Solvay Specialty Polymers Amodel® FR-4133 Polyphthalamide (PPA) Resin, 33% Glass Reinforced, Dry as Molded  (d

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® FR-4133 Polyphthalamide (PPA) Resin, 33% Glass Reinforced, Dry as Molded  (d.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AMODEL FR-4133 is a 33% glass-reinforced polyphthalamide (PPA) resin designed for electrical and electronic applications. This UL94-V0 resin offers the highest mechanical and electrical properties, plus superior thermal performance to resist blistering during lead-free SMT processes. Color stability is enhanced compared to previous flame-retarded grades. Quick crystallization in water-cooled molds allows for fast cycle times using mold temperatures as low as 150°F (65°C).Information provided by Solvay Advanced Polymers
Physical Properties Metric English Comments
Specific Gravity 1.68 g/cc
1.68 g/cc
ASTM D792
1.68 g/cc
1.68 g/cc
ISO 1183A
Moisture Absorption at Equilibrium 0.10 %
0.10 %
24 hours; ASTM D570
Mechanical Properties Metric English Comments
Hardness, Rockwell R 125
125
ASTM D785
Tensile Strength, Yield 191 MPa
27700 psi
ISO 527
199 MPa
28900 psi
ASTM D638
72.0 MPa

@Temperature 175 °C
10400 psi

@Temperature 347 °F
ISO 527
89.0 MPa

@Temperature 150 °C
12900 psi

@Temperature 302 °F
ISO 527
119 MPa

@Temperature 100 °C
17300 psi

@Temperature 212 °F
ISO 527
Elongation at Break 1.8 %
1.8 %
ISO 527
2.2 %

@Temperature 100 °C
2.2 %

@Temperature 212 °F
ISO 527
3.1 %

@Temperature 150 °C
3.1 %

@Temperature 302 °F
ISO 527
4.6 %

@Temperature 175 °C
4.6 %

@Temperature 347 °F
ISO 527
Elongation at Yield 1.8 %
1.8 %
ASTM D638
Tensile Modulus 14.7 GPa
2130 ksi
ISO 527
15.7 GPa
2280 ksi
ASTM D638
5.80 GPa

@Temperature 175 °C
841 ksi

@Temperature 347 °F
ISO 527
7.00 GPa

@Temperature 150 °C
1020 ksi

@Temperature 302 °F
ISO 527
10.4 GPa

@Temperature 100 °C
1510 ksi

@Temperature 212 °F
ISO 527
Flexural Strength 266 MPa
38600 psi
ISO 178
267 MPa
38700 psi
ASTM D790
101 MPa

@Temperature 175 °C
14600 psi

@Temperature 347 °F
ISO 178
127 MPa

@Temperature 150 °C
18400 psi

@Temperature 302 °F
ISO 178
173 MPa

@Temperature 100 °C
25100 psi

@Temperature 212 °F
ISO 178
Flexural Modulus 12.3 GPa
1780 ksi
ISO 178
12.8 GPa
1860 ksi
ASTM D790
5.00 GPa

@Temperature 175 °C
725 ksi

@Temperature 347 °F
ISO 178
6.50 GPa

@Temperature 150 °C
943 ksi

@Temperature 302 °F
ISO 178
9.40 GPa

@Temperature 100 °C
1360 ksi

@Temperature 212 °F
ISO 178
Compressive Strength 156 MPa
22600 psi
ASTM D695
Shear Strength 83.0 MPa
12000 psi
ASTM D732
Izod Impact, Notched 0.850 J/cm
1.59 ft-lb/in
ASTM D256
Izod Impact, Unnotched 6.41 J/cm
12.0 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 11.0 kJ/m²
5.23 ft-lb/in²
ISO 180/1A
Izod Impact, Unnotched (ISO) 50.0 kJ/m²
23.8 ft-lb/in²
ISO 180/1U
Charpy Impact Unnotched 9.70 J/cm²
46.2 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 1.40 J/cm²
6.66 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 326 °C
619 °F
ASTM D3418
326 °C
619 °F
ISO 11357-3
Deflection Temperature at 1.8 MPa (264 psi) 301 °C
574 °F
ASTM D648
307 °C
585 °F
ISO 75Af
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Surface Resistance 2.00e+16 ohm
2.00e+16 ohm
ASTM D257
Dielectric Strength 20.0 kV/mm

@Thickness 1.57 mm
508 kV/in

@Thickness 0.0620 in
ASTM D149
30.0 kV/mm

@Thickness 0.787 mm
762 kV/in

@Thickness 0.0310 in
ASTM D149
Comparative Tracking Index >= 600 V
>= 600 V
Hot Wire Ignition, HWI >= 120 sec
>= 120 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A