Polymer Property : Tensile Modulus = 305 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Modulus 2.10 GPa
305 ksi
ASTM D638
Plaskolite PETG Mirror Sheet
Versatile fabrication properties with good impact strength, good design flexibility, and speed of fabrication.Data provided by the manufacturer, Plaskolite, Inc.
Tensile Modulus 2.10 GPa
305 ksi
50 mm/min; ASTM D638
Ovation Polymers OPTRENE 20GF Polypropylene, 20% Glass Reinforced
Properties of chemically coupled glass reinforced (20%) polypropylene with high strength and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All ..
Tensile Modulus 2.10 GPa
305 ksi
5 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® 4404 PPC+PC (Europe-Africa-Middle East)
High heat polycarbonate copolymer, with HDT of 287F at 264 psi. FDA food contact compliant. Effective Jan 15th, 2008 this grade should not be used for medical applications which require biocompatibi..
Tensile Modulus 2.10 GPa
305 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics Lexan® 943X PC Copolymer
Lexan* 943X is a UV stabilized medium flow impact modified injection molding (IM) grade. This resin offers UL94 V0 @ 1.5mm flame retardancy based on non-bromine, non-chlorine FR systems, low tempera..
Tensile Modulus 2.10 GPa
305 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DL0039E PC (Asia Pacific)
LNP* Lubricomp* DL0039E is a compound based on Polycarbonate resin containing PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retardant, Easy Molding.
Tensile Modulus 2.10 GPa
305 ksi
MD; ASTM D882
Eastman 9921P PET Film  (discontinued **)
Voridian PET 9921P is produced at Voridian’s manufacturing sites in Rotterdam and Zarate, it is PTA/CHDM based, and it is sold to customers in the Europe, Middle East and Africa, Argentina, Bolivia..
Tensile Modulus 2.10 GPa
305 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics Cycoloy® CP8320 PC+ABS (Europe-Africa-Middle East)
Cycoloy Medium Heat Plating Grade for Automotive
Tensile Modulus 2.10 GPa
305 ksi
ISO 527-2
Total Lacqrene® 4240(EU) High Impact Polystyrene  (discontinued **)
LACQRENE® 4240 is a high heat resistance, high impact polystyrene for the extrusion industry. Good mechanical and thermal properties leads to the production of thermoformed articles of good rigidi..
Tensile Modulus 2.10 GPa
305 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics Lexan® EXL9330 PC Copolymer
Opaque PC-Siloxane copolymer with excellent processability. Non-chlorinated, non-brominated flame retardant product in most colors. UV-stabilized. UL rated f1/V-0/5VA.
Tensile Modulus 2.10 GPa
305 ksi
1 mm/min; ISO 527-1,-2
Inno-Comp INNOPOL® CS 2-9120 20% Talc-Filled Polypropylene Block-Copolymer
INNOPOL® CS 2-9120 is a 20% talc-filled compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOL® CS 2-9120 is developed for producing..
Tensile Modulus 2.10 GPa
305 ksi
ISO 527-1/-2
Mitsubishi Xantar® C CM 206 Polycarbonate/ABS Blend
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances ..
Tensile Modulus 2.10 GPa
305 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL RN0401 PPE+PS
Noryl RN0401 resin is an unfilled Post Consumer Recycle (PCR) based injection moldable modified polyphenylene ether blend comprising at least 20% PCR content. Available in black only.
Tensile Modulus 2.10 GPa
305 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DP002 PC (Europe-Africa-Middle East)
LNP* Lubricomp* DP002 is a compound based on Polycarbonate resin containing PTFE and Silicone. Added features of this material include: Internally Lubricated, Easy Molding.
Tensile Modulus 2.10 GPa
305 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRILOY D2000P PC
LNP LUBRILOY* D2000P is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Exceptional Processing, Wear Resistant.
Tensile Modulus 2.10 GPa

@Temperature 100 °C
305 ksi

@Temperature 212 °F
2; ISO 527-2
Solvay Specialty Polymers Amodel® AT-1002 HS Polyphthalamide (PPA)
Amodel® AT-1002 HS is a neat, toughened, heat stabilized polyphthalamide (PPA) resin that offers superior retention of properties after humid thermal aging; high impact at low temperature and bet..
Tensile Modulus 2.10 GPa
305 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics Xenoy® HX5600HP PBT+PC (Asia Pacific)
Xenoy HX5600HP is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing..
Tensile Modulus 2.10 GPa
305 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics Xenoy® HX5600HP PBT+PC (Europe-Africa-Middle East)
Xenoy HX5600HP is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing..
Tensile Modulus 2.10 GPa
305 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics XYLEX X7503 PC+POLYESTER
PC-Siloxane copolymer + Polyester alloy, High Impact, Transparent
Tensile Modulus 2.10 GPa
305 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics Valox® K3501 PBT (Europe-Africa-Middle East)
Unfilled PBT, Hydrollytically Stable, Heat Stabilized, Impact Modified. A hydrollytically stable grade designed for improved performance under heat/humidity environments. Targeted at automotive unde..
Tensile Modulus 2.10 GPa
305 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics XYLEX EXXX0292 PC+POLYESTER (Europe-Africa-Middle East)
XYLEX* EXXX0292 is a transparent copolyester/polycarbonate blend with high flow, V2 UL94 rating at 1.5mm and Tg of 108 C
Tensile Modulus 2.10 GPa
305 ksi
ISO Data.
Styron Pulse® 840P ABS + Polycarbonate
PULSE® 840P Engineering resin has been designed to provide excellent processability, high heat resistance, and high impact strength at both room and low temperatures. PULSE 840P Engineering resin..
Tensile Modulus 2.10 GPa
305 ksi
ISO 527-1
Sax Polymers SAXLAC 340Q Acrylonitrile Butadiene Styrene
Saxalac 340Q is an siliconized, UV protected, high impact resistant and easy flowing ABS injection molding grade, characterized by good processability and high stiffness.Mechanical property data tes..
Tensile Modulus 2.10 GPa
305 ksi
ASTM D638
Total PS CPDS 855S Chlorine and Bromine Free Flame Retardant High Impact Polystyrene
Total Petrochemicals Polystyrene 855S is a chlorine and bromine free flame retardant high impact polystyrene with excellent thermal stability and processability for injection molding.Suitable Applic..
Tensile Modulus 2.10 GPa
305 ksi
ASTM D638
Eastman Drystar 0601 Copolyester, Injection Molded
This product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman’s copolyesters are highly valued for their excellen..
Tensile Modulus 2.10 GPa
305 ksi
Covestro Bayblend® T 45 Polycarbonate/ABS Blend
High impact and notched impact strength, little risk of brittle fracture, high dimensional accuracy, good platable.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was sep..
Tensile Modulus 2.10 GPa
305 ksi
chs 2.0 in/min; ASTM D638
Diamond Polymers Centrex® 814 General Purpose Injection Molding Grade
Centrex 814 resin is a high-gloss, high-impact grade of ASA (acrylonitrile-styrene-acrylate). It is an injection molding grade with a good balance of physical properties, gloss and processing perfor..
Tensile Modulus 2.10 GPa
305 ksi
1mm/min; ISO 527-1
Denka MALECCA K-600 ABS
A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de..
Tensile Modulus 2.10 GPa

@Temperature 80.0 °C
305 ksi

@Temperature 176 °F
ISO Data
BASF Ultramid® 8272G HS BK-102 12% Glass Filled PA6 (Dry)
Ultramid 8272G HS BK-102 is a 12% glass fiber reinforced, black pigmented, thermally modified, nylon 6 blow molding compound offering an excellent balance of engineering properties combined with the..
Tensile Modulus 2.10 GPa
305 ksi
ASTM D638
Ineos Nova Zylar® 530 Clear Impact Modified Acrylic Copolymer  (discontinued **)
Features:High clarityStyrenic processing advantagesExcellent property retention after ETO and gamma sterilizationMeets USP XXIII specifications for Class VI plasticsUL94 HB @ 1.5 mm for uncolored ma..