- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 148 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 148 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C @Thickness 3.20 mm |
298 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® 4701R PPC High heat resistant polyphthlate carbonate, provides DTUL of 300F at 264 psi. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C @Thickness 3.20 mm |
298 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® 4701R PPC (Asia Pacific) High heat resistant polyphthlate carbonate, provides DTUL of 300F at 264 psi. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C @Thickness 3.20 mm |
298 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® 4704 PPC (Asia Pacific) High heat resistant polycarbonate copolymer, provides DTUL of 300F at 264 psi. FDA food contact compliant in limited colors. Effective January 15th, 2008 this grade will no longer be supported with .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C | 298 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hylex® P1310G30 HB Polycarbonate, 30% Fiberglass Reinforced, UV Stabilized Information provided by Ravago. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C @Thickness 6.35 mm |
298 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| PolyOne LubriOne™ PC-30CF/20T Polycarbonate (PC) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C | 298 °F | |
| Covestro Apec® DP 1-9349/5 Polycarbonate
(discontinued **) Key Features:Release agentUnfilledSuitable processing methods:Injection moldingThermoformingInformation provided by Bayer Polymers.As of 1 September 2015, Bayer MaterialScience was separated from Ba.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C | 298 °F | ASTM D648 |
| LG Chemical LUPOY GP-2301F General Purpose Modified PC, 30% Glass Fiber Reinforced, Flame Retardant Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C | 298 °F | ASTM D648 |
| LyondellBasell Higlass SB224-1 Polypropylene Copolymer, 10% Glass Fiber Key Features: conventional melt flow, medium modulus, chemically coupled, glass fiber-reinforced polypropylene copolymer, excellent impact strength, good processabilityApplications: automotive wheel.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C @Thickness 3.20 mm |
298 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL V02570 PPE+HIPS (Asia Pacific) Noryl* V02570 is a 25% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C @Thickness 3.20 mm |
298 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL V02570 PPE+HIPS (Europe-Africa-Middle East) Noryl* V02570 is a 25% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C @Thickness 3.20 mm |
298 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL V03550 PPE+HIPS Noryl* V03550 is a 35% milled fibre reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C | 298 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP KFP032 Acetal Copolymer LNP LUBRICOMP* KFP032 is a compound based on Acetal Copolymer resin containing 10% Glass Fiber, 15% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C | 298 °F | ASTM D648 |
| Techmer ES Electrafil® J-50/CF/10/TF/13/SI/2 Polycarbonate, 10% Carbon Fiber Reinforced, 13% PTFE, 2% Silicone |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C | 298 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON RFD03 PA 66 (Asia Pacific) LNP* STATKON* RFD03 is a compound based on PA 66 resin contaning Carbon Powder, Glass Fiber. Added features include: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C | 298 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP KF002L Acetal Homopoly LNP* THERMOCOMP* KF002L is a compound based on Acetal Homopolymer resin containing 10% Glass Fiber. Added features of this material include: Low Extractible. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C @Thickness 6.40 mm |
298 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® GP-8300G MPPE, 30% Glass Filled Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C | 298 °F | ISO 75 |
| Teijin Panlite® GN-3430R Improved Mold Release, Glass Fiber Reinforced, Flame Resistant Polycarbonate Resin GF 30% reinforced, flame retardant and mold release grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need mechanical property e.g., stiffnessPrecision machin.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C | 298 °F | ISO 75 |
| Teijin Panlite® GS-3430 Friction and Abrasion Resistant, Glass Fiber Reinforced Polycarbonate Resin GF 30% reinforced grade, meeting UL 94 V-2. It is compounded with fluorine powder to improve friction and abrasion resistance, maintaining excellent characteristics of polycarbonate resin.Applicatio.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C @Thickness 3.20 mm |
298 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP MX85738 PP (Asia Pacific) LNP* Thermocomp* MX85738 is a compound based on Polypropylene resin containing Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C | 298 °F | ASTM D648 |
| Techmer ES Electrafil® J-50/CF/10/TF/15 Polycarbonate, 10% Carbon Fiber Reinforced, 15% PTFE |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C @Thickness 3.20 mm |
298 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL GTX GTX918W PPE+PS+PA (Asia Pacific) High flow NORYL GTX resin for under-the-hood and electrical applications requiring retention of properties under thermal load |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C @Thickness 3.20 mm |
298 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL GTX GTX918WR PPE+PS+PA High flow PPE+PS+PA for under-the-hood and electrical applications. With mold release |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C @Thickness 3.20 mm |
298 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Noryl GTX GTX918WR PPE+PS+PA (Asia Pacific) High flow PPE+PS+PA for under-the-hood and electrical applications. With mold releaseThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C @Thickness 6.40 mm |
298 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL PX1712 PPE+HIPS (Asia Pacific) PPE/HIPS unfilled high heat for auto interior |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C | 298 °F | |
| Covestro Apec® HT KU 1-9340/5 High-Heat Polycarbonate Transparent and opaque shades possible, easy-to-demold.Applications: Medical sector: superheated steam sterilization.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was s.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C | 298 °F | ASTM D648 |
| A. Schulman ComAlloy Comtuf® 105 Polypropylene, Glass Reinforced, Chemically Coupled, Impact Modified Data provided by the manufacturer, ComAlloy International Company.40% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C | 298 °F | ISO 75 |
| Azoty Tarnow™ TARNOFORM 300 MW4 POM Mineral filled injection molding grade based on Tarnoform 300 reinforced with 20% wollastonite; such a compound has high stiffness, dimensional stability and hardness combined with low shrinkage.Inf.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C | 298 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 125 Polypropylene, Glass Reinforced, Chemically Coupled Data provided by the manufacturer, ComAlloy International Company.50% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C | 298 °F | ASTM D648 |
| E-Polymers SEPAZ® N6000FR Nanoclay 4% Flame Retardant Nano Composite Resin Nanocomposite: SEPAZ Nano PA6 nanocomposites have been prepared successfully in commercial scale through 'in situ' polymerization or melt extrusion. The unique performance properties of nanocomposi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C @Thickness 3.20 mm |
298 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL FE1740PW PPE+PS (Europe-Africa-Middle East) Noryl* FE1740PW Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 40 % Glass Reinforced, injection moldable grade with improved hydrolytic stability and with a Tensile Modulus > 11000 MPa; thi.. |
|||