Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 5.00 GPa | 725 ksi | |
Plastcom SLOVAMID 66 GF 15 HI PA66, 15% glass fibre FeaturesChemically reinforced with 15% glass fibre, suitable for mouldings with high strength and toughness also at minus temperatures. Used in the automotive, engineering and electrical industry. I.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | |
Plastcom SLOVAMID 66 GF 15 TS PA66, 15% glass fibre FeaturesChemically reinforced with 15% glass fibre, suitable for mouldings with high strength and toughness also at minus temperatures. Used in the automotive, engineering and electrical industry. W.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
Ovation Polymers Opnyl OP66GF13 Nylon 66, 13% Glass Reinforced Nylon 66 - Glass reinforced (13 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ASTM D790 |
NHEP Spectron™ E6126 Nylon 66, 20% Glass Fiber Natural color. E6126 exhibits high rigidity, mechanical strength, and excellent appearance. It is suitable for wide range of applications.Property data measured at room temperature, 50% RH.Informati.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
Nilit FRIANYL B63 W-SG-GV 2010 Nylon 6 for injection molding, 20% mineral filled, 10% glass fiber reinforced Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Modulus | 5.00 - 25.5 GPa @Temperature -40.0 - 250 °C |
725 - 3700 ksi @Temperature -40.0 - 482 °F |
Average value: 13.8 GPa Grade Count:3 |
Overview of materials for Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled". Specific grades with glass content between 45% an.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | |
Lehmann & Voss LUVOCOM® 50-8376 Polycarbonate, unreinforced Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical engineering.Antistatic.Isotropic shrinkage characteristics.Reduced moment.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ASTM D790 |
Loxim 315 01V0 Nylon 6 Information provided by Loxim Industries |
|||
Flexural Modulus | 5.00 GPa @Temperature 150 °C |
725 ksi @Temperature 302 °F |
ISO 178 |
Solvay Specialty Polymers Amodel® AFA-6133 V0 Z Polyphthalamide (PPA), 33% Glass Fiber (Conditioned) Amodel® AFA-6133 V0 Z is a 33% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin specifically formulated for connector applications requiring compatibility with both in.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® GR-4017 ABS, Glass Filled Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL GTX GTX8120P PPE+PA (Europe-Africa-Middle East) GTX8120P is a glass filled extrudable Noryl GTX with low thermal conductivity, suitable for thermal breaks |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP UF003AS PPA (Europe-Africa-Middle East) LNP* THERMOCOMP* UF003AS is a compound based on Polyphthlamide resin containing Glass Fiber. Added features include; Heat Stabilized. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | Tangent; ASTM D790 |
Washington Penn Homopolymer Polypropylene 50% Talc Filled Talc-filled polypropylene compounds have been tailored specifically to meet the requirements of each of the major automobile producers. Grades are available to meet FDA food and drug packaging requi.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
Polyram RamTal PM3009G4 Polyacetal for Injection Molding, 20% Glass Fiber Reinforced 20% Glass fiber reinforced polyacetal for injection molding applications.Information provided by Polyram. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | D790 |
Zhejiang Juner 301-G15 15% Glass Fibre Reinforced and Flammable Resistant Applications: Electrons and Electricity: TV Components, Plugs of Computers, Exhaust Fans of Computers, Plugs, Sockets, Shells of Electronics, Framework of Level Output Transformers, Pipe Pedestals, .. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
Polyram PlusTek PB305G33BK37 Nylon 6, 33% Glass Fiber Reinforced, UV and Heat Stabilized 33% Glass fiber reinforced, UV and heat stabilized Nylon 6. Approved and listed by W.R.A.S. and NSF/ANSI 61 International for potable water.Information provided by Polyram. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
Polyram PlusTek PD300G5 Nylon 12 for Injection Molding, 25% Glass-Fiber Reinforced 25% Glass-fiber reinforced Nylon 12, heat stabilized and hydrolysis resistant for injection molding applications.Information provided by Polyram. |
|||
Flexural Modulus | >= 5.00 GPa | >= 725 ksi | ASTM-D790 |
Polyram PlusTek RA300G4 Nylon 6.6, 20% Glass Fiber 20% glass fiber reinforced polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ASTM D 790 |
Cossa Polimeri ESTAPROP 1540 GFC V0 H Flame Retardant Polypropylene, 20% Glass Filled PP with 20% glass fiber reinforcedFlame retardant class UL V0 and class M2 according to NL P92-507Information provided by Cossa Polimeri S.r.l. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | DIN 52457 |
CP-Polymer-Technik Wellamid® 6000 GV 15 HWCP 15% Glass Fiber Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
Eurostar Staramide PF003U PA6, 15% Glass Fiber Filled, Injection Molded Staramide PF003U is an 15% Glass Fiber Reinforced, Polyamide 6 Injection Molding Resin, UV Stabilized (also known as Staramide 6 15V S4)Information provided by Eurostar. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
Ascend Performance Materials Vydyne® 909 BK Nylon 66/6, 25% Glass Reinforced, Conditioned Vydyne® 909 BK is a halogenated, 25% glass-filled, flame-retardant PA66/6 copolymer with excellent strength and toughness. It is lubricated for machine feed and easy mold release and has Underwrite.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
Ascend Performance Materials Vydyne® 909 Nylon 66/6, 25% Glass Reinforced, Ignition Resistant, Conditioned Vydyne® 909 is halogenated, 25% glass-filled, flame-retardant PA66/6 copolymer with excellent strength and toughness. It is lubricated for machine feed and easy mold release and has an Underwriters.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
BASF Ultramid® B3EG6 BK00564 30% Glass Filled PA6 (Conditioned) Ultramid B3EG6 BK00564 is a 30% glass fiber reinforced, pigmented black injection molding PA6 grade. It conforms to FDA requirements of 21 CFR 177.1500. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
BASF Ultramid® B3EG6 LS BK 23189 30% Glass Filled PA6 (Conditioned) Information provided by BASF |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
BASF Ultramid® B3GK24 10/20% Glass Bead/Fiber Filled PA6 (Dry) Ultramid B3GK24 is 30% combined glass-fiber and glass bead injection molding PA6 grade for industrial articles having very high dimensional stability. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ASTM D790 |
Adell BR-33 Nylon 6, 15% Glass Reinforced Data provided by Adell Plastics, Inc. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ASTM D790 |
Beijing Chemical Industry KAIFA® 301-G15 PBT Resin 15% glass fiber reinforced, flame retardantInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO Value |
BASF Capron® 8260 40% Mineral-Filled Nylon 6 (Dry)
(discontinued **) Capron 8260 is a 40% mineral reinforced polyamide 6 injection molding compound. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability includi.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | |
Lehmann & Voss LUVOCOM® 50/GF/20/TF/10/BK Polycarbonate, with glass fiber and PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi.. |