Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

SABIC Innovative Plastics Cycoloy® XCY480 PC+ABS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® XCY480 PC+ABS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High flowThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.14 %
0.14 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.47 %

@Temperature 23.0 °C
 0.47 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
SABIC Method
Melt Flow 12 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 12 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
38 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 38 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
39 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 39 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 42.0 MPa
6090 psi
Type I, 50 mm/min; ASTM D 638
43.0 MPa
6240 psi
50 mm/min; ISO 527
Tensile Strength, Yield 49.0 MPa
7110 psi
Type I, 50 mm/min; ASTM D 638
51.0 MPa
7400 psi
50 mm/min; ISO 527
Elongation at Break 40 %
40 %
Type I, 50 mm/min; ASTM D 638
50 %
50 %
50 mm/min; ISO 527
Elongation at Yield 4.0 %
4.0 %
Type I, 50 mm/min; ASTM D 638
4.0 %
4.0 %
50 mm/min; ISO 527
Tensile Modulus 2.15 GPa
312 ksi
1 mm/min; ISO 527
2.27 GPa
329 ksi
50 mm/min; ASTM D 638
2.27 GPa
329 ksi
5 mm/min; ASTM D 638
Flexural Strength 73.0 MPa
10600 psi
ASTM D 790
Flexural Yield Strength 47.0 MPa
6820 psi
2 mm/min; ISO 178
Flexural Modulus 2.10 GPa
305 ksi
2 mm/min; ISO 178
2.14 GPa
310 ksi
ASTM D 790
Izod Impact, Notched 2.60 J/cm

@Temperature -30.0 °C
 4.87 ft-lb/in

@Temperature -22.0 °F
 ASTM D 256
4.50 J/cm

@Temperature 0.000 °C
 8.43 ft-lb/in

@Temperature 32.0 °F
 ASTM D 256
5.60 J/cm

@Temperature 23.0 °C
 10.5 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Notched (ISO) 19.0 kJ/m²

@Temperature -30.0 °C
 9.04 ft-lb/in²

@Temperature -22.0 °F
 80*10*3; ISO 180/1A
46.0 kJ/m²

@Temperature 0.000 °C
 21.9 ft-lb/in²

@Temperature 32.0 °F
 80*10*3; ISO 180/1A
55.0 kJ/m²

@Temperature 23.0 °C
 26.2 ft-lb/in²

@Temperature 73.4 °F
 80*10*3; ISO 180/1A
Charpy Impact, Notched 2.00 J/cm²

@Temperature -30.0 °C
 9.52 ft-lb/in²

@Temperature -22.0 °F
 V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
5.50 J/cm²

@Temperature 23.0 °C
 26.2 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Impact Test 130 J
95.9 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 µm/m-°C

@Temperature -30.0 - 80.0 °C
 44.4 µin/in-°F

@Temperature -22.0 - 176 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -30.0 - 80.0 °C
 44.4 µin/in-°F

@Temperature -22.0 - 176 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 94.0 °C
201 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
118 °C
244 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
117 °C

@Thickness 3.20 mm
 243 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
95.0 °C

@Thickness 3.20 mm
 203 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Vicat Softening Point 118 °C
244 °F
Rate B/50; ISO 306
118 °C
244 °F
Rate B/120; ISO 306
129 °C
264 °F
Rate A/50; ISO 306
Users viewing this material also viewed the following:
Copyright © lookpolymers.com All Rights Reserved