Polymer Property : Tensile Modulus = 1830 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	12.6 GPa @Temperature 23.0 °C	1830 ksi @Temperature 73.4 °F	ISO 527-2
Solvay Specialty Polymers Amodel® AS-4133 HS Polyphthalamide (PPA) (Unverified Data**) Amodel AS-4133 HS is a 33% glass reinforced, lubricated, heat stabilized grade of polyphthalamide (PPA) that offers fast cycle times and moldability in hot water molds. Typical applications include ..
Tensile Modulus	12.6 GPa	1830 ksi	d.a.m.; ISO 527-1, -2; 1 mm/min
Lanxess DurethanÂ® BKV 40H2.0 EF 900116 Nylon 6, Glass Fiber Reinforced PA 6, 40% glass fibers, injection molding, improved flowability, heat-aging stabilizedInformation provided by LANXESS.
Tensile Modulus	12.6 GPa	1830 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP OCL13XXP PPS - LINEAR (Europe-Africa-Middle East) LNP* Stat-kon* OCL13XXP is a compound based on PPS - LINEAR resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive.
Tensile Modulus	12.6 GPa	1830 ksi	ISO 527-2
Solvay Specialty Polymers AmodelÂ® AS-1933 HS Polyphthalamide (PPA), 33% Glass Fiber AmodelÂ® AS-1933 HS is a 33% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material e..
Tensile Modulus	12.6 GPa	1830 ksi	1 mm/min, Type 1A; ISO 527-2
Solvay Specialty Polymers AmodelÂ® AS-1935 HS Polyphthalamide (PPA), 35% Glass Fiber AmodelÂ® AS-1935 HS is a 35% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material e..
Tensile Modulus	12.6 GPa @Temperature 23.0 Â°C	1830 ksi @Temperature 73.4 Â°F	4; ISO 527-2
Solvay Specialty Polymers AmodelÂ® AS-4133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry) AmodelÂ® AS-4133 HS is a 33% glass reinforced, lubricated, heat stabilized grade of polyphthalamide (PPA) that offers fast cycle times and moldability in hot water molds. Testing conducted on samp..
Tensile Modulus	12.6 GPa	1830 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP Stat-kon OCL13 PPS - LINEAR (Europe-Africa-Middle East) LNP* Stat-kon* OCL13 is a compound based on PPS - LINEAR resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for..
Tensile Modulus	12.6 GPa	1830 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON OCL13XXP PPS - LINEAR (Europe-Africa-Middle East) LNP* Stat-kon* OCL13XXP is a compound based on PPS - LINEAR resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive.
Tensile Modulus	12.6 GPa	1830 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RX09411H PA 66 LNP* Thermocomp* RX09411H is a compound based on Nylon 66 containing Proprietary Fillers. Characteristics are: Radiopacity and Healthcare.
Tensile Modulus	12.6 GPa	1830 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP UX06003 PPA (Europe-Africa-Middle East) LNP* THERMOCOMP* UX06003 is a compound based on Polyphalamide resin containing Carbon Fiber. Added features include Electrically Conductive, Mold Release, Heat Stabilized.
Tensile Modulus	12.6 GPa	1830 ksi	ISO 527-1/-2
DuPont Performance Polymers Rynite® FR531 NC010 Polyethylene Terephthalate (PET) (Unverified Data**) 36% Reinforced Flame Retardant Polyethylene Terephthalate Information provided by DuPont Performance Polymers
Tensile Modulus	12.6 GPa	1830 ksi	1 mm/min
Arkema Group Rilsan® ASR 20 Nylon 12, 20% Carbon Fiber Filled (Dry) Designation ISO 1874-PA12,M,16-090,CF20Rigid grade with carbon fiber filler (20%) for injection molding. Available color: black. High strength-to-weight ratio. Very low shrinkage: include 0,5% on av..
Tensile Modulus	12.6 GPa	1830 ksi	1[mm/min]; ISO 527-1/2
Akro-Plastic Akromid® A3 GF 50 (2423) PA 6.6 Conditioned, 50% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat..
Tensile Modulus	12.6 GPa	1830 ksi	1mm/min; ISO 527
BASF Ultramid® B3WG7 BK00564 35% Glass Filled PA6 (Dry) Ultramid B3WG7 BK00564 is a 35% glass fiber reinforced, pigmented black, injection molding PA6 grade for highly rigid, dimensionally stable components which are resistant to high temperature aging a..
Tensile Modulus	12.6 GPa	1830 ksi	ASTM D-638
Glastic GLASGUARD Scuff and Bulkhead Liners GlasGuard Scuff and Bulkhead Liners serve as a method of protecting trailer walls from damage caused by forklift trucks and careless loading and unloading of freight. Manufactured of 1/4" thick fib..
Tensile Modulus	12.6 GPa	1830 ksi	ISO 527-2
Solvay Specialty Polymers Amodel® AS-1933 HS Polyphthalamide (PPA) (Unverified Data**) Amodel AS-1933 HS is a 33% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material excee..
Tensile Modulus	12.6 GPa @Temperature 23.0 °C	1830 ksi @Temperature 73.4 °F	ISO 527-2
Solvay Specialty Polymers Amodel® AS-4133 HN Polyphthalamide (PPA), Dry, 33% Glass Fiber Reinforcement, Heat Stabilizer Amodel AS-4133 HN polyphthalamide (PPA) is a non-lubricated, heat stabilized grade that offers fast cycle times and is hot-water moldable. Typical applications include electrical and electronic comp..
Tensile Modulus	12.6 GPa	1830 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP VERTON RVN17SXS PA 66 (Europe-Africa-Middle East) LNP* VERTON* RVN17SXS is a compound based on PA 66 resin containing Long Glass Fiber, MoS2. Added features include; Wear Resistant.