- Polymer Property : Melt Index of Compound = 2.0 g/10 min
Polymer Property : Melt Index of Compound = 2.0 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 280 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 536 °F |
ASTM D1238 |
| Ovation Polymers UTTAP QU BM513 GF BM Nylon, 13% Glass Reinforced Glass reinforced (13 %) High Temperature Polyamide - Blow Molding grade with excellent chemical resistance, improved flow and high HDT. *All properties are measured after 48 hours of conditioning at.. |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Polykemi AB POLYfill PPH TS2020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Polykemi AB SCANFILL FOIL ABYX52C1 PP/PE, Thermoforming Grade Information provided by Polykemi AB |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
2.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics Lexan® HP9NR PC Low flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. For blow molding .. |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
2.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics Lexan® HPH4704 PPC High heat specialty polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, gamma and e-beam steril.. |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
2.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics Lexan® HPH4704 PPC (Asia Pacific) High heat specialty polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, gamma and e-beam steril.. |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
2.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics Lexan® ML7664 PC Copolymer (Asia Pacific) Lexan* ML7664 polycarbonate (PC) siloxane resin, is a product targeting (profile) extrusion applications requiring extreme low temperature ductility. Lexan* ML7664 resin is a non-FR product availabl.. |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Polykemi AB POLYfill PP TOUCH 25325 R3 Polypropylene, Glass Fiber Reinforced, Scratch Resistant Information provided by Polykemi AB |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Polykemi AB POLYfill PPC T2020 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
2.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics Lexan® SLX2531T PC Copolymer Transparent weatherable PC copolymer for blowmolding/extrusion. |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 5.00 kg, Temperature 372 °C |
2.0 g/10 min @Load 11.0 lb, Temperature 702 °F |
ASTM D1238 |
| 3M Dyneon™ PFA 6502TA Perfluoroalkoxy Fluorothermoplastic
(discontinued **) Dyneon PFA 6502TA is a fluorothermoplastic resin developed for compression molding applications. PFA 6502TA has a wide processing window with excellent color stability when longer residence times or.. |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| ICO Polymers ICORENEâ„¢ 150-1334 LMDPE Rotational Molding Resin Description: ICORENE 150-1334 is a linear medium density polyethylene developed for use in rotational molding. It has very high stiffness, toughness, and scratch resistance combined with good proce.. |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| LG Chemical IH830C PMMA, General Purpose Grade for Injection Molding Highest of all grades in heat resistanceMechanical strength and surface hardnessParticularly recommended for tail lamp, reflectors, and general lighting fixturesFeatures: Excellent transparency and .. |
|||
| Melt Index of Compound | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Lushan VB150 Adhesive Resin for Aluminum-Plastic Composite Panel (ACP) Adhesive resin Lushan series for Aluminum-plastic Composite Panel (ACP) proved required bonding strength between aluminum and the filled polyethylene core. The sandwich structure of Aluminum-plastic.. |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 5.00 kg, Temperature 280 °C |
2.0 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics NORYL PX138H PPE+HIPS (Asia Pacific) Modified PPO Resin with 20% Glass Fibre Reinforced |
|||
| Melt Index of Compound | 2.0 g/10 min | 2.0 g/10 min | Condition E; ASTM D1238 |
| A. Schulman CP763-01 Extruded, Blow Molding and Injection Molding Grade Polyethylene DescriptionCP 763-01 is an extruded, blow molding, and injection molding grade of low density polyethylene having good processability and heat sealability. ApplicationCP 763-01 meets the specificat.. |
|||
| Melt Index of Compound | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| A. Schulman LP552-01 Injection Molding, Extrusion Grade Compound DescriptionLP 522-01 is an injection molding and/or extrusion grade compoundApplicationLP 552-01 meets FDA Regulation CFT 177.1520(c)3.1.Information provided by A. Schulman. |
|||
| Melt Index of Compound | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| A. Schulman LP552-01 Injection Molding, Extrusion Grade Compound DescriptionLP 522-01 is an injection molding and/or extrusion grade compoundApplicationLP 552-01 meets FDA Regulation CFT 177.1520(c)3.1.Information provided by A. Schulman. |
|||
| Melt Index of Compound | 2.0 g/10 min | 2.0 g/10 min | Condition 190/2.16; ASTM D1238 |
| Chevron Phillips Marlex® M151 LLDPE Pipe and Corrugated Extrusion Resin Characteristics: Good long-term hoop strengthExtended outdoor lifeClean N550 carbon blackApplications: PipesNot recommended for contact with food productsInformation provided by Chevron Phillips. |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Dow H110-02N Polypropylene Homopolymer Resin OverviewContains a nucleating agentHigh clarityGood melt strengthComplies with U.S. FDA 21 CFR 177.1520 (c)3.2a, Canadian HPFB No ObjectionDOW H110-02N Polypropylene Resin is intended for use in ext.. |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 21.6 kg, Temperature 150 °C |
2.0 g/10 min @Load 47.6 lb, Temperature 302 °F |
Fainplast |
| Fainplast Compounds HAX HF 019/HT6 Halogen Free PVC High fire performances, good flexibility |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 21.6 kg, Temperature 150 °C |
2.0 g/10 min @Load 47.6 lb, Temperature 302 °F |
|
| Fainplast Compounds HAX HFX 024-15C Halogen Free PVC This product is a LSFOH silane grafted compound for cable insulation and sheating, cross-linkable by heat and moisture by previous addition of a suitable catalyst masterbatch. It is recommended to s.. |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Arkema Group OREVAC® 18360 Maleic Anhydride Modified Polyethylene OREVAC® 18360 is anhydride modified polyethylene. It is available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polyethylene (PE) resins. OREVAC® 1.. |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Arkema Group OREVAC® 18370 Maleic Anhydride Modified Polyethylene OREVAC® 18370 is anhydride modified polyethylene. It is available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polyethylene (PE) resins. OREVAC® 1.. |
|||
| Melt Index of Compound | 2.0 g/10 min @Temperature 230 °C |
2.0 g/10 min @Temperature 446 °F |
ASTM D1238 |
| Amco PRIMATOP PP CO 002-12 RC Clarified Random Copolymer Features:low flowcontainers clarifiersexcellent processingexcellent clarityApplications:bottlescontainersFormer A-Top Polymers product; part of Amco product line since 2013. |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 5.00 kg, Temperature 372 °C |
2.0 g/10 min @Load 11.0 lb, Temperature 702 °F |
ASTM D1238 |
| 3M Dyneon™ PFA FLEX 8502 UHPZ Perfluoroalkoxy Fluorothermoplastic Granules Dyneon™ PFA-FLEX UHP family exhibits improved environmental stress crack resistance to stress cracking agents such as fluorsurfactants and fluorosurfactant-containing chemicals. In addition, this f.. |
|||
| Melt Index of Compound | 2.0 - 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 - 3.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Arkema Group LOTRYL® 14 MGC 02 Copolymer Ethylene - Methyl Acrylate LOTRYL® 14 MGC 02 is a random copolymer of ethylene and methyl acrylate made by high-pressure radicalar polymerisation process. Due to the Methyl Acrylate content, LOTRYL® 14 MGC 02 is a polymer o.. |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Arkema Group OREVAC® PPC Grafted Maleic Anhydride Polypropylene OREVAC PPC is a grafted maleic anhydride polypropylene used in the manufacturing of multilayer oxygen barrier tube. OREVAC PPC is mainly used in multi-layer tube to have good adhesion between PP, PA.. |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Dow H110-02NZ Polypropylene Homopolymer Resin OverviewContains a nucleating agentGood melt strengthComplies with U.S. FDA 21 CFR 177.1520 (c)3.2aDOW H110-02NZ Polypropylene Resin is intended for use in extrusion and thermoforming processes in o.. |
|||
| Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Chase Plastics CP Pryme® PE100-LD2M General Purpose Low Density Polyethylene Information provided by Chase Plastics. |
|||