SABIC Innovative Plastics Lexan® HPH4704 PPC (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphthalate Carbonate
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® HPH4704 PPC (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High heat specialty polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, gamma and e-beam sterilizable.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Density 1.19 g/cc
0.0430 lb/in³
ASTM D792
1.20 g/cc
0.0434 lb/in³
ISO 1183
Water Absorption 0.19 %

@Time 86400 sec
0.19 %

@Time 24.0 hour
ASTM D570
Moisture Absorption 0.350 %
0.350 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.16 %
0.16 %
ISO 62
Linear Mold Shrinkage, Flow 0.0080 - 0.010 cm/cm

@Thickness 3.20 mm
0.0080 - 0.010 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 2.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
2.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 2.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
2.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 92
92
ASTM D785
Hardness, Rockwell R 127
127
ASTM D785
Tensile Strength at Break 68.0 MPa
9860 psi
50 mm/min; ISO 527
77.0 MPa
11200 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 65.0 MPa
9430 psi
Type I, 50 mm/min; ASTM D638
68.0 MPa
9860 psi
50 mm/min; ISO 527
Elongation at Break 78 %
78 %
Type I, 50 mm/min; ASTM D638
102 %
102 %
50 mm/min; ISO 527
Elongation at Yield 7.0 %
7.0 %
50 mm/min; ISO 527
8.0 %
8.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.10 GPa
305 ksi
5 mm/min; ASTM D638
2.17 GPa
315 ksi
1 mm/min; ISO 527
Flexural Yield Strength 66.0 MPa
9570 psi
2 mm/min; ISO 178
97.0 MPa
14100 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.07 GPa
300 ksi
2 mm/min; ISO 178
2.33 GPa
338 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 3.70 J/cm
6.93 ft-lb/in
ASTM D256
0.840 J/cm

@Temperature -30.0 °C
1.57 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched 32.0 J/cm
59.9 ft-lb/in
ASTM D4812
Tensile Impact Strength 577 kJ/m²
275 ft-lb/in²
Type S; ASTM D1822
Dart Drop, Total Energy 149 J
110 ft-lb
ASTM D3029
74.0 J

@Temperature 23.0 °C
54.6 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Specific Heat Capacity 1.25 J/g-°C
0.299 BTU/lb-°F
ASTM C351
Thermal Conductivity 0.210 W/m-K
1.46 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 1.8 MPa (264 psi) 150 °C
302 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
148 °C

@Thickness 3.20 mm
298 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 165 °C
329 °F
Rate B/50; ISO 306
167 °C
333 °F
Rate B/120; ISO 306
173 °C
343 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 130 °C
266 °F
UL 746B
UL RTI, Mechanical with Impact 130 °C
266 °F
UL 746B
UL RTI, Mechanical without Impact 130 °C
266 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.47 mm
HB

@Thickness 0.0579 in
UL 94
Optical Properties Metric English Comments
Refractive Index 1.60
1.60
ASTM D542
Haze 1.0 %

@Thickness 2.54 mm
1.0 %

@Thickness 0.100 in
ASTM D1003
Transmission, Visible 85 %
85 %
2.54 mm; ASTM D1003
Electrical Properties Metric English Comments
Volume Resistivity >= 2.50e+17 ohm-cm
>= 2.50e+17 ohm-cm
ASTM D257
Dielectric Constant 3.1

@Frequency 1.00e+6 Hz
3.1

@Frequency 1.00e+6 Hz
ASTM D150
3.27

@Frequency 50.0 - 60.0 Hz
3.27

@Frequency 50.0 - 60.0 Hz
ASTM D150
Dielectric Strength 20.0 kV/mm

@Thickness 3.20 mm
508 kV/in

@Thickness 0.126 in
in air; ASTM D149
Dissipation Factor 0.0016

@Frequency 50.0 - 60.0 Hz
0.0016

@Frequency 50.0 - 60.0 Hz
ASTM D150
0.026

@Frequency 100 Hz
0.026

@Frequency 100 Hz
ASTM D150
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten; ASTM D495
Comparative Tracking Index 175 - 250 V
175 - 250 V
UL 746A
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
UL 746A
High Amp Arc Ignition, HAI 15 - 30 arcs
15 - 30 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
UL 746A
Descriptive Properties Value Comments
Specific Volume 0.83cm^3/g