Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polymer Property : Dielectric Strength = 508 kV/in Product List

Electrical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Electrical Properties Metric English Comments
Dielectric Strength 20.0 kV/mm
508 kV/in
Plastcom SLOVAMID 6 FRM 2 PA6, flame retardant
FeaturesDetermined for electrotechnical use. Delivered in natural mode. PA 6 for injection moulding with reduced flammability, with nonhalogen flame retardant. Excellent fluidity of the material pre..
Dielectric Strength 20.0 - 25.0 kV/mm
508 - 635 kV/in
IEC 60243-1
Raschig Group MELOPLAS® 183 MF
Cellulose-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in white and colored shades. Improved dimensional stability and electrical properties as compared with MP 18..
Dielectric Strength 20.0 kV/mm

@Thickness 3.17 mm
508 kV/in

@Thickness 0.125 in
ASTM D149
Chevron Phillips Marlex® HHM TR-144 Polyethylene, Film Grade; HDPE  (discontinued **)
FDA approved.Data provided by the manufacturer
Dielectric Strength 20.0 kV/mm
508 kV/in
Average value: 20.0 kV/mm Grade Count:3
Overview of materials for High Density Polyethylene (HDPE), Film Grade
This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Film Grade". Each property range of values reported is minimum and max..
Dielectric Strength >= 20.0 kV/mm
>= 508 kV/in
Superior Quality
Kazanorgsintez PC-007 Polycarbonate
Production Method: Obtained by means of polycondensation method. Application: Intended for product manufacture by method of extrusion and die-casting.Information Provided by Kazanorgsintez
Dielectric Strength >= 20.0 kV/mm
>= 508 kV/in
Superior Quality
Kazanorgsintez PC-015 Polycarbonate
Production Method: Obtained by means of polycondensation method. Application: Intended for product manufacture by method of die-casting.Information Provided by Kazanorgsintez
Dielectric Strength 20.0 kV/mm
508 kV/in
ASTM D149/DIN 53481
Kolon KOPA® KN332G30VO G/F Reinforced & Flame Retardant Nylon 66
KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstandin..
Dielectric Strength >= 20.0 kV/mm

@Frequency 50.0 Hz
>= 508 kV/in

@Frequency 50.0 Hz
ASTM D149
Iran Petrochemical (PCC) PC 5970 Polycarbonate
Suitable for injection moldingInformation provided by Iran Petrochemical Commercial Co.
Dielectric Strength 20.0 kV/mm

@Thickness 2.00 mm
508 kV/in

@Thickness 0.0787 in
ASTM D149
Gromax CCP PBT 1100-630S
Product Description: PBT unreinforced medium viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Exce..
Dielectric Strength 20.0 kV/mm

@Thickness 2.00 mm
508 kV/in

@Thickness 0.0787 in
ASTM D149
Gromax CCP ABS/PBT 7320H-104 20% Glass Fiber Filled
Product Description: A 20% glass fiber reinforced injection molding grade. Characteristics:Low warp age and excellent dimensionally stable Excellent electrical property Excellent mechanic and chemi..
Dielectric Strength 20.0 kV/mm

@Thickness 2.00 mm
508 kV/in

@Thickness 0.0787 in
ASTM D149
Gromax PBT 2000-201D
Product Description: PBT unreinforced injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Excellent mechanic an..
Dielectric Strength 20.0 kV/mm
508 kV/in
DIN 53481
Schwartz Technical Plastics LAMIGAMID® 100 Polyamide 6, Extruded, Conditioned
Application: machine parts under 80 mm diameter, hammer-heads, cup-shaped bearing shellsInformation provided by Schwartz Technical Plastics GmbH
Dielectric Strength 20.0 kV/mm
508 kV/in
DIN 53481
Schwartz Technical Plastics LAMIGAMID® 324 Cast Polyamide 6, MoS2, Heat Stabilized, Conditioned
Application: heavy-duty wheels, running speed up to 3m/sInformation provided by Schwartz Technical Plastics GmbH
Dielectric Strength 20.0 - 25.0 kV/mm

@Thickness 1.00 mm
508 - 635 kV/in

@Thickness 0.0394 in
ASTM D149
Solvay Specialty Polymers Solef® 32008 Polyvinylidene Fluoride (PVDF)
Solef® 32008 PVDF copolymer is a low viscosity and very flexible grade for Wire & Cable applications.Features: Copolymer; Good Flexibility; Low ViscosityUses: Wire & Cable ApplicationsAdditional ..
Dielectric Strength 20.0 kV/mm

@Thickness 3.20 mm
508 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
SABIC Innovative Plastics Valox® IQ4860HR PBT
Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified.
Dielectric Strength 20.0 kV/mm
508 kV/in
ASTM D149
Shinkong Synthetic Fibers Shinite® F102G30 PET, 30% Glass Filled, Fire Retardant, Halogen Free
Information from Shinkong Synthetic Fibers Corp.
Dielectric Strength 20.0 kV/mm
508 kV/in
ASTM D149
SCG Chemicals EL-Leneâ„¢ H2001WC High Density Polyethylene Wire & Cable Grade
Key Characteristics:Excellent environmental stress cracking resistance (ESCR), high mechanical properties, high speed extrusionRecommended Applications:Jacketing of fiber optical cablesJacketing of ..
Dielectric Strength 20.0 kV/mm
508 kV/in
IEC 672-1
CeramTec Rubalit® IS 95 Alumina
Rubalit® IS 95 is a high-performance alumina ceramic. Aluminas exhibit good mechanical properties such as hardness, compressive and tensile strength, and elastic modulus. They perform well at eleva..
Dielectric Strength 20.0 kV/mm
508 kV/in
IEC 60243-1
Polyplastics FR-PET® CN9030 Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Flame retardant, General purpose
Information provided by PolyPlastics.
Dielectric Strength 20.0 kV/mm
508 kV/in
IEC 243
Vyncolit X680 Novolac Phenolic
Glass fiber and glass bead filled phenolic molding compound with excellent mechanical and thermal properties. Easily transformed into complex shapes. UL listed.USES: Complex precision parts with t..
Dielectric Strength <= 20.0 kV/mm
<= 508 kV/in
IEC 60243
Borealis Casico™ FR4820 Natural Low Smoke Zero Halogen Flame Retardant Insulation Compound for Building Energy Cables
Casico™ FR4820 is a thermoplastic, low smoke zero halogen (LSZH) flame retardant, UV stabilized, natural insulation compound combining with excellent extrusion properties. It is based on the novel..
Dielectric Strength 20.0 kV/mm
508 kV/in
Dow Corning SE 1896 FR KIT
Two-part, translucent, heat cure.Information provided by Dow Corning
Dielectric Strength 20.0 kV/mm
508 kV/in
IEC 60243-1
DSM Arnitel® EM400 Polyether Ester Elastomer (European and Asian Grade)
Product description: Arnitel® combines the advantages of engineering thermoplastics, being easy to process with excellent mechanical properties, at the same time with the flexibility of rubbers.Arn..
Dielectric Strength 20.0 kV/mm

@Thickness 2.00 mm
508 kV/in

@Thickness 0.0787 in
ASTM D149
Chang Chun Plastic PBT3015 15% Glass Fiber Enforced PBT
Information provided by Dowell Trading Company Ltd.
Dielectric Strength 20.0 kV/mm

@Thickness 2.00 mm
508 kV/in

@Thickness 0.0787 in
ASTM D149
Beijing Ranger Chem PBT-201-G30 291 Flame Retarding FR PBT
Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin..
Dielectric Strength 20.0 kV/mm
508 kV/in
Step by step; ASTM D149
Ascend Performance Materials VYDYNE® 45 Nylon, Impact Modified, Weather Stable
Typical property data. VYDYNE is a registered trademark of Solutia Inc.
Dielectric Strength 20.0 kV/mm

@Thickness 2.00 mm
508 kV/in

@Thickness 0.0787 in
ASTM D149
Beijing Ranger Chem PBT-201-G20 202 Environmental Protection Flame Retarding FR PBT
Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin..
Dielectric Strength 20.0 kV/mm

@Thickness 3.17 mm
508 kV/in

@Thickness 0.125 in
ASTM D149
Chevron Phillips Marlex® HMN 5580 Polyethylene, Injection Molding Grade, HDPE  (discontinued **)
Meets FDA Regulation 177.1520. High stiffness, excellent surface appearance, good impact strength and warpage resistance.Data provided by the manufacturer
Dielectric Strength 20.0 kV/mm

@Thickness 1.00 mm
508 kV/in

@Thickness 0.0394 in
IEC 60243
Ascend Performance Materials Vydyne® R533H NAT Nylon 66, 33% Glass Reinforced, DAM
Vydyne® R533H NAT is 33% glass-fiber reinforced, hydrolysis-resistant, heat-stabilized PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties..
Dielectric Strength <= 20.0 kV/mm
<= 508 kV/in
IEC 60243
Borealis Borstar® LE8707 Black Bimodal LLDPE Jacketing Compound for Energy and Communication Cables
Borstar® LE8707 is a black linear low density (LLD) jacketing compound, which is produced with the Borealis proprietary Borstar® bimodal process technology. Borstar® technology allows the manufa..