Solvay Specialty Polymers Amodel® AS-1933 HS Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AS-1933 HS Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel AS-1933 HS is a 33% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material exceeds the performance required by the automotive industry for polymeric materials exposed to antifreeze at 226°F (108°C), even when tested at 275°F (135°C). Potential applications include a variety of automotive components such as thermostat housings, heater core endcaps, heater hose connectors, and water inlets, outlets and valves. - Black: AS-1933 HS BK 324Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
ISO 1183/A
Filler Content 33 %
33 %
Glass Fiber Reinforcement
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.8 MPa
11000 psi
After Immersion in 50/50 Glycol/Water Mixture for 1,000 hours at 275°F (135°C); ASTM D638
212 MPa
30700 psi
ISO 527-2
221 MPa
32100 psi
ASTM D638
Elongation at Break 2.5 %
2.5 %
ASTM D638
2.5 %
2.5 %
ISO 527-2
Tensile Modulus 7.58 GPa
1100 ksi
After Immersion in 50/50 Glycol/Water Mixture for 1,000 hours at 275°F (135°C); ASTM D638
11.7 GPa
1700 ksi
ASTM D638
12.6 GPa
1830 ksi
ISO 527-2
Flexural Strength 309 MPa
44800 psi
ISO 178
Flexural Yield Strength 313 MPa
45400 psi
ASTM D790
Flexural Modulus 10.6 GPa
1540 ksi
ISO 178
10.8 GPa
1570 ksi
ASTM D790
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
After Immersion in 50/50 Glycol/Water Mixture for 1,000 hours at 275°F (135°C); ASTM D256
0.910 J/cm
1.70 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 9.50 kJ/m²
4.52 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 7.60 J/cm²
36.2 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 312 °C
594 °F
ISO 11357-3
Deflection Temperature at 1.8 MPa (264 psi) 277 °C
531 °F
Unannealed; ASTM D648
278 °C
532 °F
Unannealed; ISO 75-2/Af
Processing Properties Metric English Comments
Feed Temperature 79.4 °C
175 °F
Hopper Temperature
Rear Barrel Temperature 304 - 318 °C
579 - 604 °F
Front Barrel Temperature 316 - 329 °C
601 - 624 °F
Melt Temperature 321 - 343 °C
610 - 649 °F
Mold Temperature 135 °C
275 °F
Drying Temperature 121 °C
250 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content 0.10 %
0.10 %
Descriptive Properties Value Comments
Additive Heat Stabilizer
Appearance Black
Automotive Specifications ASTM D4000 PA121 G35 Color: BK324 Black
ASTM D6779 PA121G35
BOSCH N28 BN05-OX1 BN0510-GF45-3Gsw01SO Color: BK324 Black
CHRYSLER MS-DB478 CPN4116 Color: Black
FORD WSS-M4D861-A3 Color: BK324 Black
GM GMP.PPA.019
GM GMW16360 GMW 16360P-PPA-GF35
ISO 1874 PA6T/6I/66, MH, 12-120, GF33 Color: BK324 Black
PSA Peugeot-Citroën SPA X62 4203
VALEO PDT NVB 10 057 Color: BK324 Black
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Antifreeze Resistant
Glycol Resistant
Good Chemical Resistance
Good Creep Resistance
Good Dimensional Stability
Good Stiffness
Heat Stabilized
High Heat Resistance
High Strength
Forms Pellets
Generic PPA
Processing Method Injection Molding
RoHS Compliance RoHS Compliant
Uses Automotive Applications
Automotive Under the Hood
Housings
Industrial Applications
Industrial Parts
Machine/Mechanical Parts
Metal Replacement
Power/Other Tools
Thick-walled Parts
Valves/Valve Parts