Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 5.00 GPa @Temperature 23.0 °C |
725 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYabs N20 GF17 ABS, Glass Fiber-Reinforced Information provided by Polykemi AB |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ASTM D790 |
NHEP Spectron™ E6126 Nylon 66, 20% Glass Fiber Natural color. E6126 exhibits high rigidity, mechanical strength, and excellent appearance. It is suitable for wide range of applications.Property data measured at room temperature, 50% RH.Informati.. |
|||
Flexural Modulus | 5.00 - 10.0 GPa | 725 - 1450 ksi | ASTM D790 |
Raschig Group PiMC 1249 Sanitary, mix color PiMC is a Powder in-Mould Coating designed to improve the surface quality, durability and aesthetic appearance of SMC/BMC products. The PiMC is electro statically sprayed onto the heated mould surfa.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 3262R PC (Asia Pacific) Lexan* 3262R Polycarbonate (PC) resin is a 20% glass fiber filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant GF-PC has an UL-94 V2@1.5mm rating and is available .. |
|||
Flexural Modulus | 5.00 - 14.0 GPa @Temperature -40.0 - 121 °C |
725 - 2030 ksi @Temperature -40.0 - 250 °F |
Average value: 8.45 GPa Grade Count:8 |
Overview of materials for Nylon 66, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. .. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | |
Lehmann & Voss LUVOCOM® 1-8218 Polyamide 66, with carbon fiber, toughness-modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts; impact resistance.Reduced moment of inertia compared with metal parts.Elec.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | DIN 53452; ASTM D790 |
Kolon KOPA® KN333G15 G/F Reinforced Nylon 66 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstandin.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ASTM D790 |
Loxim 220 01V0 Polybutylene Terephthalate Information provided by Loxim Industries |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | 2mm/min; ASTM D790 |
Kingfa PBT-G15 15% Glass Fiber Reinforced PBT Features:Good size stabilityHigh mechanical propertiesHigh heat resistanceExcellent balance propertiesApplications:Injection moldingApplication partsAuto handleDoor latchE & E partsInformation Provi.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | |
Lehmann & Voss LUVOCOM® 1100/GF/20/EM/MR Polyether sulfone, with glass fiber, easy flowing, demolding aid Applications: Apparatus- and precision engineering, film- and photo industry, sporting- and leisure goods, medical- and electrical enineering, aircraft- and aerospace industry.High dimensionally sta.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | |
SPS Guang Zhou PONYLâ„¢ EP4003G10 Non-halogen flame retardance/GF10%-PA66 Characteristic: Good flame retardance, high mechanical properties, superior heat resistance, good dimensional stabilityApplications: E/E partsInformation Provided by SPS (Guang Zhou) Ltd. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP DF0029P PC LNP THERMOCOMP* DF0029P is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Exceptional Processing. Flame Retardant. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL GTX GTX8120P PPE+PA (Europe-Africa-Middle East) GTX8120P is a glass filled extrudable Noryl GTX with low thermal conductivity, suitable for thermal breaks |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
Unitika A1022GFL15 PA6, 15% Glass Fiber Reinforced, Dry Information provided by Unitika Ltd. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
Unitika A1030GFL PA6, 30% Glass Fiber Reinforced, Conditioned Information provided by Unitika Ltd. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
Unitika A175G15 PA66, 15% Glass Fiber Reinforced, Dry Information provided by Unitika Ltd. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ASTM-D790 |
Polyram PlusTek PA352M6 Nylon 6.6, 30% Low Friction Mineral Filled 30% low friction mineral filled polyamide 6.6 lubricated with molybdenum for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ASTM-D790 |
Polyram PlusTek RD302G6 Nylon 12, 30% Glass Fiber 30% glass-fiber reinforced polyamide 12 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | DIN 52457 |
CP-Polymer-Technik Wellamid® 6000 GV 15 HWCP 15% Glass Fiber Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | DIN 52457 |
CP-Polymer-Technik Wellamid® 6600/50 GV 15 HWCP 15% Glass Fiber Nylon 66, Impact Modified Until 0°C, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Flexural Modulus | >= 5.00 GPa | >= 725 ksi | IEC 1212-2 5.2 |
Hippe PF CP 207 Cellulose Paper Reinforced Phenolic Resin - Sheet Used in mechanical applications. Used in mechanical properties better than other PF CP types. Poor electrical properties under normal humidity. Also available in hot-punching versions. Improved .. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
Ascend Performance Materials Vydyne® 909 Nylon 66/6, 25% Glass Reinforced, Ignition Resistant, Conditioned Vydyne® 909 is halogenated, 25% glass-filled, flame-retardant PA66/6 copolymer with excellent strength and toughness. It is lubricated for machine feed and easy mold release and has an Underwriters.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
BASF Ultramid® B3EG6 30% Glass Filled PA6 (Conditioned) Ultramid B3EG6 is a 30% glass fiber reinforced injection molding PA6 grade. It conforms to FDA requirements of 21 CFR 177.1500. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ASTM D790 |
Beijing Chemical Industry KAIFA® 304-G20 PBT Resin 20% glass fiber reinforced, flame retardant, low bleeding, UV-resistantInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ASTM D790 |
Beijing Ranger Chem PBT-MFC-G0 FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
BASF Ultramid® B3WG6 BK00564 30% Glass Filled PA6 (Conditioned) Ultramid B3WG6 BK00564 is a 30% glass fiber reinforced, pigmented black, heat stabilized injection molding PA6 grade. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ASTM D790 |
Beijing Chemical Industry KAIFA® 301-G15 PBT Resin 15% glass fiber reinforced, flame retardantInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Flexural Modulus | 5.00 - 12.5 GPa | 725 - 1810 ksi | Average value: 8.93 GPa Grade Count:22 |
Overview of materials for Melamine-Phenolic Copolymer This property data is a summary of similar materials in the MatWeb database for the category "Melamine-Phenolic Copolymer". Each property range of values reported is minimum and maximum values of ap.. |
|||
Flexural Modulus | 5.00 GPa @Temperature 23.0 °C |
725 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYfill PPC GF15030 PD1 VT2 Polypropylene Copolymer, Glass Fiber Reinforced, Chemically Coupled, Heat Stabilized Information provided by Polykemi AB |