| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 531 °F | ASTM D-648 |
| PlastiComp Complet® LCF40-PPA Polyphthalamide, 40% Long Carbon Fiber Reinforced Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Polyphthalamide with 40% long carbon fiber reinforcementInformation provided by Plasti.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 531 °F | ASTM D-648 |
| PlastiComp Complet® LGF40-PPA Polyphthalamide, 40% Long Glass Fiber Reinforced Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Polyphthalamide with 40% long glass fiber reinforcementInformation provided by PlastiC.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C @Thickness 6.35 mm |
531 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| PolyOne Therma-Tech™ LC-6000 TC Liquid Crystal Polymer (LCP) Therma-Tech™ Thermal Management Compounds have been engineered to combine the heat transfer and cooling capabilities of metals with the design freedom, weight reduction and cost advantages of therm.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 531 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Amodel® AFA-6145 V0 Z Polyphthalamide (PPA)
(Unverified Data**) Amodel AFA-6145 V0 Z is a 45% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin specifically formulated for connector applications requiring compatibility with both infrar.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 531 °F | Annealed; ISO 75-2/Af |
| Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater than 0.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 531 °F | ASTM D648 |
| Solvay Specialty Polymers Amodel® A-1115 HS Polyphthalamide (PPA) Resin, 15% Glass Reinforced, Dry As Molded
AMODEL A-1115 HS resin is a 15% glass reinforced, heat stabilized polyphthalamide (PPA) which exhibits a high deflection temperature, high flexural modulus, and high tensile strength. Excellent cre.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 531 °F | ASTM D648 |
| Solvay Specialty Polymers Amodel® AFA-6133 V0 Polyphthalamide (PPA) Resin, 33% Glass Reinforced, Dry As Molded
&nbs AMODEL AFA-6133 V0 is a 33% glass-fiber reinforced grade of polyphthalamide (PPA) resin that was developed specifically for connector applications requiring compatibility with both "infrared" and "v.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 531 °F | ISO 75 |
| GEHR Plastics PEEK-mod Polyetheretherketone, 10% PTFE, 10% Graphite, 10% Carbon Fiber Polyether etherketone can be used at very high temperatures and it shows a good mechanical strength, toughness, hardness, flexural strength, and torsional strength. PEEK exhibits excellent chemical .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C @Thickness 3.20 mm |
531 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP UFL36AS PPA LNP* LUBRICOMP* UFL36AS is a Polyphthalamide (PPA) base resin containing 30% Glass Fiber, 15% PTFE. Added features of this material are: Heat Stabilized, Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 531 °F | Annealed; ASTM D648 |
| Solvay Specialty Polymers Amodel® AFA-6133 V0 Z Polyphthalamide (PPA), 33% Glass Fiber (Dry) Amodel® AFA-6133 V0 Z is a 33% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin specifically formulated for connector applications requiring compatibility with both in.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 531 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Amodel® AFA-6145 V0 Z Polyphthalamide (PPA), 45% Glass Fiber Amodel® AFA-6145 V0 Z is a 45% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin specifically formulated for connector applications requiring compatibility with both in.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 531 °F | Annealed; Flatwise; ISO 75-2/A |
| Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry) Amodel® AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater th.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 531 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Amodel® AS-1933 HS Polyphthalamide (PPA), 33% Glass Fiber Amodel® AS-1933 HS is a 33% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material e.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 531 °F | Unannealed; ASTM D648 |
| Techmer ES Plastiblend® TPX-HTN-000CB 15% Glass Filled Availability: North AmericaForms: Pellets Filler/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightFeatures: High Heat ResistanceInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 531 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP UF0067W PPA LNP* THERMOCOMP* UF0067W is a compound based on Polyphthalamide resin containing 30% glass fiber. Added features of this material include: Hot Water Moldable, Non-Brominated & Non-Chlorinated Flam.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C @Thickness 3.20 mm |
531 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Verton OX07411 PPS (Asia Pacific) LNP* Verton* OX07411 is a compound based on Polyphenylene Sulfide resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 531 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Verton UV00ASXS PPA (Europe-Africa-Middle East) LNP* VERTON* UV00ASXS is a compound based on Polyphthalamide resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 531 °F | ISO-R 75 Method A |
| Hippe PEEK BG Polyetheretherketone with carbon fiber, PTFE and graphite The addition to PEEK of carbon fiber, PTFE and graphite results in a material with high mechanical strength, a low coefficient of sliding friction and enhanced resistance to abrasion. The outstandi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 531 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Amodel® AS-1933 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AS-1933 HS is a 33% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material excee.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 531 °F | ASTM D648 |
| LATI LARAMID G/35 35% Glass Filled Polyphthalamide (PPA) Based Compound
(Unverified Data**) Laramid compounds are based on a unique semi-crystalline engineering polymer (polyphthalamide) offering improved performance compared to traditional engineering thermoplastics at a lower cost than s.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C @Thickness 3.20 mm |
531 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Verton OX07411 PPS LNP* Verton* OX07411 is a compound based on Polyphenylene Sulfide resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||