvaSpire® AV-700 series, AV-755 SL45 offers more attractive economics than PEEK while retaining most of PEEK's key attributes. In addition to the outstanding wear resistance, the resin also offers the outstanding combination of chemical resistance, mechanical strength and stiffness at elevated temperatures, as well as long-term and high temperature thermal-oxidative stability. AV-755 SL45 is formulated with a binary anti-friction/anti-wear additive system comprised of carbon fiber and graphite. By virtue of its additive system, this resin also offers, exceptionally high stiffness and very low moisture absorption.Features: Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; Good Wear Resistance; High Heat ResistanceUses: Automotive Applications; Bearings; Bushings; Rollers; Seals; Thrust Washer; Wear StripInjection Molding Notes: Back Pressure: MinimumInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.53 g/cc
0.0553 lb/in³
ASTM D792
Water Absorption 0.010 %

@Time 86400 sec
0.010 %

@Time 24.0 hour
ISO 62
Viscosity 600000 cP

@Shear Rate 1000 1/s,
Temperature 400 °C
600000 cP

@Shear Rate 1000 1/s,
Temperature 752 °F
Melt Viscosity; ASTM D3835
Linear Mold Shrinkage, Flow 0.00 - 0.0020 cm/cm

@Thickness 3.18 mm
0.00 - 0.0020 in/in

@Thickness 0.125 in
Linear Mold Shrinkage, Transverse 0.012 - 0.014 cm/cm

@Thickness 3.18 mm
0.012 - 0.014 in/in

@Thickness 0.125 in
ASTM D955
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 400 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 752 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 88
88
ASTM D785
Tensile Strength 169 MPa
24500 psi
5 mm/min; ASTM D638
Tensile Strength, Yield 173 MPa
25100 psi
5 mm/min, Type 1A; ISO 527-2
Elongation at Break 0.90 %
0.90 %
Type 1A, 5 mm/min; ISO 527-2
0.90 %
0.90 %
5 mm/min; ASTM D638
Tensile Modulus 30.4 GPa
4410 ksi
1 mm/min, Type 1A; ISO 527-2
33.6 GPa
4870 ksi
5 mm/min; ASTM D638
Flexural Strength 250 MPa
36300 psi
ASTM D790
266 MPa
38600 psi
ISO 178
Flexural Modulus 25.9 GPa
3760 ksi
ASTM D790
30.2 GPa
4380 ksi
ISO 178
Compressive Strength 120 MPa
17400 psi
ASTM D695
Shear Strength 70.0 MPa
10200 psi
ASTM D732
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.20 J/cm
5.99 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 6.80 kJ/m²
3.24 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 25.0 kJ/m²
11.9 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 7.00 µm/m-°C

@Temperature -50.0 - 50.0 °C
3.89 µin/in-°F

@Temperature -58.0 - 122 °F
1
Specific Heat Capacity 1.17 J/g-°C

@Temperature 50.0 °C
0.280 BTU/lb-°F

@Temperature 122 °F
ASTM C351
1.61 J/g-°C

@Temperature 200 °C
0.385 BTU/lb-°F

@Temperature 392 °F
ASTM C351
Thermal Conductivity 0.700 W/m-K
4.86 BTU-in/hr-ft²-°F
ASTM C177
Melting Point 343 °C
649 °F
ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 278 °C

@Thickness 3.20 mm
532 °F

@Thickness 0.126 in
Annealed; ASTM D648
Glass Transition Temp, Tg 152 °C
306 °F
DSC
Processing Properties Metric English Comments
Rear Barrel Temperature 354 °C
669 °F
Middle Barrel Temperature 366 °C
691 °F
Front Barrel Temperature 371 °C
700 °F
Nozzle Temperature 374 °C
705 °F
Melt Temperature 366 - 388 °C
691 - 730 °F
Mold Temperature 149 - 177 °C
300 - 351 °F
Drying Temperature 149 °C

@Time 14400 sec
300 °F

@Time 4.00 hour
Descriptive Properties Value Comments
Additive Carbon Fiber + Graphite Lubricant
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Black
Form Pellets
Injection Rate Fast
Processing Technique Injection Molding; Machining; Profile Extrusion
RoHS Compliance RoHS Compliant
Screw Compression Ratio 2.0:1.0 to 3.0:1.0