Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 6.50 GPa | 943 ksi | STN EN ISO 178 |
Plastcom SLOVAMID 66 GF 25 Polyamide 66, 25% Glass Fiber FeaturesChemically reinforced with 25% glass fiber, suitable for mouldings with high strength and toughness also at low temperatures. Used in the automotive, engineering and electrical industry. W.. |
|||
Flexural Modulus | 6.50 - 12.1348 GPa @Temperature -40.0 - 120 °C |
943 - 1760.03 ksi @Temperature -40.0 - 248 °F |
Average value: 9.41 GPa Grade Count:2 |
Overview of materials for Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler". Specific grades with glass content between 25%.. |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | ASTM D790 |
Loxim 130 01V0 Polycarbonate, 30% Glass Filled, Flame Retardant Information provided by Loxim Industries |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | ISO 178 |
Grupo Repol Dinalon® A1S25 G25PV0 25% Glass Reinforced, V-0 Rated (Phosphorous) Nylon 66 Mechanical properties are for dry as molded samples.Information provided by Grupo Repol. |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics ULTEM 2200 PEI (Europe-Africa-Middle East) 20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0 and 5VA listing. |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Ultem 2200N PEI 20% Glass fiber filled Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Ultem 2210K PEI (Europe-Africa-Middle East) 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics ULTEM AUR200G6 PEI (Europe-Africa-Middle East) The data listed in this data sheet are the lower specification limits, apart from the MFR, CTE, HDT at 1.8 MPa, Density, Tensile strain, Water Absorption, Thermal Conductivity and Shrinkage which ar.. |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Ultem PW2200 PEI (Europe-Africa-Middle East) 20% Glass fiber filled, standard flow Polyetherimide (Tg 217°C). Product designed and certified for use in Potable Water
applications. KTW, WRAS, ACS certified. NSF61 and W270 pending. US FDA and.. |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Stat-kon DE002E PC (Europe-Africa-Middle East) LNP* STATKON* DE002E is a compound based on Polycarbonate resin containing Carbon Fiber. Added features include; Easy Molding.This data was supplied by SABIC-IP for the Europe-Africa-Middle East reg.. |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp BX06088 SAN (Europe-Africa-Middle East) LNP* THERMOCOMP* BX06088 is a compound based on Styrene Acrylonitrile Blend resin containing Carbon Fiber. Added features include: Electrically Conductive.This data was supplied by SABIC-IP for the.. |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | ISO Data |
Styrolution Terblend® N NG-06 30% Glass Filled ABS/PA6 (Dry) Terblend N NG-06 is a 30% glass fiber reinforced ABS/PA6 blend with extra high rigidity and dimensional stability.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.. |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP WF0049 PBT (Europe-Africa-Middle East) LNP* Thermocomp* WF0049 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant. |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp RFB24 PA 66 (Europe-Africa-Middle East) LNP* THERMOCOMP* RFB24 is a compound based on PA 66 resin containing Glass Bead, Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | 2 mm/min; ISO 178 |
Sax Polymers SAXAMID 126F5 Nylon 6, 25% Glass Fiber SAXAMID 126F5 is a polyamide 6 injection-molding-grade reinforced with 25% glass fibers.Information provided by SAX Polymers |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | ASTM D790 |
Plenco 7080 Phenolic, Nodular, Compression Molded PLENCO 07080 is an organic fiber reinforced phenolic molding compound, offering improved mechanical strength properties along with outstanding resistance to cracking and degradation from soap and de.. |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | 2mm/min; ISO 178 |
Borealis Xmod™ GD301FE Polypropylene, Glass Fiber Reinforced Xmod™ GD301FE is a 30 % chemically coupled high performance glass fiber reinforced polypropylene compound intended for injection molding. This material shows excellent mechanical properties also a.. |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | ISO 178 |
Polyram PlusTek PA4802G6BK10 Nylon 66 for Injection Molding, 30% Glass Fiber Reinforced, PTFE Lubricated 30% Glass fiber reinforced, PTFE lubricated Nylon 66 for injection molding application.Information provided by Polyram. |
|||
Flexural Modulus | 6.50 - 8.00 GPa | 943 - 1160 ksi | ISO 178 |
Vyncolit 2530 W Novolac Phenolic Mineral and organic filled phenolic molding compound with excellent thermal properties.USES: Lamp sockets, special lamp holders, pan handles and knobs.Information provided by Vyncolit, a Sumitomo Ba.. |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | cond; ISO 178 |
DSM Novamid® 3021GH30 NAT PA66-GF30 30% Glass Reinforced, Heat Stabilized |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | DIN 52457 |
CP-Polymer-Technik Wellamid® 6000 GVS 20/10 HWCP 20% Glass Fiber and 10% Glass Sphere Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | DIN 52457 |
CP-Polymer-Technik Wellamid® 6600/58 GV 30 HWCP 30% Glass Fiber Nylon 66, Impact Modified Until -40°C, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | 2 mm/min; ISO 178 |
Eurostar Star C BX6088 ABS, 20% Carbon Filled, Injection Molding Star C BX06008 is a 20% Carbon Fiber Reinforced ABS Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | 2 mm/min; ISO 178 |
Eurostar Staramide RFB24 PA66, 20/10% Glass Fiber/Glass Bead Filled Injection Molded RFB24 is a Glass Bead and Glass Fiber Reinforced, Polyamide 66 Injection Molding Resin (also known as Staramide 66 2010VK Z3)Information provided by Polymer Technology & Services, the North American.. |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | ISO 178 |
Eurotec® Tecomid® NB40 GR20 NL PA 6 20% glass fiber reinforced Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good.. |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | ISO 178 |
Eurotec® Tecodur® PB70 GR20 NL CA 01 PBT/PET 20% glass fiber reinforced Excellent stiffness and hardnessGood mechanical strengthGood creep and fatigue behaviorVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance.. |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | ISO 178 |
Ascend Performance Materials Vydyne® R533 NT Nylon 66, 33% Glass Reinforced, Conditioned Vydyne® R533 NT is general-purpose, 33% glass-fiber reinforced PA66 resin. Available in natural, it is an injection-molding grade that is lubricated for good machine feed, flow and mold release. Gl.. |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | 2 [mm/min]; ISO 178 |
Akro-Plastic Akromid® S3 GF 23 1 (2917) PA 6.10 Dry, 23% Glass Filled A characteristic property of AKROMID® S (PA 6.10) is that it has a renewable-resource content of up to 70 % and therefore fulfils the current definition of a bioplastic. The plant-based raw materia.. |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | ASTM D790 |
Beijing Chemical Industry KAIFA® 301-G20F PBT Resin 20% glass fiber reinforced, flame retardant, good flow, low bleedingInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Flexural Modulus | 6.50 GPa | 943 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON RCL42 PA 66 (Europe-Africa-Middle East) LNP* Stat-kon* REL42 is a compound based on Nylon 66 resin containing PTFE, Carbon Fiber. |