Polymer Property : Melt Flow = 1.0 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Melt Flow 1.0 - 4.0 g/10 min
1.0 - 4.0 g/10 min
(Condition L) ASTM D-1238
Multibase Multi-Flex® TPE A 6900 LC BLK
The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Melt Flow 1.0 g/10 min

@Load 0.325 kg,
Temperature 270 °C
1.0 g/10 min

@Load 0.716 lb,
Temperature 518 °F
Plastcom SLOVAMID 66 CF 40 PA66, 40% carbon fibre
FeaturesChemically reinforced with 40% carbon fibre, suitable for mouldings with high strength and toughness also at minus temperatures. Used in the automotive, engineering and electrical industry. ..
Melt Flow 1.0 g/10 min

@Load 0.325 kg,
Temperature 270 °C
1.0 g/10 min

@Load 0.716 lb,
Temperature 518 °F
Plastcom SLOVAMID 66 GF 25 FRG 5 TS PA66, 25% glass fibre, flame retardant
FeaturesPA 66 for injection moulding, chemically reinforced with 25% glass fibre and non-halogen flame retardant, with heat resistance and nonflammability, achieves V 0 in accordance with UL 94. Non..
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
STN EN ISO 1133
Plastcom SLOVAMID 66 GF 25 FRI 3 Polyamide 66, 25% Glass Fiber, Halogen Free Flame Retardant
FeaturesPA 66 for injection moulding, chemically reinforced with 25% glass fiber and non-halogen flame retardant, with heat and flammability resistance, achieves V-0 in accordance with UL 94. Non-h..
Melt Flow <= 1.0 g/10 min

@Load 5.00 kg,
Temperature 190 °C
<= 1.0 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ASTM D1238
Polimeri Europa Europrene® SOL T 6205 Styrene - Butadiene Block Copolymer
Europrene® SOL T 6205 is a radial block copolymer obtained by anionic polymerization. The polymer is based on styrene and butadiene, where bound styrene is 25% weight and diblock content is 15%. ..
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Polimeri Europa Flexirene® FG 20 U Butene Copolymer Linear Low Density Polyethylene
Flexirene FG 20 U is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for blown film extrusion.Main Applications: Flexirene FG 20 U is recommended for the ..
Melt Flow 1.0 g/10 min
1.0 g/10 min
(Condition L) ASTM D-1238-94a
Multibase Multi-Flex® TPO D 5302 E MB
Data provided by Multibase.
Melt Flow 1.0 g/10 min

@Load 0.325 kg,
Temperature 270 °C
1.0 g/10 min

@Load 0.716 lb,
Temperature 518 °F
Plastcom SLOVAMID 6 GF 50 LTS PA6, 50% glass fibre
FeaturesPA 6 for injection moulding, chemically strengthened with 50% of glass fibre, for mouldings with high strength and toughness used in the automotive, electrical, engineering and consumer-good..
Melt Flow 1.0 g/10 min

@Load 5.00 kg,
Temperature 190 °C
1.0 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ISO 1133
Premix Thermoplastics PRE-ELEC® CP 1318  (discontinued **)
PRE-ELEC CP 1318 is a conductive thermoplastic compound based on a polyolefin copolymer. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivit..
Melt Flow 1.0 - 4.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 - 4.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Polymer Resources AC-G10 Acetal Copolymer, 10% Glass Reinforced
Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Melt Flow 1.0 - 4.0 g/10 min
1.0 - 4.0 g/10 min
ASTM D1238
Polymer Resources PPX-FRG30 Modified PPO, UL 94 V-1, 30% Glass Reinforced  (Unverified Data**)
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Melt Flow 1.0 g/10 min

@Load 2.16 kg
1.0 g/10 min

@Load 4.76 lb
ISO 1133
Total Finathene® LL 4010 FH 18 LLDPE film  (discontinued **)
Linear low density polyethylene made by gas phase process for blown film applications. Advised temperature profile: 190 to 220°C.Information provided provided by Total Petrochemicals.Total Petroche..
Melt Flow 1.0 g/10 min
1.0 g/10 min
Exxon Method
ExxonMobil Exceed™ 350D60 LDPE/Hexene Tough Premium Film Resin  (discontinued **)
Data provided by the manufacturer, Exxon Chemical.A hexene copolymer produced using Exxon Chemical's EXXPOL® technology. Films made from EXCEED 350D60 resin have outstanding tensile, impact streng..
Melt Flow 1.0 g/10 min
1.0 g/10 min
Exxon Method
ExxonMobil Exceed™ 350D65 LDPE/Hexene Tough Premium Liner Film Resin, 0.8 mil Film  (discontinued **)
Data provided by the manufacturer, Exxon Chemical.A hexene copolymer produced using Exxon Chemical's EXXPOL® technology. Films made from EXCEED 350D65 resin have outstanding tensile, impact streng..
Melt Flow 1.0 g/10 min
1.0 g/10 min
ASTM D1238
Huntsman PE1504 EVA Film Extrusion  (discontinued **)
5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: Fi..
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 275 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 527 °F
ASTM D3275
Solvay Specialty Polymers Halar® 9414 Polyethylene, Chlorotrifluoroethylene (ECTFE)  (Unverified Data**)&l
Halar® 9414 is a filled, pearl-white, semicrystalline melt processable fluorinated resin. It is designed for electrostatic powder coatings and can be used as a primer, intermediate or topcoat in pr..
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Celanese Ateva® 1062ASB Ethylene Vinyl Acetate Copolymer Film  (discontinued **)
Ateva® 1062ASB resin is suitable for co-extrusion applications with excellent sealability, strength, and low COF. This EVA resin may be safely used as articles or components of articles intended f..
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Celanese AT 253 Low Density Polyethylene (LDPE)  (discontinued **)
AT 253 is a non-CSA homopolymer suitable for pipe applications. This resin should not be used in pipes for potable water. Additives: Applications: Tubes & PipesInformation provided by Celanese Corp..
Melt Flow 1.0 g/10 min
1.0 g/10 min
ASTM D1238
LyondellBasell Petrothene® GA601032 Linear Low Density Polyethylene
ApplicationsPETROTHENE® GA 601 series are pelletized, linear low density polyethylenes for applications requiring maximum strength and toughness. These products offer excellent additive homogene..
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Multibase Multi-Flex® A 7606 TPE Thermoplastic Elastomer
Features: Chemical Resistance, Good Heat StabilizedOzone ResistantGeneral Purpose Friction, Low Processability, Good Forms:PelletsProcessing Method:ExtrusionInjection Molding Uses: Automotive App..
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 400 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 752 °F
ASTM D1238
Solvay Specialty Polymers AvaSpire® AV-722 Polyaryletherketone (PAEK)
AvaSpire® AV-722 is an unreinforced polyaryletherketone (PAEK) that offers improved economics relative to PEEK while retaining most of PEEK's key performance attributes. AV-722 resin has been for..
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Polyram Bondyram® 4108 Maleic Anhydride Modified Linear Low Density Polyethylene
Recommended as coupling agent for PE composites filled with high filler content for halogen Free Flame Retarded cables composites.Information provided by Polyram.
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
ELASTO UK Dryflex® 500450S SEBS Based Material, Unfilled Qualities, 45A Hardness, Translucent
The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha..
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238, ISO 1133
DuPont™ Entira® AS MK 400 Ionomer Resin
Entira™ AS MK400 is an extremely hygroscopic ionomer resin that is supplied as free-flowing pellets.
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
condition E; ASTM D1238
DuPont™ Surlyn® 9020 Ionomer Resin, Zinc
Surlyn® 9020 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The resin contains an addit..
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Dow TUFLIN™ HS-7046 NT 7 Linear Low Density Polyethylene Resin
Hexene Linear Low Density Resin Slot Cast Extrusion Outstanding Drawdown Capability Complies with U.S. FDA 21 CFR 177.1520 (c) 3.1a TUFLIN™ HS-7046 NT 7 is an ethylene-hexene copolymer, designed f..
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM-D1238
Braskem FG31D LLDPE Blown Film Extrusion Polyethylene Copolymer
The FG31D resin is a linear low-density polyethylene, copolymer of butene-1, produced by the solution process for blow film extrusion in blends with polyethylene. It has excellent mechanical propert..
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Carmel Olefins IPETHENE® 210 Low Density Polyethylene
IPETHENE® 210 is a low density polyethylene extrusion grade, containing no additives. It exhibits a good balance between mechanical and optical properties. APPLICATIONS IPETHENE® 210 is mainly u..
Melt Flow 1.0 g/10 min
1.0 g/10 min
ASTM D1238
ExxonMobil LL 1001.32 Cast Film Resin  (discontinued **)
LL 1001.32 is a butene LLDPE resin. Films made from LL 1001.32 have very good tensile and toughness properties.Information provided by ExxonMobil Chemical
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Braskem LL 118 LLDPE Blown Film Extrusion Polyethylene
Description: LL118 is a Linear Low Density Polyethylene, copolymer of butene-1, produced by Spherilene process. Developed for blown film extrusion in blends with polyethylenes. Films obtained with t..