Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 212 MPa | 30700 psi | ISO 527-2 |
Solvay Specialty Polymers Amodel® AS-1933 HS Polyphthalamide (PPA), 33% Glass Fiber Amodel® AS-1933 HS is a 33% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material e.. |
|||
Tensile Strength at Break | 212 MPa | 30700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP 9X10312 PA (Asia Pacific) 9X10312 is 50% glass fiber reinforced, impact modified nylon material. High modulus, high flow and good ductility, Low Moisture Absorption. |
|||
Tensile Strength at Break | 212 MPa | 30700 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP PX94085 PA 6 (Europe-Africa-Middle East) LNP* THERMOCOMP* PX94085 is a compound based on PA6 resin, containing Glass Fiber. |
|||
Tensile Strength at Break | 212 MPa | 30700 psi | ISO 527-2 |
Solvay Specialty Polymers Amodel® AS-1933 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AS-1933 HS is a 33% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material excee.. |