Polymer Property : Tensile Strength at Break = 221 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 221 MPa
32100 psi
5.1 mm/min; ASTM D638
PolyOne Stat-Tech™ NN-40CF/000 FRV0 Natural Polyamide 66 (Nylon 66)
Information provided by PolyOne
Tensile Strength at Break 221 MPa
32100 psi
ASTM D638
Niche Polymer PA66GF43BK Nylon 66, 43% Glass Fiber Filled
Information provided by Niche Polymer
Tensile Strength at Break 221 MPa
32100 psi
ASTM D638
Niche Polymer PA66GF43N Nylon 66, 43% Glass Fiber Filled
Information provided by Niche Polymer
Tensile Strength at Break 221 MPa
32000 psi
ASTM D638
Polymer Resources NY6-G43 Nylon 6, 43% Glass Reinforced
Nylon 6, 43% Glass Reinforced, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are teste..
Tensile Strength at Break 221 MPa
32000 psi
ASTM D638
Ravago Manufacturing Americas Hylon® N1043HL Nylon 6/6 (DAM)
Information provided by Ravago.
Tensile Strength at Break 221 MPa
32000 psi
ASTM D638
Ravago Manufacturing Americas Hylon® N1043L Nylon 6/6 (DAM)
Information provided by Ravago.
Tensile Strength at Break 221 MPa
32100 psi
5.1 mm/min; ASTM D638
PolyOne Edgetek® NN-40CF/000 FRV0 NATURAL Polyamide 66 (Nylon 66)
The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for ..
Tensile Strength at Break 221 MPa
32100 psi
Type I, 5.1 mm/min; ASTM D638
PolyOne Nymax™ GF 1200 A 43 HS Natural Polyamide 66 (Nylon 66)
The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil..
Tensile Strength at Break 221 MPa
32100 psi
Type I, 5.1 mm/min; ASTM D638
PolyOne Nymax™ GF 1200 A 43 Natural Polyamide 66 (Nylon 66)
The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil..
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 4008 A (Hot Water Moldable) Polyphthalamide (PPA), Glass Fiber
Tensile Strength at Break 221 MPa
32100 psi
ASTM D638
Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA)  (Unverified Data**)
Amodel AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater than 0..
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 4011 A (Hot Water Moldable) Polyphthalamide (PPA), Glass Fiber
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 4483 High Temperature Nylon (HTN), Carbon Fiber
Tensile Strength at Break 221 MPa
32000 psi
ASTM D638
Polymer Resources NY6-G43-[color]-H Nylon 6, 43% Glass Reinforced, Heat Stabilized
Nylon 6, 43% Glass Reinforced, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon..
Tensile Strength at Break 221 MPa
32100 psi
ISO 527-1/-2
Lanxess Durethan® DP AKV 50 HR H2.0 901510 Nylon 66, 50% Glass Fiber
PA 66, injection molding grade, 50% glass fibers, good heat-ageing resistance, and hydrolysis resistanceApplication Examples: coolant manifolds
Tensile Strength at Break 221 MPa
32100 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RFN18 PA 66 (Europe-Africa-Middle East)
LNP* Lubricomp* RFN18 is a compound based on Nylon 66 resin containing Glass Fiber, MOS2.
Tensile Strength at Break 221 MPa
32100 psi
ASTM D638
Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry)
Amodel® AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater th..
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 2183 Polyetherimide (PEI); Carbon Fiber
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 2283 LF Polyetheretherketone (PEEK), Carbon Fiber - Low Flow
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 2299 X 108578 C Polyetheretherketone (PEEK), Long Glass Fiber
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 291 Nylon 6/6 (PA), Carbon Fiber
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 285 A Nylon 6 (PA); Carbon Fiber
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 287 TFE 15 Nylon 6/6 (PA), Carbon Fiber - PTFE Lubricated
Tensile Strength at Break 221 MPa
32100 psi
ASTM D638
Solvay Specialty Polymers Amodel® AS-1933 HS Polyphthalamide (PPA)  (Unverified Data**)
Amodel AS-1933 HS is a 33% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material excee..
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 283 Nylon 6/6 (PA); Carbon Fiber
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 4285 Thermoplastic Polyimide (TPI) Carbon Fiber
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 4499 X 96265 High Temperature Nylon (HTN), Glass Fiber - PTFE Lubricated - Perfluoropolyether Oil
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 2285 LF TFE 15 Polyetheretherketone (PEEK), Carbon Fiber - PTFE Lubricated
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 4007 Polyphthalamide (PPA), Glass Fiber
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company VLF 82311 A Rigid Thermoplastic Polyurethane (RTPU), Long Glass Fiber