Polymer Property : Flexural Strength = 18400 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 127 MPa
18400 psi
ASTM D790
SABIC Innovative Plastics Lexan® LF1520 PC (Asia Pacific)
Flexural Strength 127 MPa
18400 psi
ISO 178
SABIC Innovative Plastics LNP Lubricomp DFL329EF PC
LNP LUBRICOMP* DFL329EF is a compound based on Polycarbonate resin containing Flame Retardant, Glass Fiber, PTFE. Added features of this material include: Flame Retardant.This data was supplied by ..
Flexural Strength 127 MPa

@Temperature 150 °C
18400 psi

@Temperature 302 °F
ISO 178
Solvay Specialty Polymers Amodel® FR-4133 Polyphthalamide (PPA) Resin, 33% Glass Reinforced, Dry as Molded  (d
AMODEL FR-4133 is a 33% glass-reinforced polyphthalamide (PPA) resin designed for electrical and electronic applications. This UL94-V0 resin offers the highest mechanical and electrical properties, ..
Flexural Strength 127 MPa
18400 psi
ASTM D790
Solvay Specialty Polymers AvaSpire® AV-630 Polyaryletherketone (PAEK)
AvaSpire® AV-630 is an unreinforced polyaryletherketone (PAEK) developed as an alternative to low melt flow PEEK for the extrusion of ultra-thin films. Films with thicknesses as low as 0.2 mils (..
Flexural Strength 127 MPa
18400 psi
ISO 178
Solvay Specialty Polymers AvaSpire® AV-651 Polyaryletherketone (PAEK)
AvaSpire® AV-651 is an unreinforced polyaryletherketone (PAEK) that offers more ductility and impact strength than PEEK, with higher chemical and environmental stress cracking resistance than Ava..
Flexural Strength 127 MPa
18400 psi
ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP 5C003 FP-V (PVDF)
LNP THERMOCOMP* 5C003 is a compound based on Polyvinylidene Fluoride resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive.
Flexural Strength 127 MPa
18400 psi
ISO 178
SABIC Innovative Plastics LNP Thermocomp 9X06477 SPS
LNP* Thermocomp* 9X06477 is a compound based on Syndiotactic Polystyrene resin containing Glass Fiber. Characteristics of this grade is Heat Stabilized.This data was supplied by SABIC-IP for the Am..
Flexural Strength 127 MPa
18400 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGN2000 PC (Asia Pacific)
Flexural Strength 127 MPa
18400 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Infino® LB-3150GW PC, 15% Glass Filled High Impact
High-impact resistant PC/GF that can be used for middle mold frame of LCD TVInformation provided by Samsung Cheil Industries.
Flexural Strength 127 MPa
18400 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Starex® GR-4020 ABS, 20% Glass Filled
Information provided by Samsung Cheil Industries.
Flexural Strength 127 MPa
18400 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Starex® GR-4030 ABS, 30% Glass Filled
Information provided by Samsung Cheil Industries.
Flexural Strength 127 MPa
18400 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Infino® LB-3150GW PC, 15% Glass Filled High Impact
High-impact resistant PC/GF that can be used for middle mold frame of LCD TVInformation provided by Samsung Cheil Industries.
Flexural Strength 127 MPa
18400 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Starex® GR-4020 ABS, 20% Glass Filled
Information provided by Samsung Cheil Industries.
Flexural Strength 127 MPa
18400 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Starex® GR-4030 ABS, 30% Glass Filled
Information provided by Samsung Cheil Industries.
Flexural Strength 127 MPa
18400 psi
ISO 178
SABIC Innovative Plastics LNP Lubricomp KFI12A Acetal Homopolymer
LNP LUBRICOMP* KFI12A is a compound based on Acetal Homopolymer resin containing Glass Fiber, Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABI..
Flexural Strength 127 MPa
18400 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP WCP36 PBT (Europe-Africa-Middle East)
LNP* LUBRICOMP* WCP36 is a compound based on Polybutylene Terephalate resin containing Carbon Fiber, PTFE, Silicone. Added features include; Internally Lubricated, Electrically Conductive.
Flexural Strength 127 MPa
18400 psi
ASTM D790
SABIC Innovative Plastics Xenoy® 1760 PBT+PC (Asia Pacific)
Flexural Strength 127 MPa
18400 psi
ASTM D 790
SABIC Innovative Plastics LNP Thermocomp 5C003
LNP THERMOCOMP* 5C003 is a compound based on Polyvinylidene Fluoride resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as THERMOCOMP* FP-VC..
Flexural Strength 127 MPa
18400 psi
ASTM D790
Plenco 7556 Phenolic, Briquette, Injection Molded
PLENCO 07556 is a glass fiber reinforced novolac phenolic molding compound, with good physical strengths and heat resistance along with excellent dimensional stability. UL recognized under component..
Flexural Strength 127 MPa
18400 psi
DIN EN ISO 178
Wolf Kunststoff ZEDEX® ZX-324V2T A3F PEEK, PTFE Modified
Reduced friction; High wear resistance; High elasticity; Stress resistantApplications: Shipbuilding; Chemical Engineering; Automotive Technology; Machine ToolsInformation provided by Zedex
Flexural Strength 127 MPa
18400 psi
ASTM D790
A. Schulman ComAlloy Lubrilon® 511 Polycarbonate, Glass Fiber/PTFE, UL
Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma..
Flexural Strength 127 MPa
18400 psi
ASTM D790
Asahi Kasei Thermylene® P6-30FG-0632 30% Glass Fiber Reinforced, Heat Stabilized
Information provided by Asahi Thermofil
Flexural Strength 127 MPa
18400 psi
ASTM D790
Solvay Specialty Polymers AvaSpire® AV-630 Polyaryletherketone (PAEK)  (Unverified Data**)
AvaSpire AV-630 is an unreinforced polyaryletherketone (PAEK) developed as an alternative to low melt flow PEEK for the extrusion of ultra-thin films. Films with thicknesses as low as 0.2 mils (5 mi..
Flexural Strength 127 MPa
18400 psi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DFL329 PC
LNP LUBRICOMP* DFL329 is a compound based on Polycarbonate resin containing 10% Glass Fiber, 15% PTFE. Added features of this material include: Flame Retardant, Internally Lubricated.
Flexural Strength 127 MPa
18400 psi
ISO 178
Solvay Specialty Polymers AvaSpire® AV-651 Polyaryletherketone (PAEK)  (Unverified Data**)
AvaSpire AV-651 is an unreinforced polyaryletherketone (PAEK) that offers more ductility and impact strength than PEEK, with higher chemical and environmental stress cracking resistance than AvaSpir..